Tack free polymerizable polyester compositions
Assignee: Occidental Chemical Corp
•
Filing: 1975-06-27
•
Granted: 1976-11-30
•
Expires: 1995-06-27
Abstract
Abstract Polymerizable polyester compositions containing a saturated polyester having three or more terminal carboxylic acid groups and an hydroxyl number of less than about 10 are provided. Such compositions are free from tackiness in the uncured state and which on curing are resistant to shrinkage and have improved surface smoothness. The compositions are useful as sheet molding compounds.
Inventors
- 👤 Raymond R. Hindersinn
- 👤 Jeffrey E. Selley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:05
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/06; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
143 words
A polymerizable polyester composition of components comprising: 1. a saturated polyester containing three or more terminal carboxylic acid groups and having a molecular weight of about 2,000 to about 25,000, and an acid number of from about 7 to about 170 and a hydroxyl number of less than about 10, such polyester generally being terminated with at least one moiety having at least two unreacted carboxylic acid groups; 2. an ⊕, β, -ethylenically unsaturated polyester of a diol and an α, β-ethylenically unsaturated dicarboxylic compound, and 3. an α, β-ethylenically unsaturated monomer copolymerizable with said unsaturated polyester; said saturated polyester being present in the amount of at least about 5 parts by weight and said unsaturated polyester being present in the amount of at least about 30 parts by weight per 100 parts by weight of the mixture of polyesters and copolymerizable monomer.
Claim 2
Dependent Claim
143 words
A polymerizable polyester composition of components comprising: 1. a saturated polyester containing three or more terminal carboxylic acid groups and having a molecular weight of about 2,000 to about 25,000, and an acid number of from about 7 to about 170 and a hydroxyl number of less than about 10, such polyester generally being terminated with at least one moiety having at least two unreacted carboxylic acid groups; 2. an ⊕, β, -ethylenically unsaturated polyester of a diol and an α, β-ethylenically unsaturated dicarboxylic compound, and 3. an α, β-ethylenically unsaturated monomer copolymerizable with said unsaturated polyester; said saturated polyester being present in the amount of at least about 5 parts by weight and said unsaturated polyester being present in the amount of at least about 30 parts by weight per 100 parts by weight of the mixture of polyesters and copolymerizable monomer.
Claim 3
Dependent Claim
36 words
The composition of claim 1 wherein the copolymerizable monomer is present in the amount of about 20 to about 60 parts by weight per 100 parts by weight of the mixture of polyesters and copolymerizable monomer.
Claim 4
Dependent Claim
14 words
The composition of claim 1 wherein the composition also comprises an inorganic thickening agent.
Claim 5
Dependent Claim
28 words
The composition of claim 3 wherein the inorganic thickener is selected from the group consisting of magnesium oxide, magnesium hydroxide, basic magnesium carbonate, calcium hydroxide, and mixtures thereof.
Claim 6
Dependent Claim
62 words
The composition of claim 1 wherein the saturated polyester is obtained by reacting initially a diol with a dicarboxylic acid, anhydride, acid halide or diester to form a polyester having at least one terminal hydroxyl group and subsequently reacting the initially prepared polyester with a polycarboxylic acid or anhydride having at least three carboxy groups to prepare a carboxyl terminated saturated polyester.
Claim 7
Dependent Claim
36 words
The composition of claim 5 wherein the polyester initially formed is the product of reaction of a mixture of ethylene glycol and 1,4-butane diol with adipic acid, which polyester is subsequently reacted with 1,2,4-benzene tricarboxylic anhydride.
Claim 8
Dependent Claim
36 words
The composition of claim 5 wherein the polyester initially formed is the product of reaction of a mixture of ethylene glycol and 1,4-butane diol with adipic acid, which polyester is subsequently reacted with 1,2,4,5-benzene tetracarboxylic anhydride.
Claim 9
Dependent Claim
64 words
The composition of claim 1 wherein the saturated polyester is obtained by reacting initially a diol with a dicarboxylic acid or anhydride to form a polyester having at least one terminal hydroxyl group and subsequently reacting the initially prepared polyester with a mixture of a polycarboxylic acid having at least three carboxy groups and a dicarboxylic acid to prepare a carboxy terminated saturated polyester.
Claim 10
Dependent Claim
76 words
The composition of claim 8 wherein the polyester initially formed is the product of reaction of a mixture of ethylene glycol and 1,4 butane diol with adipic acid, which polyester is subsequently reacted with a mixture of 1,2,4,5-benzene tetracarboxylic anhydride and succinic adhydride wherein the 1,2,4,5-benzene tetracarboxylic anhydride is present in the amount of at least about 10 parts by weight per 100 parts by weight of the mixture of 1,2,4,5-benzene tetracarboxylic anhydride and succinic anhydride.
Claim 11
Dependent Claim
19 words
The composition of claim 9 wherein the 1,2,4,5-benzene tetracarboxylic anhydride and succinic anhydride are present in approximately equimolar amounts.
Claim 12
Dependent Claim
75 words
The composition of claim 9 wherein the polyester initially formed is the product of reaction of a mixture of ethylene glycol and 1,4-butane diol with adipic acid, which polyester is subsequently reacted with a mixture of 1,2,4-benzene tricarboxylic anhydride and succinic anhydride wherein the 1,2,4-benzene tricarboxylic anhydride is present in the amount of at least about 10 parts by weight per 100 parts by weight of the mixture of 1,2,4-benzene tricarboxylic anhydride and succinic anhydride.
Claim 13
Dependent Claim
19 words
The composition of claim 11 wherein the 1,2,4-benzene tricarboxylic anhydride and succinic anhydride are present in approximately equimolar amounts.
Claim 14
Dependent Claim
31 words
A thickened non-tacky sheet molding compound comprising a polymerizable polyester composition as defined in claim 1, a filler, an inorganic thickening agent, a free radical generating catalyst, and reinforcing glass fibers.
Claim 15
Dependent Claim
27 words
A thickened non-tacky sheet molding compound comprising a polymerizable polyester composition as defined in claim 1, a filler, a free radical generating catalyst, and reinforcing glass fibers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-30 | 1980-05-31 | 1980-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-30 | 1984-05-31 | 1984-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-30 | 1988-05-31 | 1988-11-30 | $7700.00 | Window Closed / Lapsed |