Aqueous polymerization of unsaturation carboxylic acid monomers using anionic surfactant mixed with the monomer and polyhydric alcohol prior to reaction
Assignee: Valspar Corp
•
Filing: 1975-06-09
•
Granted: 1977-01-25
•
Expires: 1995-06-09
Abstract
Abstract Monoethylenic monomers, including from about 1 to about 30% by weight of monoethylenic carboxylic acid, are placed in solution in a liquid mixture containing a low molecular weight polyhydric alcohol, and an anionic surfactant. This liquid mixture is dispersed in water and polymerized at an elevated polymerization temperature using agitation and in the presence of a free radical polymerization catalyst. The dispersion of polymer particles is then at least partially neutralized, preferably with ammonia or an amine to form an aqueous dispersion which is stable in the absence of emulsifying agent and which is useful in coating.
Inventors
- 👤 Kazys Sekmakas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 05:01
CPC Classifications
C; C08; C08F; C08F246/00; C08F220/00; C08F220/02; C08F220/04; C08F220/06; C08F8/00; C08F8/44; C09; C09D; C09D125/00; C09D125/02; C09D125/04; C09D125/08; C09D125/14; C09D161/00; C09D161/20; C09D161/26; C09D161/28; C08F212/00; C08F212/02; C08F212/04; C08F212/06; C08F212/08; C08F2810/00; C08F2810/50
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
167 words
A method of producing a dispersion of copolymer particles in water comprising, forming a liquid mixture of monoethylenic monomers and from 2% up to about 50%, based on the weight of said monomers, of water insoluble polyhydric alcohol selected from trihydric alcohols and tetrahydric polyhydric alcohols, said polyhydric alcohol having a molecular weight of from 300 up to about 6000, said mixture including from 1-30% of anionic surfactant, based on the weight of said polyhydric alcohol, said monomers including from about 1 to about 30% by weight of monoethylenic carboxylic acid, dispersing said mixture in water to form a dispersion, said dispersion including a free radical polymerization catalyst, subjecting the dispersed liquid mixture in said dispersion containing the said catalyst to agitation at an elevated polymerization temperature, with said monomers being in solution in the dispersed mixture, until polymerization of said monomers has been completed and copolymer particles have been formed, and then neutralizing at least 10% of the acidity in said copolymer particles with a base.
Claim 2
Independent Claim
167 words
A method of producing a dispersion of copolymer particles in water comprising, forming a liquid mixture of monoethylenic monomers and from 2% up to about 50%, based on the weight of said monomers, of water insoluble polyhydric alcohol selected from trihydric alcohols and tetrahydric polyhydric alcohols, said polyhydric alcohol having a molecular weight of from 300 up to about 6000, said mixture including from 1-30% of anionic surfactant, based on the weight of said polyhydric alcohol, said monomers including from about 1 to about 30% by weight of monoethylenic carboxylic acid, dispersing said mixture in water to form a dispersion, said dispersion including a free radical polymerization catalyst, subjecting the dispersed liquid mixture in said dispersion containing the said catalyst to agitation at an elevated polymerization temperature, with said monomers being in solution in the dispersed mixture, until polymerization of said monomers has been completed and copolymer particles have been formed, and then neutralizing at least 10% of the acidity in said copolymer particles with a base.
Claim 3
Dependent Claim
31 words
A method as recited in claim 1 in which said base is an amine and neutralization is carried out to provide a dispersion having a pH in the range of 5-11.
Claim 4
Dependent Claim
20 words
A method as recited in claim 1 in which said polyhydric alcohol is employed in an amount of from 2-20%.
Claim 5
Dependent Claim
22 words
A method as recited in claim 1 in which said polyhydric alcohol is a polyoxypropylene adduct of a trihydric or tetrahydric alcohol.
Claim 6
Dependent Claim
16 words
A method as recited in claim 1 in which said polyhydric alcohol is a lactone derivative.
Claim 7
Dependent Claim
24 words
A method as recited in claim 4 in which said polyoxypropylene derivative has a molecular weight in the range of from 350 to 5,000.
Claim 8
Dependent Claim
58 words
A method as recited in claim 1 in which said polyhydric alcohol is employed in an amount of from 3-12%, said monoethylenic carboxylic acid is present in an amount of from 3-20% of the weight of monoethylenic monomers, and said anionic surfactant is used in an amount of from 2-15%, based on the weight of the polyhydric alcohol.
Claim 9
Dependent Claim
40 words
A method as recited in claim 1 in which said monoethylenic monomers carry functional groups other than the carboxyl group, said other functional groups being selected from the hydroxy group, the amido group, the methylol group, and the amino group.
Claim 10
Dependent Claim
16 words
A method as recited in claim 1 in which said catalyst is dissolved in the water.
Claim 11
Dependent Claim
14 words
A method as recited in claim 9 in which said catalyst is a persulfate.
Claim 12
Dependent Claim
23 words
A method as recited in claim 1 in which said anionic surfactant is a 50% dispersion of sodium dioctyl sulfosuccinate in ethylene glycol.
Claim 13
Dependent Claim
8 words
The product of the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-25 | 1980-07-26 | 1981-01-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-25 | 1984-07-26 | 1985-01-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-25 | 1988-07-26 | 1989-01-25 | $7700.00 | Window Closed / Lapsed |