US3989666A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Crosslinker-platinum catalyst-inhibitor and method of preparation thereof
Assignee: Dow Silicones Corp
•
Filing: 1974-12-02
•
Granted: 1976-11-02
•
Expires: 1994-12-02
Abstract
Abstract A crosslinker-platinum catalyst-inhibitor is prepared by heating in a closed system for 10 to 30 hours at 50° C. to 90° C. a mixture of a siloxane having at least three silicone-bonded hydrogen atoms, an acetylenic alcohol and a platinum catalyst and then removing the unreacted acetylenic alcohol at reduced pressure and 20° C. to 30° C., a complex product is obtained which when combined with a vinyl containing siloxane polymer has an extended shelf-life but can be cured by heating. The complex product functions as a crosslinker, a catalyst and an inhibitor which retards the reactions of silicon-bonded hydrogen atoms with aliphatic unsaturation catalyzed by platinum.
Inventors
- 👤 Randolph G. Niemi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 09:02
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/38; C08G77/382; C08G77/398; C08K; C08K5/00; C08K5/0008; C08K5/0025; C08K5/04; C08K5/05; C08L83/06; C08G77/12; C08G77/20; C08G77/22; C08G77/24; C08G77/26; C08G77/48; C08G77/50; C08G77/52; C08G77/70
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
240 words
A method of preparing a crosslinker-platinum catalyst-inhibitor composition comprising mixing a siloxane having an average of at least three silicon-bonded hydrogen atoms per molecule, an acetylenic alcohol and a platinum catalyst to form a mixture, heating the mixture in a closed system for 10 to 30 hours at a temperature of from 50°C. to 90°C. and thereafter removing unreacted acetylenic alcohol by applying a reduced pressure of 700 to 750 millimeters of mercury for at least 10 hours at a temperature of from 20°C. to 30°C., said siloxane having an average of at least three silicon-bonded hydrogen atoms per molecule, there being in addition an average of up to two monovalent organic radicals per silicon atom selected from the group consisting of monovalent hydrocarbon radicals free of aliphatic unsaturation and monovalent fluorinated hydrocarbon radicals free of aliphatic unsaturation, the remaining valences of the silicon atoms being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals free of aliphatic unsaturation, divalent hydrocarbon ether radicals free of aliphatic unsaturation and divalent fluorinated arylene radicals wherein at least one divalent radical is a divalent oxygen atom and said divalent radicals linking silicon atoms, said siloxane being liquid at a temperature of 50°C. to 90°C. in said mixture, said acetylenic alcohol having a vapor pressure sufficient to be removed from the mixture after the heating step at the temperature and pressure specified for the removal of unreacted
Claim 2
Independent Claim
240 words
A method of preparing a crosslinker-platinum catalyst-inhibitor composition comprising mixing a siloxane having an average of at least three silicon-bonded hydrogen atoms per molecule, an acetylenic alcohol and a platinum catalyst to form a mixture, heating the mixture in a closed system for 10 to 30 hours at a temperature of from 50°C. to 90°C. and thereafter removing unreacted acetylenic alcohol by applying a reduced pressure of 700 to 750 millimeters of mercury for at least 10 hours at a temperature of from 20°C. to 30°C., said siloxane having an average of at least three silicon-bonded hydrogen atoms per molecule, there being in addition an average of up to two monovalent organic radicals per silicon atom selected from the group consisting of monovalent hydrocarbon radicals free of aliphatic unsaturation and monovalent fluorinated hydrocarbon radicals free of aliphatic unsaturation, the remaining valences of the silicon atoms being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals free of aliphatic unsaturation, divalent hydrocarbon ether radicals free of aliphatic unsaturation and divalent fluorinated arylene radicals wherein at least one divalent radical is a divalent oxygen atom and said divalent radicals linking silicon atoms, said siloxane being liquid at a temperature of 50°C. to 90°C. in said mixture, said acetylenic alcohol having a vapor pressure sufficient to be removed from the mixture after the heating step at the temperature and pressure specified for the removal of unreacted
Claim 3
Dependent Claim
7 words
The crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 4
Dependent Claim
7 words
The crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 5
Dependent Claim
40 words
The method in accordance with claim 1 in which the siloxane is a copolymer having an average of at least two trimethylsiloxy units, three dimethylsiloxane units and five methylhydrogensiloxane units, the acetylenic alcohol is 3-methyl-1-butyn-3-ol and the platinum catalyst is
Claim 6
Dependent Claim
7 words
The crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 7
Dependent Claim
7 words
The crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 8
Dependent Claim
106 words
A curable composition comprising 1. an organosilicon polymer having an average of from one to three groups per silicon atom selected from the group consisting of monovalent hydrocarbon radicals, aliphatic-unsaturation-free monovalent halohydrocarbon radicals and cyanoalkyl radicals, there being an average per molecule of (1) of at least two monovalent hydrocarbon radicals containing aliphatic unsaturation, the remaining valences of the silicon atoms of the said organosilicon polymer being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals, divalent hydrocarbon ether radicals and divalent haloarylene radicals, said divalent radicals linking silicon atoms, and 2. the crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 9
Dependent Claim
106 words
A curable composition comprising 1. an organosilicon polymer having an average of from one to three groups per silicon atom selected from the group consisting of monovalent hydrocarbon radicals, aliphatic-unsaturation-free monovalent halohydrocarbon radicals and cyanoalkyl radicals, there being an average per molecule of (1) of at least two monovalent hydrocarbon radicals containing aliphatic unsaturation, the remaining valences of the silicon atoms of the said organosilicon polymer being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals, divalent hydrocarbon ether radicals and divalent haloarylene radicals, said divalent radicals linking silicon atoms, and 2. the crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 10
Dependent Claim
106 words
A curable composition comprising 1. an organosilicon polymer having an average of from one to three groups per silicon atom selected from the group consisting of monovalent hydrocarbon radicals, aliphatic-unsaturation-free monovalent halohydrocarbon radicals and cyanoalkyl radicals, there being an average per molecule of (1) of at least two monovalent hydrocarbon radicals containing aliphatic unsaturation, the remaining valences of the silicon atoms of the said organosilicon polymer being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals, divalent hydrocarbon ether radicals and divalent haloarylene radicals, said divalent radicals linking silicon atoms, and 2. the crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 11
Dependent Claim
106 words
A curable composition comprising 1. an organosilicon polymer having an average of from one to three groups per silicon atom selected from the group consisting of monovalent hydrocarbon radicals, aliphatic-unsaturation-free monovalent halohydrocarbon radicals and cyanoalkyl radicals, there being an average per molecule of (1) of at least two monovalent hydrocarbon radicals containing aliphatic unsaturation, the remaining valences of the silicon atoms of the said organosilicon polymer being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals, divalent hydrocarbon ether radicals and divalent haloarylene radicals, said divalent radicals linking silicon atoms, and 2. the crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 12
Dependent Claim
18 words
The curable composition according to claim 5 wherein (1) is a triorganosiloxy-endblocked polydiorganosiloxane having a viscosity of at
Claim 13
Dependent Claim
12 words
The curable composition according to claim 7 wherein the radicals of (1)
Claim 14
Dependent Claim
18 words
The curable composition according to claim 6 wherein (1) is a triorganosiloxy-endblocked polydiorganosiloxane having a viscosity of at
Claim 15
Dependent Claim
11 words
The curable composition according to claim 9 wherein the radicals of
Claim 16
Independent Claim
172 words
A method of preparing a crosslinker-platinum catalyst-inhibitor composition comprising mixing a siloxane having an average of at least three silicon-bonded hydrogen atoms per molecule, an acetylenic alcohol and a platinum catalyst to form a mixture, heating the mixture in a closed system for 10 to 30 hours at a temperature of from 50°C. to 90°C., said siloxane having an average of at least three silicon-bonded hydrogen atoms per molecule, there being in addition an average of up to two monovalent organic radicals per silicon atom selected from the group consisting of monovalent hydrocarbon radicals free of aliphatic unsaturation and monovalent fluorinated hydrocarbon radicals free of aliphatic unsaturation, the remaining valences of the silicon atoms being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals free of aliphatic unsaturation, divalent hydrocarbon ether radicals free of aliphatic unsaturation and divalent fluorinated arylene radicals wherein at least one divalent radical is a divalent oxygen atom and said divalent radicals linking silicon atoms, said siloxane being liquid at a
Claim 17
Independent Claim
172 words
A method of preparing a crosslinker-platinum catalyst-inhibitor composition comprising mixing a siloxane having an average of at least three silicon-bonded hydrogen atoms per molecule, an acetylenic alcohol and a platinum catalyst to form a mixture, heating the mixture in a closed system for 10 to 30 hours at a temperature of from 50°C. to 90°C., said siloxane having an average of at least three silicon-bonded hydrogen atoms per molecule, there being in addition an average of up to two monovalent organic radicals per silicon atom selected from the group consisting of monovalent hydrocarbon radicals free of aliphatic unsaturation and monovalent fluorinated hydrocarbon radicals free of aliphatic unsaturation, the remaining valences of the silicon atoms being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals free of aliphatic unsaturation, divalent hydrocarbon ether radicals free of aliphatic unsaturation and divalent fluorinated arylene radicals wherein at least one divalent radical is a divalent oxygen atom and said divalent radicals linking silicon atoms, said siloxane being liquid at a
Claim 18
Dependent Claim
7 words
The crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 19
Dependent Claim
7 words
The crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 20
Dependent Claim
40 words
The method in accordance with claim 11 in which the siloxane is a copolymer having an average of at least two trimethylsiloxy units, three dimethylsiloxane units and five methylhydrogensiloxane units, the acetylenic alcohol is 3-methyl-1-butyn-3-ol and the platinum catalyst is
Claim 21
Dependent Claim
7 words
The crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 22
Dependent Claim
7 words
The crosslinker-platinum catalyst-inhibitor composition prepared by the
Claim 23
Dependent Claim
130 words
A curable composition comprising 1. an organosilicon polymer having an average of from one to three groups per silicon atom selected from the group consisting of monovalent hydrocarbon radicals, aliphatic-unsaturation-free monovalent halohydrocarbon radicals and cyanoalkyl radicals, there being an average per molecule of (1) of at least two monovalent hydrocarbon radicals containing aliphatic unsaturation, the remaining valences of the silicon atoms of the said organosilicon polymer being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals, divalent hydrocarbon ether radicals and divalent haloarylene radicals, said divalent radicals linking silicon atoms, and 2. the crosslinker-platinum catalyst-inhibitor composition prepared by the method of claim 11 wherein the amount of acetylenic alcohol is present in an amount sufficient to retard cure at room temperature and minimize
Claim 24
Dependent Claim
130 words
A curable composition comprising 1. an organosilicon polymer having an average of from one to three groups per silicon atom selected from the group consisting of monovalent hydrocarbon radicals, aliphatic-unsaturation-free monovalent halohydrocarbon radicals and cyanoalkyl radicals, there being an average per molecule of (1) of at least two monovalent hydrocarbon radicals containing aliphatic unsaturation, the remaining valences of the silicon atoms of the said organosilicon polymer being satisfied by divalent radicals selected from the group consisting of divalent oxygen atoms, divalent hydrocarbon radicals, divalent hydrocarbon ether radicals and divalent haloarylene radicals, said divalent radicals linking silicon atoms, and 2. the crosslinker-platinum catalyst-inhibitor composition prepared by the method of claim 13 wherein the amount of acetylenic alcohol is present in an amount sufficient to retard cure at room temperature and minimize
Claim 25
Dependent Claim
18 words
The curable composition according to claim 15 wherein (1) is a triorganosiloxy-endblocked polydiorganosiloxane having a viscosity of at
Claim 26
Dependent Claim
11 words
The curable composition according to claim 17 wherein the radicals of
Claim 27
Dependent Claim
18 words
The curable composition according to claim 16 wherein (1) is a triorganosiloxy-endblocked polydiorganosiloxane having a viscosity of at
Claim 28
Dependent Claim
16 words
The curable composition according to claim 19 wherein the radicals of (1) are methyl and vinyl.
References Cited (Backward Citations)
US3445420A
Cited
US3715334A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |