Method of treating waste produced during stainless steel making
Assignee: Japan Metals and Chemical Co Ltd
•
Filing: 1975-06-12
•
Granted: 1977-01-25
•
Expires: 1995-06-12
Abstract
Abstract A method of treating waste produced during stainless steel making is disclosed. The method comprises the steps of kneading a sludge cake with a mixture of dust and scale to obtain a kneaded mass, adding an organic binder and eventually adding water with an inorganic binder to said kneaded mass, shaping said kneaded mass into a briquette, and heating said briquette at a low temperature. The briquette obtained can be used as a ferroalloy making raw material. Metal oxides contained in the briquette are reduced by a dry reduction refining added with a carbonaceous reducing agent and eventually with a flux to separate usable metals.
Inventors
- 👤 Hiroshi Fukuoka
- 👤 Teruhiko Kameyama
- 👤 Yuji Takahashi
- 👤 Kenji Nicho
- 👤 Tatsuo Misawa
- 👤 Tsuneyuki Inoue
- 👤 Kimiaki Imai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:10
CPC Classifications
C; C22; C22B; C22B7/00; C22B7/02; C21; C21B; C21B11/00; C21B11/10; C21B13/00; C21B13/0006; C22B1/00; C22B1/14; C22B1/24; C22B1/242; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
190 words
A method of treating waste produced during stainless steel making and processing, comprising: forming a sludge cake containing 2-5 weight percent water by dehydrating slurry-like pickling sludge containing 30-70 weight percent water produced during pickling treatment in connection with a cold rolling step of stainless steel processing; kneading the sludge cake containing 2-15 weight percent water with a mixture of dust produced during stainless steel making and scale produced during a hot rolling step of stainless steel processing, thereby obtaining a kneaded mass; adding to said kneaded mass 1 to 5 weight percent of an organic binder and less than 5 weight percent of an inorganic binder, said weight percents being based upon the solid components of said kneaded mass; adjusting the water content while kneading to obtain a water content in the range of 8 to 20 weight percent of the total kneaded mass; shaping the kneaded mass under pressure into the form of a briquette; heating the briquette to reduce its water content; charging one or more briquettes, together with a carbonaceous reducing agent into an electric furnace for pyrometallurgically reduction refining to exact metal from such briquettes.
Claim 2
Independent Claim
190 words
A method of treating waste produced during stainless steel making and processing, comprising: forming a sludge cake containing 2-5 weight percent water by dehydrating slurry-like pickling sludge containing 30-70 weight percent water produced during pickling treatment in connection with a cold rolling step of stainless steel processing; kneading the sludge cake containing 2-15 weight percent water with a mixture of dust produced during stainless steel making and scale produced during a hot rolling step of stainless steel processing, thereby obtaining a kneaded mass; adding to said kneaded mass 1 to 5 weight percent of an organic binder and less than 5 weight percent of an inorganic binder, said weight percents being based upon the solid components of said kneaded mass; adjusting the water content while kneading to obtain a water content in the range of 8 to 20 weight percent of the total kneaded mass; shaping the kneaded mass under pressure into the form of a briquette; heating the briquette to reduce its water content; charging one or more briquettes, together with a carbonaceous reducing agent into an electric furnace for pyrometallurgically reduction refining to exact metal from such briquettes.
Claim 3
Dependent Claim
60 words
A method of treating waste produced during stainless steel making and processing as claimed in claim 1, wherein said briquette is charged together with a carbonaceous reducing agent and with a flux into the electric furnace in which refining is effected to extract a metal component from said briquette to reuse said metal component as a steel making raw material.
Claim 4
Dependent Claim
33 words
A method of treating waste produced during a stainless steel making and processing as claimed in claim 1, wherein said organic binder comprises a pulp waste liquid, molasses, tar emulsion, or carboxymethyl cellulose.
Claim 5
Dependent Claim
26 words
A method of treating waste produced during a stainless steel making and processing as claimed in claim 1, wherein said inorganic binder comprises bentonite or pozzuolan.
Claim 6
Dependent Claim
36 words
A method of treating waste produced during a stainless steel making and processing as claimed in claim 1, wherein said kneaded mass is shaped under a pressure of 1,000 to 4,000 Kg/cm 2 into said briquette.
Claim 7
Dependent Claim
41 words
A method of treating waste produced during a stainless steel making and processing as claimed in claim 1, wherein said briquette after heating contains less than 5 wt.% of water and has a squeezing strength on the order of 50 Kg/unit.
Claim 8
Dependent Claim
27 words
A method of treating waste produced during a stainless steel making and processing as claimed in claim 1, wherein said carbonaceous reducing agent comprises charcoal or coke.
Claim 9
Dependent Claim
26 words
A method of treating waste produced during a stainless steel making and processing as claimed in claim 1, wherein said flux comprises silica or caustic lime.
References Cited (Backward Citations)
US1312218A
Cited
US1536033A
Cited
US2176689A
Cited
US2582469A
Cited
US2582386A
Cited
DE1039546B
Cited
GB853532A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-25 | 1980-07-26 | 1981-01-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-25 | 1984-07-26 | 1985-01-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-25 | 1988-07-26 | 1989-01-25 | $7700.00 | Window Closed / Lapsed |