Cobaltic promoters in unsaturated polyester resin sheet molding and bulk molding compound
Assignee: Air Products and Chemicals Inc
•
Filing: 1975-04-30
•
Granted: 1976-10-26
•
Expires: 1995-04-30
Abstract
Abstract This invention relates to an improvement in a process for preparing unsaturated polyester resins which are chemically thickened with a Group II metal oxide or hydroxide and the resulting product. The improvement for extending the shelf life of said molding compound while providing for enhanced curing rates at the molding temperature comprises: Incorporating at least an effective proportion of a cobaltic promotor in said molding compound for selectively extending the shelf life of said molding compound and for providing enhanced cure rate.
Inventors
- 👤 Melville W. Uffner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:07
CPC Classifications
C; C08; C08F; C08F299/00; C08F299/02; C08F299/04; C08F299/0442; C08F299/0464; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
91 words
In a process for preparing a molding compound comprising mixing an unsaturated polyester resin with an unsaturated monomer, soluble and copolymerizable therewith, and chemically thickening with a Group II metal oxide or hydroxide, the improvement for extending the shelf life while providing enhanced cure rate at the molding temperature for said molding compound which comprises: incorporating at least an effective proportion of a cobaltic promoter having a valence of 3 and soluble in said molding compound for selectively extending the shelf life and enhancing the cure rate of said molding compound.
Claim 2
Dependent Claim
91 words
In a process for preparing a molding compound comprising mixing an unsaturated polyester resin with an unsaturated monomer, soluble and copolymerizable therewith, and chemically thickening with a Group II metal oxide or hydroxide, the improvement for extending the shelf life while providing enhanced cure rate at the molding temperature for said molding compound which comprises: incorporating at least an effective proportion of a cobaltic promoter having a valence of 3 and soluble in said molding compound for selectively extending the shelf life and enhancing the cure rate of said molding compound.
Claim 3
Dependent Claim
12 words
The process of claim 1 wherein said molding compound contains a catalyst.
Claim 4
Dependent Claim
22 words
The process of claim 2 wherein said catalyst is selected from the group consisting of a perester, a peroxide, and a hydroperoxide.
Claim 5
Dependent Claim
34 words
The process of claim 3 wherein said catalyst is included in said molding compound in a proportion of from about 0.25 to 2 parts by weight of the unsaturated polyester resin and unsaturated monomer.
Claim 6
Dependent Claim
35 words
The process of claim 4 wherein said cobaltic promoter is incorporated in said molding compound in a proportion for providing 0.006 to 0.036 parts cobalt metal per 100 parts unsaturated polyester resin and unsaturated monomer.
Claim 7
Dependent Claim
32 words
The process of claim 5 wherein said chemical thickener is included in said molding compound in a proportion of 0.5 to 25 parts per 100 parts unsaturated polyester resin and unsaturated monomer.
Claim 8
Dependent Claim
34 words
The process of claim 6 wherein said cobaltic promotor is selected from the group consisting of cobaltic halides, cobaltic monocarboxylic acids having from 2 to 20 carbon atoms in the structure and cobaltic sulfate.
Claim 9
Dependent Claim
13 words
The process of claim 6 wherein said cobaltic promoter is a cobaltic beta-diketone.
Claim 10
Dependent Claim
21 words
The process of claim 7 wherein said cobaltic beta-diketone is selected from the group consisting of cobaltic acetylacetonate and cobaltic acetonylacetonate.
Claim 11
Dependent Claim
24 words
The process of claim 9 wherein said chemical thickener is a magnesium compound selected from the group consisting of magnesium oxide and magnesium hydroxide.
Claim 12
Dependent Claim
23 words
The process of claim 10 wherein said molding compound includes a thermoplastic polymer suited for imparting low shrink characteristics to said molding compounds.
Claim 13
Dependent Claim
18 words
The process of claim 11 wherein said promoter is cobaltic acetyl acetonate and said catalyst is t-butyl perbenzoate.
Claim 14
Dependent Claim
84 words
In a thermosettable molding compound comprising an unsaturated polyester resin and an unsaturated monomer soluble in an copolymerizable therewith, said molding compound chemically thickened with a Group II metal oxide or hydroxide, the improvement for imparting extended shelf life to said molding compound and for providing desired cure rate which comprises: an effective proportion of a cobaltic promoter having a valence of 3 substantially uniformly dispersed in said molding compound for extending the shelf life of said molding compound and enhancing said cure rate.
Claim 15
Dependent Claim
84 words
In a thermosettable molding compound comprising an unsaturated polyester resin and an unsaturated monomer soluble in an copolymerizable therewith, said molding compound chemically thickened with a Group II metal oxide or hydroxide, the improvement for imparting extended shelf life to said molding compound and for providing desired cure rate which comprises: an effective proportion of a cobaltic promoter having a valence of 3 substantially uniformly dispersed in said molding compound for extending the shelf life of said molding compound and enhancing said cure rate.
Claim 16
Dependent Claim
13 words
The molding compound of claim 13 wherein said molding compound contains a catalyst.
Claim 17
Dependent Claim
23 words
The molding compound of claim 14 wherein said catalyst is selected from the group consisting of a perester, a peroxide, and a hydroperoxide.
Claim 18
Dependent Claim
35 words
The molding compound of claim 15 wherein said catalyst is included in said molding compound in a proportion of from about 0.25 to 2 parts by weight of the unsaturated polyester resin and unsaturated monomer.
Claim 19
Dependent Claim
36 words
The molding compound of claim 16 wherein said cobaltic promoter is incorporated in said molding compound in a proportion for providing 0.006 to 0.036 parts cobalt metal per 100 parts unsaturated polyester resin and unsaturated monomer.
Claim 20
Dependent Claim
34 words
The molding compound of claim 17 wherein said chemical thickener is included in said molding compound in a proportion of from 0.5 to 25 parts per 100 parts unsaturated polyester resin and unsaturated monomer.
Claim 21
Dependent Claim
33 words
The molding compound of claim 18 wherein said cobaltic promoter is selected from the group consisting of cobaltic halides, cobaltic monocarboxylic acids having from 220 carbon atoms in the structure and cobaltic sulfate.
Claim 22
Dependent Claim
14 words
The molding compound of claim 19 wherein said cobaltic promoter is a cobaltic beta-diketone.
Claim 23
Dependent Claim
24 words
The molding compound of claim 20 wherein said cobaltic beta-diketone is selected from the group consisting of cobaltic acetyl acetonate and cobaltic acetonyl acetonate.
Claim 24
Dependent Claim
25 words
The molding compound of claim 21 wherein said chemical thickener is a magnesium compound selected from the group consisting of magnesium oxide and magnesium hydroxide.
Claim 25
Dependent Claim
24 words
The molding compound of claim 22 wherein said molding compound includes a thermoplastic polomer suited for imparting low shrink characteristics to said molding compound.
Claim 26
Dependent Claim
18 words
The molding compound of claim 23 wherein said promoter is cobaltic acetyl acetonate and said catalyst is t-butylperbenzoate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-26 | 1980-04-26 | 1980-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-26 | 1984-04-26 | 1984-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-26 | 1988-04-26 | 1988-10-26 | $7700.00 | Window Closed / Lapsed |