Method for manufacture of micaceous α-iron oxide
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1975-04-25
•
Granted: 1976-10-19
•
Expires: 1995-04-25
Abstract
Abstract Ferric sulfate obtained by the oxidation of ferrous sulfate or ferric sulfate available in its original state is added to an alkali hydroxide at a ratio such that the amount of said alkali hydroxide will be in excess of its stoichiometric proportion, so as to form a pasty substance. Then, this pasty substance is subjected to a hydrothermal treatment. From the resultant product of the treatment, there are obtained micaceous α-iron oxide crystals and aqueous solutions of sodium sulfate and alkali hydroxide.
Inventors
- 👤 Soichiro Nobuoka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:11
CPC Classifications
C; C01; C01G; C01G49/00; C01G49/02; C01G49/06; C01P; C01P2004/00; C01P2004/20; C01P2004/60; C01P2004/61
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
175 words
In a method for the manufacture of micaceous iron oxide by preparing an aqueous solution of ferric sulfate, mixing the resultant aqueous solution of ferric sulfate with an aqueous solution of sodium hydroxide at a ratio such that the concentration of the alkali hydroxide in the mixture will represent an excess of the stoichiometric proportion necessary for the formation of ferric hydroxide whereby there is formed a hydrated paste which is subjected to a hydrothermal treatment thereby producing a solution containing therein α-iron oxide in the shape of hexagonal lamellate crystals in conjunction with Na 2 SO 4 and alkali hydroxide, the improvement which consists essentially of: a. separating from said solution said α-iron oxide to obtain α-iron oxide in the shape of hexagonal lamellate crystals; b. separating Na 2 SO 4 crystals by crystallization from the liquid which remains after said separation of α-iron oxide; c. obtaining consequently an aqueous solution of alkali hydroxide; and d. wherein the aqueous solution of alkali hydroxide from the step (c) is used for mixture with ferric sulfate.
Claim 2
Dependent Claim
175 words
In a method for the manufacture of micaceous iron oxide by preparing an aqueous solution of ferric sulfate, mixing the resultant aqueous solution of ferric sulfate with an aqueous solution of sodium hydroxide at a ratio such that the concentration of the alkali hydroxide in the mixture will represent an excess of the stoichiometric proportion necessary for the formation of ferric hydroxide whereby there is formed a hydrated paste which is subjected to a hydrothermal treatment thereby producing a solution containing therein α-iron oxide in the shape of hexagonal lamellate crystals in conjunction with Na 2 SO 4 and alkali hydroxide, the improvement which consists essentially of: a. separating from said solution said α-iron oxide to obtain α-iron oxide in the shape of hexagonal lamellate crystals; b. separating Na 2 SO 4 crystals by crystallization from the liquid which remains after said separation of α-iron oxide; c. obtaining consequently an aqueous solution of alkali hydroxide; and d. wherein the aqueous solution of alkali hydroxide from the step (c) is used for mixture with ferric sulfate.
Claim 3
Dependent Claim
194 words
In a method for the manufacture of micaceous iron oxide by preparing an aqueous solution of ferrous sulfate, adding an oxidizing agent to said solution to oxidize said ferrous sulfate to ferric sulfate, mixing the resultant aqueous solution of ferric sulfate with an aqueous solution of sodium hydroxide at a ratio such that the concentration of the alkali hydroxide in the mixture will represent an excess of the stoichiometric proportion necessary for the formation of ferric hydroxide whereby there is formed a hydrated paste which is subjected to a hydrothermal treatment thereby producing a solution containing therein α-iron oxide in the shape of hexagonal lamellate crystals in conjunction with Na 2 SO 4 and alkali hydroxide, the improvement which consists essentially of: a. separating from said solution said α-iron oxide to obtain α-iron oxide in the shape of hexagonal lamellate crystals; b. separating Na 2 SO 4 crystals by crystallization from the liquid which remains after said separation of α-iron oxide, c. obtaining consequently an aqueous solution of alkali hydroxide; and d. wherein the aqueous solution of alkali hydroxide from the step (c) is used for mixture with the aqueous solution of ferric sulfate.
Claim 4
Dependent Claim
194 words
In a method for the manufacture of micaceous iron oxide by preparing an aqueous solution of ferrous sulfate, adding an oxidizing agent to said solution to oxidize said ferrous sulfate to ferric sulfate, mixing the resultant aqueous solution of ferric sulfate with an aqueous solution of sodium hydroxide at a ratio such that the concentration of the alkali hydroxide in the mixture will represent an excess of the stoichiometric proportion necessary for the formation of ferric hydroxide whereby there is formed a hydrated paste which is subjected to a hydrothermal treatment thereby producing a solution containing therein α-iron oxide in the shape of hexagonal lamellate crystals in conjunction with Na 2 SO 4 and alkali hydroxide, the improvement which consists essentially of: a. separating from said solution said α-iron oxide to obtain α-iron oxide in the shape of hexagonal lamellate crystals; b. separating Na 2 SO 4 crystals by crystallization from the liquid which remains after said separation of α-iron oxide, c. obtaining consequently an aqueous solution of alkali hydroxide; and d. wherein the aqueous solution of alkali hydroxide from the step (c) is used for mixture with the aqueous solution of ferric sulfate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-19 | 1980-04-19 | 1980-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-19 | 1984-04-19 | 1984-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-19 | 1988-04-19 | 1988-10-19 | $7700.00 | Window Closed / Lapsed |