US3988263A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermally stable coprecipitated catalysts useful for methanation and other reactions
Assignee: Union Oil Company of California
•
Filing: 1975-10-14
•
Granted: 1976-10-26
•
Expires: 1995-10-14
Abstract
Abstract Catalysts having a high degree of thermal stability, comprising alumina and one or more of the metals iron, cobalt, nickel, copper and zinc, are prepared from aqueous solutions containing a dissolved aluminum salt, a salt of at least one of the aforesaid metals in divalent form, and a delayed precipitant such as urea. With all components in homogeneous solution at a relatively low pH and temperature, the solution is heated to a temperature sufficient to hydrolyze the delayed precipitant with resultant liberation of ammonia and carbon dioxide homogeneously throughout the solution, until the pH of the solution rises sufficiently to effect coprecipitation of the metal salts as hydroxides and/or carbonates. The resulting coprecipitate is then recovered, washed, dried, shaped and calcined in conventional fashion to obtain a final product which is very active, and displays much greater thermal stability than corresponding prior art catalysts prepared by non-homogeneous coprecipitation with alkaline, ionic reagents such as sodium carbonate, ammonium hydroxide, or ammonium carbonate. The nickel-containing catalysts are particularly useful for methanation, but they are all useful in a variety of other reactions.
Inventors
- 👤 Rowland C. Hansford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 14:06
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/70; B01J23/72; B01D; B01D53/00; B01D53/34; B01D53/74; B01D53/86; B01D53/864; B01J23/06; B01J23/74; B01J23/75; B01J23/755; B01J23/76; B01J23/80; B01J37/00; B01J37/02; B01J37/03; C; C07; C07C; C07C1/00; C07C1/02; C07C1/04; C07C1/0425; C07C1/0445; C07C2521/00; C07C2521/02; C07C2521/04; C07C2523/00; C07C2523/70; C07C2523/74; C07C2523/75
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
194 words
A method for the manufacture of a composite catalyst comprising about 20-95 wt.% of alumina and about 5-80 wt.% of an oxide or oxides of at least one active divalent metal selected from the class consisting of iron, cobalt, nickel, copper and zinc, which comprises: 1. forming at a relatively low temperature a homogeneous aqueous solution of an aluminum salt, a salt or salts of at least one of said active metals, and a delayed precipitant, said delayed precipitant being a water-soluble compound which, at said relatively low temperature, does not bring about any significant precipitation of the metal salts dissolved in said solution, but which will hydrolyze at a relatively higher temperature to form ammonia and carbon dioxide; 2. heating said aqueous solution to a sufficiently high temperature and for a sufficient time to bring about hydrolysis of said delayed precipitant with resultant gradual increase in pH of said solution, and formation of a homogeneous coprecipitate of basic compounds of aluminum and of the divalent metal content of said solution; 3. separating said coprecipitate from said solution before the latter reaches a pH above about 8; and 4. drying and calcining said coprecipitate.
Claim 2
Independent Claim
194 words
A method for the manufacture of a composite catalyst comprising about 20-95 wt.% of alumina and about 5-80 wt.% of an oxide or oxides of at least one active divalent metal selected from the class consisting of iron, cobalt, nickel, copper and zinc, which comprises: 1. forming at a relatively low temperature a homogeneous aqueous solution of an aluminum salt, a salt or salts of at least one of said active metals, and a delayed precipitant, said delayed precipitant being a water-soluble compound which, at said relatively low temperature, does not bring about any significant precipitation of the metal salts dissolved in said solution, but which will hydrolyze at a relatively higher temperature to form ammonia and carbon dioxide; 2. heating said aqueous solution to a sufficiently high temperature and for a sufficient time to bring about hydrolysis of said delayed precipitant with resultant gradual increase in pH of said solution, and formation of a homogeneous coprecipitate of basic compounds of aluminum and of the divalent metal content of said solution; 3. separating said coprecipitate from said solution before the latter reaches a pH above about 8; and 4. drying and calcining said coprecipitate.
Claim 3
Dependent Claim
13 words
A method as defined in claim 1 wherein said delayed precipitant is urea.
Claim 4
Dependent Claim
34 words
A catalyst composition comprising between about 20-95 wt.% alumina and about 5-80 wt.% of an oxide or oxides of nickel, calculated as NiO, said catalyst having been prepared by the method of claim 1.
Claim 5
Dependent Claim
16 words
A catalyst composition prepared as defined in claim 1, and consisting of alumina and copper oxide.
Claim 6
Dependent Claim
43 words
A catalyst composition comprising between about 30-85% by weight of alumina, and about 15-70% by weight of an oxide or oxides of nickel, calculated as NiO, said catalyst having been prepared by the method of claim 1, using urea as said delayed precipitant.
Claim 7
Independent Claim
200 words
A method for the manufacture of a composite catalyst comprising about 20-90 wt.% of alumina and about 10-80 wt.% of an oxide or oxides of at least one active divalent metal selected from the class consisting of iron, cobalt, nickel, copper and zinc, which comprises: 1. forming at a relatively low temperature, a homogeneous aqueous solution of an aluminum salt, a salt or salts of at least one of said active metals, and a delayed precipitant, said delayed precipitant being a water-soluble compound which, at said relatively low temperature does not raise the pH of said solution above about 4.0, but which will hydrolyze at a relatively higher temperature to form ammonia and carbon dioxide, the proportion of said delayed precipitant employed being at least sufficient to generate by hydrolysis an amount of ammonia stoichiometrically sufficient to convert all metal salts in solution to their hydroxides; 2. heating said solution to bring about a sufficient hydrolysis of said delayed precipitant to raise the pH of said solution to between about 6 and 7.5, with resultant substantially complete coprecipitation of the metal salts in said solution as hydroxides and/or other basic compounds; and 3. recovering, drying and calcining the resulting coprecipitate.
Claim 8
Independent Claim
200 words
A method for the manufacture of a composite catalyst comprising about 20-90 wt.% of alumina and about 10-80 wt.% of an oxide or oxides of at least one active divalent metal selected from the class consisting of iron, cobalt, nickel, copper and zinc, which comprises: 1. forming at a relatively low temperature, a homogeneous aqueous solution of an aluminum salt, a salt or salts of at least one of said active metals, and a delayed precipitant, said delayed precipitant being a water-soluble compound which, at said relatively low temperature does not raise the pH of said solution above about 4.0, but which will hydrolyze at a relatively higher temperature to form ammonia and carbon dioxide, the proportion of said delayed precipitant employed being at least sufficient to generate by hydrolysis an amount of ammonia stoichiometrically sufficient to convert all metal salts in solution to their hydroxides; 2. heating said solution to bring about a sufficient hydrolysis of said delayed precipitant to raise the pH of said solution to between about 6 and 7.5, with resultant substantially complete coprecipitation of the metal salts in said solution as hydroxides and/or other basic compounds; and 3. recovering, drying and calcining the resulting coprecipitate.
Claim 9
Dependent Claim
13 words
The method as defined in claim 6 wherein said delayed precipitant is urea.
Claim 10
Dependent Claim
40 words
A catalyst composition comprising between about 30-60 wt.% alumina and about 40-70 wt.% of an oxide or oxides of nickel, calculated as NiO, said catalyst having been prepared by the method of claim 6, using urea as said delayed precipitant.
Claim 11
Dependent Claim
73 words
A catalyst composition comprising between about 70-90% by weight of alumina, and about 10-30% by weight of an oxide or oxides of nickel, calculated as NiO, sufficient of said alumina component having been coprecipitated with said nickel oxide component by the method of claim 6, using urea as said delayed precipitant, to provide in the finished catalyst at least one part by weight of coprecipitated alumina per part of said nickel oxide component.
Claim 12
Dependent Claim
16 words
A catalyst composition prepared as defined in claim 6, and consisting of alumina and copper oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-26 | 1980-04-26 | 1980-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-26 | 1984-04-26 | 1984-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-26 | 1988-04-26 | 1988-10-26 | $7700.00 | Window Closed / Lapsed |