Lightweight aggregate for concrete and method for making same
Assignee: Individual
•
Filing: 1974-07-24
•
Granted: 1976-11-16
•
Expires: 1994-07-24
Abstract
Abstract The invention provides a lightweight aggregate for eventual use in making concrete having commercially acceptable compressive strength. Bloating agents of iron oxide serve to greatly expand conventional aggregate under conventional heat treatment. Small beads of heat decomposable plastic may also be mixed with finely divided aggregate base material prior to pellet extrusion after which furnace heat treatment creates a strong, porous pellet. Modifications in handling the aggregate process improve product control and in some of the completed aggregate serve to seal outer surfaces of aggregate against fluid penetration.
Inventors
- 👤 Leon I. Kirschner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 06:37
CPC Classifications
C; C04; C04B; C04B20/00; C04B20/02; C04B20/04; C04B20/06; C04B20/068
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
104 words
An aggregate in pelletized form consisting of finely divided base material of the class consisting of rock, cinders, pumice, perlite, slag, and clay, as one ingredient and finely divided magnetic oxide of iron, as the other ingredient, intermixed therewith in the proportion of about 2 to 7% by weight of iron oxide to base material, said mixture being in bloated form by having been heated to a temperature of the order of about 2,000° F., said aggregate being characterized by great porosity, and substantial compressive strength, whereby when present in concrete utilizing such aggregate, such concrete has relatively light weight and normal compressive strength.
Claim 2
Dependent Claim
104 words
An aggregate in pelletized form consisting of finely divided base material of the class consisting of rock, cinders, pumice, perlite, slag, and clay, as one ingredient and finely divided magnetic oxide of iron, as the other ingredient, intermixed therewith in the proportion of about 2 to 7% by weight of iron oxide to base material, said mixture being in bloated form by having been heated to a temperature of the order of about 2,000° F., said aggregate being characterized by great porosity, and substantial compressive strength, whereby when present in concrete utilizing such aggregate, such concrete has relatively light weight and normal compressive strength.
Claim 3
Dependent Claim
24 words
The aggregate according to claim 1, wherein each pellet is the result of heat-treating an aqueous paste extrusion of said mixture in unbloated form.
Claim 4
Dependent Claim
61 words
The aggregate according to claim 2, wherein said pellets have enhanced porosity resulting from including heat decomposable plastic beads in the aqueous paste prior to extrusion, said beads originally having been between about 1/64 in. and about 1/16 in. in dimension, the amount of beads throughout said mixture being sufficient to provide desired porosity to said aggregate after said heat treatment.
Claim 5
Independent Claim
108 words
A method of making aggregate for use with Portland cement, said method comprising mixing base material in subdivided form, said base material being of the class consisting of rock, cinders, pumice, perlite, slag, and clay and finely divided magnetic oxide of iron in the proportion of about 2 to 7% by weight of iron oxide to base material, compacting the same to form pellets and heating to a temperature of the order of about 2,000° F to bloat the base material to create porous bodies, said porous bodies having substantial compressive strength and being useful with Portland cement for providing light weight concrete having substantially normal compressive strength.
Claim 6
Independent Claim
108 words
A method of making aggregate for use with Portland cement, said method comprising mixing base material in subdivided form, said base material being of the class consisting of rock, cinders, pumice, perlite, slag, and clay and finely divided magnetic oxide of iron in the proportion of about 2 to 7% by weight of iron oxide to base material, compacting the same to form pellets and heating to a temperature of the order of about 2,000° F to bloat the base material to create porous bodies, said porous bodies having substantial compressive strength and being useful with Portland cement for providing light weight concrete having substantially normal compressive strength.
Claim 7
Dependent Claim
42 words
The method according to claim 4, wherein said base material is made into a finely divided form, mixed with said magnetic oxide of iron and water to form a paste, extruded to form pellets and thereafter heated to bloat the base material.
Claim 8
Dependent Claim
64 words
The method according to claim 5, wherein small beads between about 1/64 and 1/16 inch of heat decomposable plastic material are mixed in the paste containing such base material and iron oxide, said beads being present in sufficient quantity to create the desired degree of porosity in the finished aggregate, the heat treatment serving to decompose said beads as part of the bloating process.
Claim 9
Dependent Claim
32 words
The method according to claim 6, wherein borax in the form of a colloidal gel is mixed with the pellet forming materials prior to extrusion in sufficient quantity to improve pellet extrusions.
References Cited (Backward Citations)
US2902379A
Cited
US2961399A
Cited
US3140956A
Cited
US3258349A
Cited
US3425577A
Cited
US3844812A
Cited
US3854972A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-16 | 1980-05-17 | 1980-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-16 | 1984-05-17 | 1984-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-16 | 1988-05-17 | 1988-11-16 | $7700.00 | Window Closed / Lapsed |