Separation and/or purification of precious metals
Assignee: Swarsab Mining Exploration and Development Co Ltd
•
Filing: 1975-08-29
•
Granted: 1976-12-14
•
Expires: 1995-08-29
Abstract
Abstract A process for the treatment of a concentrate of by-metals comprises heating the concentrate at between 1100 DEG C and 1500 DEG C, preferably at about 1300 DEG C, in a gaseous stream which comprises oxygen. The heating step is effected for a period of time sufficient to ensure quantitative removal of one or more of lead, arsenic, silver, bismuth and/or tellurium and the oxidation of ruthenium, rhodium and iridium to their oxides.
Inventors
- 👤 Willem H. Pittie
- 👤 Gerhardus Overbeek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:46
CPC Classifications
C; C22; C22B; C22B11/00; C01; C01G; C01G5/00; C01G5/003; C22B11/04; C22B3/00; C22B3/20; C22B3/26; C22B3/262; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
103 words
A process for the recovery of rhodium, ruthenium, iridium and osmium values from a concentrate containing said values as well as impurities selected from the group consisting essentially of lead, arsenic, silver, bismuth and tellurium, said process comprising (a) heating said concentrate at a temperature of between about 1100° C. and 1500° C. in a gaseous stream containing oxygen for a time sufficient to quantitatively volatilize and separate the impurities and the osmium values from said concentrate and to leave a residue containing oxidized ruthenium, rhodium and iridium values, and (b) collecting the volatilized impurities and osmium values removed by said gas stream.
Claim 2
Dependent Claim
103 words
A process for the recovery of rhodium, ruthenium, iridium and osmium values from a concentrate containing said values as well as impurities selected from the group consisting essentially of lead, arsenic, silver, bismuth and tellurium, said process comprising (a) heating said concentrate at a temperature of between about 1100° C. and 1500° C. in a gaseous stream containing oxygen for a time sufficient to quantitatively volatilize and separate the impurities and the osmium values from said concentrate and to leave a residue containing oxidized ruthenium, rhodium and iridium values, and (b) collecting the volatilized impurities and osmium values removed by said gas stream.
Claim 3
Dependent Claim
14 words
A process as claimed in claim 1 in which the gaseous stream is air.
Claim 4
Dependent Claim
17 words
A process as claimed in claim 1 in which the heating is effected at about 1300° C.
Claim 5
Dependent Claim
27 words
A process as claimed in claim 1 in which collection is effected by scrubbing with an alkali hydroxide solution which dissolves said volatilized impurities and osmium values.
Claim 6
Dependent Claim
37 words
A process as claimed in claim 4 in which the dissolved impurities in the alkali hydroxide solution are precipitated therefrom by ethanol leaving the osmium values in solution, and after separation, the dissolved osmium values are precipitated.
Claim 7
Dependent Claim
56 words
A process as claimed in claim 1 in which the residue containing oxidized ruthenium, rhodium and iridium values is fused with potassium hydroxide, the resultant melt is solidified and leached with water to dissolve the ruthenium values to leave an insoluble residue containing the rhodium and iridium values, after separation the dissolved ruthenium values are precipitated.
Claim 8
Dependent Claim
25 words
A process as claimed in claim 6 in which the fusion is carried out at about 700° C for a period of about 90 minutes.
Claim 9
Dependent Claim
48 words
A process as claimed in claim 6 in which the insoluble residue is treated with both hydrochloric acid and hydrogen peroxide in an autoclave to dissolve rhodium and iridium values and to leave a further insoluble residue, and after separation the dissolved rhodium and iridium values are precipitated.
Claim 10
Dependent Claim
17 words
A process as claimed in claim 8 in which the autoclave is heated to about 150° C.
References Cited (Backward Citations)
US3413114A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-12-14 | 1980-06-14 | 1980-12-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-12-14 | 1984-06-14 | 1984-12-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-12-14 | 1988-06-14 | 1988-12-14 | $7700.00 | Window Closed / Lapsed |