Sapphire growth from the melt using porous alumina raw batch material
Assignee: Corning Glass Works
•
Filing: 1975-03-10
•
Granted: 1976-12-21
•
Expires: 1995-03-10
Abstract
Abstract A method of growing sapphire crystals from the melt wherein a porous alumina raw material is used to replenish the melt during growth. The porous alumina is subjected to a high temperature, low pressure environment to remove adsorbed water and oxygen which, if allowed to enter the melt, would result in poor monocrystals. A sequence of steps is provided which allows a simultaneous outgassing of one charge of porous alumina and a continuous replenishing of the melt with porous alumina of a previously outgassed charge. The previously outgassed charge of alumina must be handled in a system devoid of water and oxygen to avoid readsorption of the impurities.
Inventors
- 👤 Gerald S. Meiling
- 👤 Walter L. Morgan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 08:48
CPC Classifications
C; C30; C30B; C30B15/00; C30B15/02
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
172 words
A method of growing substantially monocrystalline highly transparent alumina bodies on a seed crystal from the melt and using a polycrystalline, porous alumina raw batch material to continuously replenish the melt during successive growth cycles comprising the steps of: A. vacuum degassing a charge of the porous alumina raw batch material in a first chamber at a temperature sufficient to substantially eliminate adsorbed water and oxygen in the alumina, thereafter, B. transferring the charge of porous alumina in an inert atmosphere to a second chamber, C. maintaining an inert atmosphere in the second chamber, D. isolating the atmosphere of the first chamber from the atmosphere of the second chamber so that step A may be repeated independently of the atmosphere of the second chamber, E. metering the porous alumina under the inert atmosphere from the second chamber to the crucible in the crystal growing furnace at a rate sufficient to maintain the melt level in the crucible, and F. growing substantially monocrystalline alumina bodies from the melt in the crystal growing furnace.
Claim 2
Independent Claim
172 words
A method of growing substantially monocrystalline highly transparent alumina bodies on a seed crystal from the melt and using a polycrystalline, porous alumina raw batch material to continuously replenish the melt during successive growth cycles comprising the steps of: A. vacuum degassing a charge of the porous alumina raw batch material in a first chamber at a temperature sufficient to substantially eliminate adsorbed water and oxygen in the alumina, thereafter, B. transferring the charge of porous alumina in an inert atmosphere to a second chamber, C. maintaining an inert atmosphere in the second chamber, D. isolating the atmosphere of the first chamber from the atmosphere of the second chamber so that step A may be repeated independently of the atmosphere of the second chamber, E. metering the porous alumina under the inert atmosphere from the second chamber to the crucible in the crystal growing furnace at a rate sufficient to maintain the melt level in the crucible, and F. growing substantially monocrystalline alumina bodies from the melt in the crystal growing furnace.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein the water in the porous alumina raw batch is reduced to less than about 0.001% by weight.
Claim 4
Dependent Claim
45 words
The method of claim 1 wherein the temperature of the first chamber sufficient to reduce adsorbed impurities is between about 800°-1100° C and the vacuum degassing is accomplished with a vacuum pressure of between about 10.sup. -5 and 10.sup. -6 torr for about 8-36 hours.
Claim 5
Dependent Claim
24 words
The method of claim 1 wherein the vacuum degassing is accomplished at a pressure of not greater than about 5 × 10.sup. -5 torr.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-21 | 1980-06-21 | 1980-12-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-21 | 1984-06-21 | 1984-12-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-21 | 1988-06-21 | 1988-12-21 | $7700.00 | Window Closed / Lapsed |