Method of making a through-hardened scale-free forged powdered metal article without heat treatment after forging
Assignee: Federal Mogul LLC
•
Filing: 1973-09-24
•
Granted: 1977-01-11
•
Expires: 1993-09-24
Abstract
Abstract A method of making forged powdered iron base metal articles of high Rc hardness without need for further machining, surface treatment nor heat treatment after quenching comprising forming a pre-alloyed metal powder, compressing said powder into a briquette, sintering said briquette into a preform, heating said preform to a temperature above its austenizing temperature, forging said preform while above its austenizing temperature into a forged article, permitting the article to cool to approximately its austenizing temperature, and promptly quenching said forged article in a quenching batch.
Inventors
- 👤 Myron C. Sarnes
- 👤 Robert N. Haynie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 17:08
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/17; B22F3/24
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
163 words
A method of making a through-hardened scale-free forged powdered metal article having a density of at least about 99.5% of theoretical, a surface hardness of at least Rc 40, and an as forged dimension requiring no further machining other than surface grinding, all directly from quenching comprising: compressing an iron alloy powder into a briquette, sintering said briquette into a sintered preform; adjusting the temperature of said preform to such degree as to put said preform in an austenetic condition; forging said heated preform in one step while at said austenetic condition into a forged article; quenching said forged article in an oil quenching bath substantially immediately after said forging step while remaining in said austenetic condition; and removing said quenched forged article from the quenching bath, and stress relieving said forged article to produce a forged powdered metal article having a surface hardness of at least Rc 40 and a surface finish and dimension requiring no further machining other than surface grinding.
Claim 2
Independent Claim
163 words
A method of making a through-hardened scale-free forged powdered metal article having a density of at least about 99.5% of theoretical, a surface hardness of at least Rc 40, and an as forged dimension requiring no further machining other than surface grinding, all directly from quenching comprising: compressing an iron alloy powder into a briquette, sintering said briquette into a sintered preform; adjusting the temperature of said preform to such degree as to put said preform in an austenetic condition; forging said heated preform in one step while at said austenetic condition into a forged article; quenching said forged article in an oil quenching bath substantially immediately after said forging step while remaining in said austenetic condition; and removing said quenched forged article from the quenching bath, and stress relieving said forged article to produce a forged powdered metal article having a surface hardness of at least Rc 40 and a surface finish and dimension requiring no further machining other than surface grinding.
Claim 3
Dependent Claim
32 words
The method of claim 1, wherein the powdered alloy composition comprises, for each 100% by weight, 0.25 to 0.5% manganese, 0.25 to 0.5% nickel, 0.2 to 0.9% carbon and the remainder iron.
Claim 4
Dependent Claim
32 words
The method of claim 2, wherein the sintering of said briquette is accomplished in a gaseous atmosphere of high carbon potential and provides a carburizing effect on the surface of the preform.
Claim 5
Dependent Claim
15 words
The method of claim 3, wherein the powdered alloy composition comprises 0.5 to 0.9% carbon.
Claim 6
Dependent Claim
67 words
The method of claim 1, wherein the adjustment of the preform temperature prior to forging is carried out immediately after sintering to conserve heat energy by utilizing the residual heat of the sintered (article) preform toward reaching an austenizing temperature range which assures the preform being in an austenetic condition and also by eliminating the necessity of expending heat in subsequent carburization to attain the desired hardness.
Claim 7
Dependent Claim
28 words
The method of claim 1, wherein following said forging step and prior to said quenching step the temperature of the forged article is allowed to become substantially stabilized.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-01-11 | 1980-07-12 | 1981-01-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-01-11 | 1984-07-12 | 1985-01-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-01-11 | 1988-07-12 | 1989-01-11 | $7700.00 | Window Closed / Lapsed |