Diffusion method for depositing microporous film
Assignee: Tenneco Polymers Inc
•
Filing: 1974-03-29
•
Granted: 1977-02-01
•
Expires: 1994-03-29
Abstract
Abstract Describes procedure for deposition of microporous grain layer in and on a substrate for the production of leather replacement products in which the deposition liquid diffuses upwardly through the substrate to deposit the polymer from a solution thereof which has been laminated and coated on the top surface of the substrate.
Inventors
- 👤 Wu Lan Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:27
CPC Classifications
D; D06; D06N; D06N3/00; D06N3/12; D06N3/14; D06N3/0086; D06N3/0088
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
298 words
A method for forming a vapor permeable, breatheable, grain layer on the top surface of a porous natural leather replacement product substrate which comprises the steps of: A. coating a solution of a polyurethane elastomer in a solvent onto a release surface of a flexible sheet; B. wetting the said leather replacement product substrate with a wetting liquid which is miscible with the solvent of Step A, and in which the polyurethane elastomer of Step A is insoluble to produce a wetted substrate free from a surface film of wettting liquid on its top surface; C. laminating the product of Step A to the product of Step B so that the polyurethane solution of Step A is in contact with the top surface of the wetted substrate of Step B by bringing the said products into registry, passing through nip rolls, depositing the polyurethane elastomer as a base film on the top surface of the substrate by bathing the laminate in a separate bath of the wetting liquid, and removing said flexible sheet; D. applying a solution of a polyurethane elastomer in a solvent to the side of the base film carrying the deposited elastomer of Step C; E. bringing the uncoated bottom surface of the polyurethane elastomer solution coated substrate of Step D into registry with the top surface of a porous support which is wetted with a wetting liquid which is miscible with the solvent of Step D, and in which the polyurethane elastomer of Step D is insoluble; F. maintaining the contact of Step E until the polyurethane elastomer of Step D is deposited as a grain layer on the base film of Step C as a result of diffusion of said wetting liquid through the substrate; G. washing the resulting product and thereafter drying.
Claim 2
Independent Claim
298 words
A method for forming a vapor permeable, breatheable, grain layer on the top surface of a porous natural leather replacement product substrate which comprises the steps of: A. coating a solution of a polyurethane elastomer in a solvent onto a release surface of a flexible sheet; B. wetting the said leather replacement product substrate with a wetting liquid which is miscible with the solvent of Step A, and in which the polyurethane elastomer of Step A is insoluble to produce a wetted substrate free from a surface film of wettting liquid on its top surface; C. laminating the product of Step A to the product of Step B so that the polyurethane solution of Step A is in contact with the top surface of the wetted substrate of Step B by bringing the said products into registry, passing through nip rolls, depositing the polyurethane elastomer as a base film on the top surface of the substrate by bathing the laminate in a separate bath of the wetting liquid, and removing said flexible sheet; D. applying a solution of a polyurethane elastomer in a solvent to the side of the base film carrying the deposited elastomer of Step C; E. bringing the uncoated bottom surface of the polyurethane elastomer solution coated substrate of Step D into registry with the top surface of a porous support which is wetted with a wetting liquid which is miscible with the solvent of Step D, and in which the polyurethane elastomer of Step D is insoluble; F. maintaining the contact of Step E until the polyurethane elastomer of Step D is deposited as a grain layer on the base film of Step C as a result of diffusion of said wetting liquid through the substrate; G. washing the resulting product and thereafter drying.
Claim 3
Dependent Claim
12 words
A method as in claim 1 wherein the solvent is dimethyl formamide.
Claim 4
Dependent Claim
22 words
A method as in claim 2 wherein the wetting liquid is a dimethyl formamide-water mixture containing 10 to 90% water by weight.
Claim 5
Dependent Claim
15 words
A method as in claim 3 wherein the wetting liquid contains 30% water by weight.
Claim 6
Dependent Claim
12 words
A method as in claim 1 wherein the wetting liquid is water.
Claim 7
Dependent Claim
18 words
A method as in claim 1 wherein the solvent is dimethyl formamide and the wetting liquid is water.
Claim 8
Dependent Claim
15 words
A method as in claim 1 wherein the polyurethane elastomer is blended with polyvinyl chloride.
Claim 9
Dependent Claim
43 words
A method as in claim 1 in which the polymer solution contains from about 30 to 120 parts by weight of inert particles per 100 parts by weight of dry elastomer in the size range of from about 200 Angstroms to 150 microns.
Claim 10
Dependent Claim
15 words
A method as in claim 8 wherein the particles are microporous, microcrystalline, resilient, cellulosic particles.
References Cited (Backward Citations)
US2657151A
Cited
US2894855A
Cited
US2905568A
Cited
US3208875A
Cited
US3238055A
Cited
NL6404231A
Cited
US3363530A
Cited
US3536553A
Cited
US3539424A
Cited
US3515573A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-02-01 | 1980-08-02 | 1981-02-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-02-01 | 1984-08-02 | 1985-02-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-02-01 | 1988-08-02 | 1989-02-01 | $7700.00 | Window Closed / Lapsed |