Process for preparing supported superacid catalysts suitable for alkylation of aromatic hydrocarbons
Assignee: Societa Italiana Resine SpA SIR
•
Filing: 1974-11-19
•
Granted: 1976-11-23
•
Expires: 1994-11-19
Abstract
Abstract Supported superacid catalysts active in the alkylation of aromatic hydrocarbons are obtained by treating an alumina-containing support at a temperature of at least 400° C and contacting the support at a temperature of at least 150° C with a Lewis or Bronsted acid defined by one of the formulae: MX n , HMX n +1 and MOX m , wherein M stands for a metal belonging to Groups IIIA, IVB, VA, VB and VIB of the Periodic System of Elements, X is a halogen (with the exception of iodine), n is an integer from 3 to 6 and m is an integer from 1 to 4.
Inventors
- 👤 George A. Olah
- 👤 Giuseppe Messina
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:47
CPC Classifications
C; C07; C07C; C07C2/00; C07C2/54; C07C2/64; C07C2/66; C07C2/68; B; B01; B01J; B01J27/00; B01J27/06; B01J27/08; B01J37/00; B01J37/22; C07C2521/00; C07C2521/02; C07C2521/04; C07C2523/00; C07C2523/12; C07C2523/16; C07C2523/24; C07C2523/26; C07C2523/28; C07C2523/30; C07C2527/00; C07C2527/06; C07C2527/08; C07C2527/12; C07C2527/1213; C07C2527/125; C07C2527/132; C07C2527/133; C07C2527/135
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
152 words
A method of preparing a superacid supported catalyst, active in the alkylation of aromatic hydrocarbons, comprising the steps of (1) heat-treating a support consisting essentially of alumina at a temperature of at least 400° C, and (2) contacting the thus treated support with at least one Lewis or Bronsted acid selected from the following classes: a. metal halides defined by the general formula MX n , b. compounds of the general formula HMX n +1 , and c. oxyhalides defined by the general formula MOX m , wherein H stands for hydrogen, O for oxygen, M for a metal selected in the Groups IIIA, IVB, VA, VB and VIB of the Periodic System of Elements, X for a halogen other than iodine, n is an integer from 3 to 6 and m is an integer from 1 to 4, and heat-treating at a temperature of at least 150° C during said contact.
Claim 2
Independent Claim
152 words
A method of preparing a superacid supported catalyst, active in the alkylation of aromatic hydrocarbons, comprising the steps of (1) heat-treating a support consisting essentially of alumina at a temperature of at least 400° C, and (2) contacting the thus treated support with at least one Lewis or Bronsted acid selected from the following classes: a. metal halides defined by the general formula MX n , b. compounds of the general formula HMX n +1 , and c. oxyhalides defined by the general formula MOX m , wherein H stands for hydrogen, O for oxygen, M for a metal selected in the Groups IIIA, IVB, VA, VB and VIB of the Periodic System of Elements, X for a halogen other than iodine, n is an integer from 3 to 6 and m is an integer from 1 to 4, and heat-treating at a temperature of at least 150° C during said contact.
Claim 3
Dependent Claim
11 words
The method of claim 1, wherein said support consists of alumina.
Claim 4
Dependent Claim
23 words
The method of claim 1, wherein said support consists essentially of at least 90% by weight alumina and less than 10 wt.% silica.
Claim 5
Dependent Claim
31 words
The method of claim 1, wherein said support consists essentially of alumina combined with at least one oxide chosen from the group consisting of boron, tungsten, molybdenium, thorium and chromium oxides.
Claim 6
Dependent Claim
30 words
The method of claim 1, wherein said support during step (1) is heat-treated at a temperature from 400° to 900° C for a period from 30 minutes to 10 hours.
Claim 7
Dependent Claim
28 words
The method of claim 1, wherein said support during step (1) is heat-treated at a temperature of about 600° C for a period from 3 to 4 hours.
Claim 8
Dependent Claim
18 words
The method of claim 1, wherein said temperature maintained during step (2) is from 150° to 500° C.
Claim 9
Dependent Claim
12 words
The method of claim 1, wherein said metal halides are metal fluorides.
Claim 10
Dependent Claim
26 words
The method of claim 8, wherein said metal fluorides are chosen from the group consisting of antimony, aluminium, niobium, tantalum, molybdenum, tungsten, titanium and boron fluorides.
Claim 11
Dependent Claim
40 words
The method of claim 1, wherein during step (2) at least one metal halide MX n in vapor form is contacted with said support at a temperature from 150° to 500° C for a period of at least 30 minutes.
Claim 12
Dependent Claim
36 words
The method of claim 10, wherein said support is contacted with at least one metal halide MX n in vapor form at a temperature of about 300° C during a period from 2 to 4 hours.
Claim 13
Dependent Claim
64 words
The method of claim 1, wherein step (2) comprises first impregnating the heat-treated support with at least one metal halide MX n dissolved in a solvent chosen from the group consisting of hydrocarbons, fluorocarbons, sulphur dioxide, hydrogen fluoride and fluorosulphonic acid, and then the impregnated support is heat-treated at a temperature from 150° to 500° C for a period of at least 30 minutes.
Claim 14
Dependent Claim
22 words
The method of claim 12, wherein in step (2) the impregnated support is heat-treated for a period from 2 to 6 hours.
Claim 15
Dependent Claim
83 words
The method of claim 1, wherein step (2) comprises first impregnating the heat-treated support with a solution of said metal halide in the form of a complex chosen from the group consisting of the complexes of metal halides MX n with sulphur dioxide, sulphur trioxide and ethers and ArH 2 +MX - n +1 complexes, Ar being an aryl radical, and then the impregnated support is heat-treated at a temperature from 150° to 500° C for a period of at least 30 minutes.
Claim 16
Dependent Claim
22 words
The method of claim 14, wherein in step (2) the impregnated support is heat-treated for a period from 2 to 6 hours.
Claim 17
Dependent Claim
19 words
The method of claim 1, wherein the said oxyhalides are chosen from the group of tantalum and niobium oxyfluorides.
Claim 18
Dependent Claim
24 words
The method of claim 12, wherein in step (2) said impregnating of said heat-treated support is conducted at a temperature of about 20°-25° C.
References Cited (Backward Citations)
US1939647A
Cited
US2536841A
Cited
US2965686A
Cited
US3551516A
Cited
US3515679A
Cited
US3746657A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-23 | 1980-05-24 | 1980-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-23 | 1984-05-24 | 1984-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-23 | 1988-05-24 | 1988-11-23 | $7700.00 | Window Closed / Lapsed |