Method for the treatment of red mud
Assignee: Magyar Aluminiumipari Troeszt
•
Filing: 1975-03-11
•
Granted: 1976-11-02
•
Expires: 1995-03-11
Abstract
Abstract Disclosed is a method for the treatment of the red mud byproduct of the Bayer aluminum process, wherein limestone, hydrated lime or other CaO-containing material is added to the red mud in certain molar proportions to the ingredients of the red mud, then the mixture is further mixed with a reducing agent, and the entire mixture is subjected to a reducing heat treatment during the course of which the mix becomes softened or molten. The iron and the slag are separated from each other while the mix is still molten, or after it has been cooled, and then the Na and Al-content of the slag is extracted with a sodium carbonate solution containing a caustic, or with a sodium carbonate solution and a solution of a caustic in two steps.
Inventors
- 👤 Gyorgy Dobos
- 👤 Zoltan Felfoldi
- 👤 Gyula Horvath
- 👤 Gyorgy Kaptay
- 👤 Zoltan Osvald
- 👤 Karoly Solymar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 19:24
CPC Classifications
C; C22; C22B; C22B7/00; C22B7/04; C01; C01F; C01F7/00; C01F7/02; C01F7/04; C01F7/06; C01F7/066; C01F7/38; C21; C21B; C21B11/00; C21B3/00; C21B3/02; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y10; Y10S; Y10S75/00; Y10S75/958
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
159 words
In a method for the treatment of the red mud byproduct of aluminum manufacture said red mud containing Fe 2 O 3 , Al 2 O 3 , Na 2 O, SiO 2 and TiO 2 , wherein the red mud is subjected to a reducing heat treatment with an added reducing agent during the course of which said red mud is molten, the iron and slag that are formed are separated from each other, and subsequently leaching out the Na and Al contents of the solidified slag, the improvement in combination therewith comprising adding to the red mud which contains more than 5% Na 2 O a CaO-containing ingredient in the following molar ratios and based on the weight of dry red mud ##EQU2## carrying out the reducing heat treatment and then leaching the Na and Al-contents of the solidified slag with a caustic solution and sodium carbonate, the entire process requiring only a single reducing heat treatment.
Claim 2
Dependent Claim
159 words
In a method for the treatment of the red mud byproduct of aluminum manufacture said red mud containing Fe 2 O 3 , Al 2 O 3 , Na 2 O, SiO 2 and TiO 2 , wherein the red mud is subjected to a reducing heat treatment with an added reducing agent during the course of which said red mud is molten, the iron and slag that are formed are separated from each other, and subsequently leaching out the Na and Al contents of the solidified slag, the improvement in combination therewith comprising adding to the red mud which contains more than 5% Na 2 O a CaO-containing ingredient in the following molar ratios and based on the weight of dry red mud ##EQU2## carrying out the reducing heat treatment and then leaching the Na and Al-contents of the solidified slag with a caustic solution and sodium carbonate, the entire process requiring only a single reducing heat treatment.
Claim 3
Dependent Claim
21 words
The process of claim 1, further comprising the adding of a reducing agent to the red mud before said heat treatment.
Claim 4
Dependent Claim
17 words
The process of claim 1, wherein said reducing heat treatment is carried out rapidly, within 20 minutes.
Claim 5
Dependent Claim
17 words
The process of claim 1, wherein after solidification iron is separated from the slag by magnetic separation.
Claim 6
Dependent Claim
17 words
The process of claim 1, wherein the iron and slag are separated from each other while molten.
Claim 7
Dependent Claim
27 words
The process of claim 1, wherein the Na and Al contents of the slag are leached in a single step with a sodium carbonate with caustic solution.
Claim 8
Dependent Claim
32 words
The process of claim 1, wherein the Na and Al contents of the slag are leached in a plurality of steps, with a caustic solution and then with a sodium carbonate solution.
References Cited (Backward Citations)
US2408241A
Cited
US2830892A
Cited
US2964383A
Cited
US3094378A
Cited
US3295961A
Cited
US3211524A
Cited
US3495973A
Cited
US3776717A
Cited
US3876749A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |