Method for producing a hot pressed component
Assignee: ZF International UK Ltd
•
Filing: 1972-07-28
•
Granted: 1976-11-02
•
Expires: 1992-07-28
Abstract
Abstract A method of producing hot pressed products, especially products of complex shapes, wherein the material from which the component is formed is hot pressed between a plurality of die parts of which at least one is of substantially uniform density and substantially compressible. This enables the shape of the die part to conform exactly or nearly so to the shape of the body being sintered throughout hot pressing, thereby resulting in obtainment of products of complex shapes.
Inventors
- 👤 Dexter William Smith
- 👤 Roland John Lumby
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:02
CPC Classifications
C; C04; C04B; C04B33/00; C04B33/32; C04B33/326; B; B22; B22F; B22F3/00; B22F3/12; B22F3/14; B28; B28B; B28B3/00; B28B3/02; B28B3/025
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
179 words
A method of producing a hot pressed component comprising the steps of: positioning material to be hot pressed in a die cavity defined between a pair of die parts, at least one of the die parts being substantially compressible during hot pressing of said material and being of substantially uniform density, and applying pressure to the die parts at an elevated temperature so as to compress said one die part and (simultaneously hot press) so as to cause pressure to be transmitted by the die parts to said material so that the material is simultaneously hot pressed by the die parts into said components, the material of said one die part different from the material to be hot pressed, and the density of said one die part remaining substantially uniform after hot pressing and being arranged so that the ratio of the density thereof, prior to hot pressing, to the density thereof, after hot pressing, is substantially equal to the ratio of the density of the material to be hot pressed to the density of the hot pressed component.
Claim 2
Independent Claim
179 words
A method of producing a hot pressed component comprising the steps of: positioning material to be hot pressed in a die cavity defined between a pair of die parts, at least one of the die parts being substantially compressible during hot pressing of said material and being of substantially uniform density, and applying pressure to the die parts at an elevated temperature so as to compress said one die part and (simultaneously hot press) so as to cause pressure to be transmitted by the die parts to said material so that the material is simultaneously hot pressed by the die parts into said components, the material of said one die part different from the material to be hot pressed, and the density of said one die part remaining substantially uniform after hot pressing and being arranged so that the ratio of the density thereof, prior to hot pressing, to the density thereof, after hot pressing, is substantially equal to the ratio of the density of the material to be hot pressed to the density of the hot pressed component.
Claim 3
Dependent Claim
22 words
A method as claimed in claim 1 wherein said die cavity is substantially completely filled by the material to be hot pressed.
Claim 4
Dependent Claim
29 words
A method as claimed in claim 1 wherein the material to be hot pressed is a silicon nitride compact and said one die part is formed of boron nitride.
Claim 5
Independent Claim
194 words
A method of producing a hot pressed component comprising the steps of positioning material to be hot pressed in a die cavity defined between a pair of die parts, at least one of the die parts being substantially compressible during hot pressing of said material and being of substantially uniform density, and applying pressure to the die parts at an elevated temperature so as to compress said one die part and so as to cause pressure to be transmitted by the die parts to said material so that the material is simultaneously hot pressed by the die parts into said component, the density of said one die part remaining substantially uniform after hot pressing and being arranged so that the ratio of the density thereof prior to hot pressing to the density thereof after hot pressing is different from the ratio of the density of the material to be hot pressed to the density of the hot pressed component, and said cavity being less than substantially completely filled by the material to be hot pressed and gradually conforming to the shape of said material as the material is compressed during the hot pressing operation.
Claim 6
Independent Claim
194 words
A method of producing a hot pressed component comprising the steps of positioning material to be hot pressed in a die cavity defined between a pair of die parts, at least one of the die parts being substantially compressible during hot pressing of said material and being of substantially uniform density, and applying pressure to the die parts at an elevated temperature so as to compress said one die part and so as to cause pressure to be transmitted by the die parts to said material so that the material is simultaneously hot pressed by the die parts into said component, the density of said one die part remaining substantially uniform after hot pressing and being arranged so that the ratio of the density thereof prior to hot pressing to the density thereof after hot pressing is different from the ratio of the density of the material to be hot pressed to the density of the hot pressed component, and said cavity being less than substantially completely filled by the material to be hot pressed and gradually conforming to the shape of said material as the material is compressed during the hot pressing operation.
Claim 7
Dependent Claim
27 words
A method as claimed in claim 4 wherein said one die part is formed from a powder material being non-reactive with the material to be hot pressed.
Claim 8
Dependent Claim
29 words
A method as claimed in claim 4 wherein the material to be hot pressed is a silicon nitride compact and said one die part is formed of boron nitride.
Claim 9
Dependent Claim
27 words
A method as claimed in claim 1 wherein said one die part is formed from a powder material being non-reactive with the material to be hot pressed.
References Cited (Backward Citations)
US2411379A
Cited
US2540457A
Cited
US2870484A
Cited
US3067465A
Cited
US3213491A
Cited
US3619861A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-11-02 | 1980-05-03 | 1980-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-11-02 | 1984-05-03 | 1984-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-11-02 | 1988-05-03 | 1988-11-02 | $7700.00 | Window Closed / Lapsed |