Molding compounds
Assignee: Owens Corning
•
Filing: 1974-09-03
•
Granted: 1976-12-21
•
Expires: 1994-09-03
Abstract
Abstract The surface characteristics, including shrink and gloss of molded thermosetting resin compounds, are improved by incorporating into the thermosetting resin a thermoplastic composition produced by the polymerization of a monomer with unsaturated elastomeric polymers.
Inventors
- 👤 Michael G. Roberts
- 👤 Charles E. Bolen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:30
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/06; Y; Y10; Y10S; Y10S525/00; Y10S525/911; Y10S525/921
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
113 words
A moldable composition comprising: a. an unsaturated, crosslinkable thermosetting resin; b. an ethylenically unsaturated first monomer; c. a thermoplastic resin soluble in said first monomer, said thermoplastic resin comprising the reaction product of a second monomer with a mixture comprising first and second unsaturated elastomeric polymers, said first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 43,000 to about 38,000, said second unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000, said thermoplastic resin being present in said moldable composition in an amount sufficient to improve at least one property of said thermosetting resin upon molding.
Claim 2
Dependent Claim
113 words
A moldable composition comprising: a. an unsaturated, crosslinkable thermosetting resin; b. an ethylenically unsaturated first monomer; c. a thermoplastic resin soluble in said first monomer, said thermoplastic resin comprising the reaction product of a second monomer with a mixture comprising first and second unsaturated elastomeric polymers, said first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 43,000 to about 38,000, said second unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000, said thermoplastic resin being present in said moldable composition in an amount sufficient to improve at least one property of said thermosetting resin upon molding.
Claim 3
Dependent Claim
28 words
The composition of claim 1 in which said unsaturated crosslinkable thermosetting resin is an unsaturated polyester and said ethylenically unsaturated first monomer is copolymerizable with said unsaturated polyester.
Claim 4
Dependent Claim
42 words
The composition of matter of claim 1 wherein said thermoplastic resin is produced from about 0.1 to about 7.5 weight percent of said first unsaturated elastomeric polymer and from about 0.1 to about 15 weight percent of said second unsaturated elastomeric polymer.
Claim 5
Dependent Claim
71 words
The composition of claim 1 wherein said thermoplastic resin is produced of from about 0.5 to about 5 weight percent of an unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 60,000 to about 200,000 and from about 0.5 to about 9 weight percent of an unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000.
Claim 6
Dependent Claim
41 words
The composition of claim 1 wherein said first unsaturated elastomeric polymer is a styrene-butadiene rubber having a weight average molecular weight of about 100,000 and said second elastomeric polymer is a weight hydroxy-terminated polybutadiene having a molecular weight of about 1,000.
Claim 7
Dependent Claim
35 words
The composition of claim 1 in which said thermoplastic resin is blended with said thermosetting resin on a monomer-free basis in a weight ratio of from about 1 to 1 to about 1 to 10.
Claim 8
Dependent Claim
35 words
The composition of claim 1 in which said thermoplastic resin is blended with said thermosetting resin on a monomer-free basis in a weight ratio of from about 1 to 2 to about 1 to 5.
Claim 9
Dependent Claim
31 words
The composition of claim 1 in which said thermoplastic resin is blended with said thermosetting resin on a monomer-free basis in a weight ratio of from about 1 to about 3.
Claim 10
Dependent Claim
44 words
The composition of claim 1 where said first unsaturated elastomeric polymer is a styrene-butadiene copolymer having a weight average molecular weight of about 83,000 and said second unsaturated elastomeric polymer is a polybutadiene having a weight average molecular weight of about 500 to 1000.
Claim 11
Dependent Claim
43 words
The composition of claim 1 in which said first unsaturated elastomeric polymer is employed in an amount within the range from about 0.1 to about 7.5 weight percent of a polymerizable mixture comprising the monomer and said first and said second unsaturated elastomers.
Claim 12
Dependent Claim
43 words
The composition of claim 1 in which said second unsaturated elastomeric polymer is employed in an amount within the range from about 0.1 to about 15 weight percent of a polymerizable mixture comprising the monomer and said first and said second unsaturated elastomers.
Claim 13
Dependent Claim
41 words
The composition of claim 1 in which said thermoplastic resin is produced in a polymerization mixture containing up to about 3 weight percent of a monofunctional or polyfunctional organic acid or organic acid anhydride containing one reactive double bond per molecule.
Claim 14
Dependent Claim
35 words
The composition of claim 1 in which said thermoplastic resin is produced employing up to 40 weight percent of a comonomer selected from the group consisting of methyl methacrylate, ethyl acrylate, acrylonitrile and vinyl pyridine.
Claim 15
Dependent Claim
69 words
The composition of claim 1 in which said first and second unsaturated elastomeric polymers each contain not less than 10 weight percent of a diene and said composition is produced employing up to about 3 weight percent acrylic acid, about 7.5 weight percent of said first unsaturated elastomeric polymer, about 15 weight percent of said second unsaturated elastomer and about 72 to about 73 weight percent of a monomer.
Claim 16
Dependent Claim
26 words
The composition of claim 1 in which said thermosetting resin and said thermoplastic resin are combined in contact with a crosslinking agent and a gelling agent.
Claim 17
Dependent Claim
8 words
The composition of claim 1 containing glass fibers.
Claim 18
Dependent Claim
49 words
The composition of claim 1 in which said moldable composition comprises about 16 weight percent of said thermosetting resin as a syrup containing about 33 percent solids, about 11 weight percent of said thermoplastic resin as a syrup containing about 33 percent solids and about 30 weight percent glass.
Claim 19
Dependent Claim
16 words
The composition of claim 2 in which said first monomer and said second monomer comprise styrene.
Claim 20
Independent Claim
125 words
A method of producing a molded composition which comprises: a. forming a mixture comprising an unsaturated, crosslinkable thermosetting resin, an ethylenically unsaturated first monomer and a thermoplastic resin soluble in said first monomer, said thermoplastic resin comprising the reaction product of a second monomer with a mixture comprising first and second unsaturated elastomeric polymers, said first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 43,000 to about 380,000, said second unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000, said thermoplastic resin being present in said mixture in an amount sufficient to improve at least one property of said thermosetting resin upon molding; and, b. molding said mixture.
Claim 21
Independent Claim
125 words
A method of producing a molded composition which comprises: a. forming a mixture comprising an unsaturated, crosslinkable thermosetting resin, an ethylenically unsaturated first monomer and a thermoplastic resin soluble in said first monomer, said thermoplastic resin comprising the reaction product of a second monomer with a mixture comprising first and second unsaturated elastomeric polymers, said first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 43,000 to about 380,000, said second unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000, said thermoplastic resin being present in said mixture in an amount sufficient to improve at least one property of said thermosetting resin upon molding; and, b. molding said mixture.
Claim 22
Dependent Claim
16 words
The method of claim 19 in which mixture is molded in contact with a gelling agent.
Claim 23
Dependent Claim
30 words
The method of claim 19 in which said first and said second unsaturated elastomeric polymers are selected from the group consisting of polybutadienes, styrene-butadiene block polymers and styrene-butadiene random copolymers.
Claim 24
Dependent Claim
32 words
The method of claim 21 in which said polybutadiene has a 1,4-trans content of about 30 percent, a 1,4-bis content of about 35 percent and a 1,2-vinyl content of about 35 percent.
Claim 25
Dependent Claim
32 words
The method of claim 21 in which said polybutadiene has a 1,4-trans content of about 60 percent, a 1,4-cis content of about 20 percent and a 1,2-vinyl content of about 20 percent.
Claim 26
Dependent Claim
35 words
The method of claim 21 in which said thermosetting resin is a polyester, said first monomer is styrene and said second monomer is styrene and said mixture is molded in contact with a gelling agent.
Claim 27
Dependent Claim
69 words
The method of claim 24 in which said polyester is produced employing a monofunctional or polyfunctional organic acid or anhydride which is reactive with said first monomer, a first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 60,000 to about 200,000 and a second elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000.
Claim 28
Dependent Claim
49 words
The method of claim 24 in which said organic acid is acrylic acid, said first unsaturated elastomeric polymer is a styrene-butadiene rubber having a weight average molecular weight of about 100,000 and said second elastomeric polymer is a hydroxy-terminated polybutadiene having a weight average molecular weight of about 1,000.
Claim 29
Dependent Claim
113 words
A molded composition comprising: a. a continuous phase comprising a thermosetting resin; and, b. a disperse phase within said continuous phase, said disperse phase being derived from a thermoplastic resin comprising the reaction product of a monomer with a mixture comprising first and second unsaturated elastomeric polymers, first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 43,000 to about 380,000, said second unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000, said thermoplastic resin being present in said thermosetting resin in an amount sufficient to improve at least one property of said thermosetting resin upon molding.
Claim 30
Dependent Claim
113 words
A molded composition comprising: a. a continuous phase comprising a thermosetting resin; and, b. a disperse phase within said continuous phase, said disperse phase being derived from a thermoplastic resin comprising the reaction product of a monomer with a mixture comprising first and second unsaturated elastomeric polymers, first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 43,000 to about 380,000, said second unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000, said thermoplastic resin being present in said thermosetting resin in an amount sufficient to improve at least one property of said thermosetting resin upon molding.
Claim 31
Independent Claim
113 words
A method of improving the properties of a thermosetting composition upon molding which comprises: a. incorporating into a continuous phase thermosetting composition a disperse phase comprising a thermoplastic resin comprising the reaction product of a monomer with a mixture comprising first and second unsaturated elastomeric polymers, said first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 43,000 to about 380,000, said second unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000, said thermoplastic resin being present in said thermosetting resin in an amount sufficient to improve at least one property of said thermosetting resin upon molding.
Claim 32
Independent Claim
113 words
A method of improving the properties of a thermosetting composition upon molding which comprises: a. incorporating into a continuous phase thermosetting composition a disperse phase comprising a thermoplastic resin comprising the reaction product of a monomer with a mixture comprising first and second unsaturated elastomeric polymers, said first unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 43,000 to about 380,000, said second unsaturated elastomeric polymer having a weight average molecular weight within the range of from about 500 to about 40,000, said thermoplastic resin being present in said thermosetting resin in an amount sufficient to improve at least one property of said thermosetting resin upon molding.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-21 | 1980-06-21 | 1980-12-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-21 | 1984-06-21 | 1984-12-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-21 | 1988-06-21 | 1988-12-21 | $7700.00 | Window Closed / Lapsed |