Polymerization of ethylenically unsaturated monomer employing a catalyst system comprising dialkylpyrocarbonate, organic acid anhydride, alkaline reagent and H2 O2
Assignee: PPG Industries Inc
•
Filing: 1975-05-30
•
Granted: 1976-10-12
•
Expires: 1995-05-30
Abstract
Abstract Ethylenically unsaturated material susceptible to free-radical polymerization, e.g., vinyl chloride monomer, is polymerized, e.g., in an aqueous medium, with an initiator system comprising, in combination, alkaline reagent, e.g., sodium bicarbonate, organic acid anhydride, e.g., isobutyric anhydride, peroxygen compound selected from organic peroxy acid (peracid), e.g., peracetic acid, and hydrogen peroxide, and alkyl pyrocarbonate, e.g., diethyl pyrocarbonate. The initiator system is added to the polymerization medium in amounts sufficient to polymerize the ethylenically unsaturated material.
Inventors
- 👤 James A. Manner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:09
CPC Classifications
C; C08; C08F; C08F4/00; C08F4/28; Y; Y10; Y10S; Y10S260/00; Y10S260/28
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
238 words
In the process for polymerizing ethylenically unsaturated material susceptible to polymerization with free radical type initiators in an aqueous or bulk polymerization medium, the improvement which comprises conducting said polymerization in the presence of an initiator system comprising, in combination, a. alkaline reagent, b. organic acid anhydride represented by the general formula: ##EQU1## wherein R 3 is selected from the group consisting of substituted and unsubstituted C 1 - C 20 alkyl, C 6 - C 10 cycloalkyl, and C 6 - C 10 aryl radicals, c. peroxygen compound selected from the group consisting of hydrogen peroxide and organic peroxy acid represented by the general formula: ##EQU2## wherein R 4 is selected from the group consisting of substituted and unsubstituted C 1 - C 20 alkyl and C 6 - C 10 aryl radicals, and d. dialkyl pyrocarbonate represented by the general formula: ##EQU3## wherein R 1 and R 2 are each selected from the group consisting of C 1 - C 20 alkyl, C 6 - C 12 cycloalkyl, C 7 - C 10 aralkyl having a single aromatic ring, and C 6 - C 8 aryl radicals, the mole ratio of dialkyl pyrocarbonate to acid anhydride being between about 0.1:1 and about 10:1, said acid anhydride, peroxygen compound and pyrocarbonate being present in amounts sufficient to generate, in the presence of said alkaline reagent, an initiating amount of initiator and thereby polymerize the ethylenically unsaturated material.
Claim 2
Dependent Claim
238 words
In the process for polymerizing ethylenically unsaturated material susceptible to polymerization with free radical type initiators in an aqueous or bulk polymerization medium, the improvement which comprises conducting said polymerization in the presence of an initiator system comprising, in combination, a. alkaline reagent, b. organic acid anhydride represented by the general formula: ##EQU1## wherein R 3 is selected from the group consisting of substituted and unsubstituted C 1 - C 20 alkyl, C 6 - C 10 cycloalkyl, and C 6 - C 10 aryl radicals, c. peroxygen compound selected from the group consisting of hydrogen peroxide and organic peroxy acid represented by the general formula: ##EQU2## wherein R 4 is selected from the group consisting of substituted and unsubstituted C 1 - C 20 alkyl and C 6 - C 10 aryl radicals, and d. dialkyl pyrocarbonate represented by the general formula: ##EQU3## wherein R 1 and R 2 are each selected from the group consisting of C 1 - C 20 alkyl, C 6 - C 12 cycloalkyl, C 7 - C 10 aralkyl having a single aromatic ring, and C 6 - C 8 aryl radicals, the mole ratio of dialkyl pyrocarbonate to acid anhydride being between about 0.1:1 and about 10:1, said acid anhydride, peroxygen compound and pyrocarbonate being present in amounts sufficient to generate, in the presence of said alkaline reagent, an initiating amount of initiator and thereby polymerize the ethylenically unsaturated material.
Claim 3
Dependent Claim
29 words
The process of claim 1 wherein the alkaline reagent is selected from the group consisting of alkali metal and alkaline earth metal carbonates and bicarbonates, and quaternary ammonium hydroxides.
Claim 4
Dependent Claim
22 words
The process of claim 1 wherein the anhydride is isobutyric anhydride, propionic anhydride, acetic anhydride, pivalic anhydride, or mixtures of such anhydrides.
Claim 5
Dependent Claim
12 words
The process of claim 1 wherein the peroxy acid is peracetic acid.
Claim 6
Dependent Claim
13 words
The process of claim 1 wherein the ethylenically unsaturated material is vinyl chloride.
Claim 7
Dependent Claim
32 words
The process of claim 1 wherein R 1 and R 2 are the same and are methyl, ethyl, isopropyl, n-butyl, isobutyl, secondary butyl, tertiary butyl, 2-ethylhexyl, cyclohexyl, 4-tertiarybutyl cyclohexyl, phenyl or benzyl.
Claim 8
Dependent Claim
75 words
The process of claim 1 wherein from about 0.001 to about 3 weight percent each of organic acid anhydride and dialkyl pyrocarbonate based on ethylenically unsaturated material, is used and the mole ratio of peroxygen compound to the sum of the moles of organic acid anhydride and dialkyl pyrocarbonate is from 0.2:1 to about 10:1 when the peroxygen compound is peroxy acid, and from 0.1:1 to about 10:1 when the peroxygen compound is hydrogen peroxide.
Claim 9
Dependent Claim
48 words
The process of claim 7 wherein the mole ratio of peroxygen compound to the sum of the moles of organic acid anhydride and dialkyl pyrocarbonate is about 1:1 when the peroxygen compound is peroxy acid, and from 0.2:1 to about 2:1 when the peroxygen compound is hydrogen peroxide.
Claim 10
Dependent Claim
16 words
The process of claim 1 wherein the initiator system contains more than one organic acid anhydride.
Claim 11
Dependent Claim
14 words
The process of claim 1 wherein the polymerization is conducted in an aqueous medium.
Claim 12
Dependent Claim
15 words
The process of claim 1 wherein the polymerization temperature is from 0° to 95° C.
Claim 13
Dependent Claim
19 words
The process of claim 1 wherein the peroxygen compound is a mixture of organic peroxy acid and hydrogen peroxide.
Claim 14
Dependent Claim
182 words
In the process for polymerizing ethylenically unsaturated material susceptible to polymerization with free radical type initiators in an aqueous or bulk polymerization medium, the improvement which comprises conducting said polymerization in the presence of an initiator system comprising, in combination, a. alkaline reagent, b. from 0.01 to about 1 weight percent, based on ethylenically unsaturated material, of organic acid anhydride representable by the general formula: ##STR10## wherein R 3 is selected from the group consisting of C 1 - C 12 alkyl radicals, c. hydrogen peroxide, and d. from 0.01 to about 1 weight percent, based on ethylenically unsaturated material, of dialkyl pyrocarbonate representable by the formula: ##STR11## wherein R 1 and R 2 are each selected from the group consisting of C 1 - C 12 alkyl, C 6 - C 10 cycloalkyl, phenyl and benzyl, the mole ratio of dialkyl pyrocarbonate to acid anhydride being between about 0.2:1 and about 1:1, the mole ratio of hydrogen peroxide to the sum of the moles of acid anhydride and dialkyl pyrocarbonate being from 0.2:1 to 2:1, thereby polymerizing the ethylenically unsaturated material.
Claim 15
Dependent Claim
182 words
In the process for polymerizing ethylenically unsaturated material susceptible to polymerization with free radical type initiators in an aqueous or bulk polymerization medium, the improvement which comprises conducting said polymerization in the presence of an initiator system comprising, in combination, a. alkaline reagent, b. from 0.01 to about 1 weight percent, based on ethylenically unsaturated material, of organic acid anhydride representable by the general formula: ##STR10## wherein R 3 is selected from the group consisting of C 1 - C 12 alkyl radicals, c. hydrogen peroxide, and d. from 0.01 to about 1 weight percent, based on ethylenically unsaturated material, of dialkyl pyrocarbonate representable by the formula: ##STR11## wherein R 1 and R 2 are each selected from the group consisting of C 1 - C 12 alkyl, C 6 - C 10 cycloalkyl, phenyl and benzyl, the mole ratio of dialkyl pyrocarbonate to acid anhydride being between about 0.2:1 and about 1:1, the mole ratio of hydrogen peroxide to the sum of the moles of acid anhydride and dialkyl pyrocarbonate being from 0.2:1 to 2:1, thereby polymerizing the ethylenically unsaturated material.
Claim 16
Dependent Claim
60 words
The process of claim 13 wherein the acid anhydride is isobutyric anhydride, propionic anhydride, acetic anhydride, pivalic anhydride, or mixturs of such anhydrides, and the dialkyl pyrocarbonate is dimethyl pyrocarbonate, diethyl pyrocarbonate, di-n-propyl pyrocarbonate, diisopropyl pyrocarbonate, di-n-butyl pyrocarbonate diisobutyl pyrocarbonate, disecondarybutyl pyrocarbonate, ditertiarybutyl pyrocarbonate, di-2-ethylhexyl pyrocarbonate, dicyclohexyl pyrocarbonate, di-4-tertiarybutyl cyclohexyl pyrocarbonate, diphenyl pyrocarbonate, dibenzyl pyrocarbonate, or mixtures of such pyrocarbonates.
Claim 17
Dependent Claim
12 words
The process of claim 14 wherein the unsaturated material is vinyl chloride.
Claim 18
Dependent Claim
28 words
The process of claim 15 wherein the polymerization is conducted in an aqueous medium and the temperature of the polymerization is from about 20° to about 70° C.
Claim 19
Dependent Claim
16 words
The process of claim 15 wherein the alkaline reagent is sodium bicarbonate or quaternary ammonium hydroxide.
Claim 20
Dependent Claim
210 words
In the process for polymerizing ethylenically unsaturated material susceptible to polymerization with free radical type initiators in an aqueous or bulk polymerization medium, the improvement which comprises conducting said polymerization in the presence of an initiator system comprising, in combination, a. alkaline reagent, b. from 0.01 to about 1 weight percent, based on ethylenically unsaturated material, of organic acid anhydride representable by the general formula: ##STR12## wherein R 3 is selected from the group consisting of C 1 - C 12 alkyl radicals, c. organic peroxy acid representable by the general formula: ##STR13## wherein R 4 is selected from the group consisting of C 1 - C 12 alkyl radicals, and d. from 0.01 to about 1 weight percent, based on ethylenically unsaturated material, of dialkyl pyrocarbonate representable by the general formula: ##STR14## wherein R 1 and R 2 are each selected from the group consisting of C 1 - C 12 alkyl radicals, C 6 - C 10 cycloalkyl, phenyl and benzyl, the mole ratio of dialkyl pyrocarbonate to acid anhydride being between about 0.2:1 and about 1:1, the mole ratio of peroxy acid to the sum of the moles of acid anhydride and dialkyl pyrocarbonate being from about 0.2:1 to about 10:1, thereby polymerizing the ethylenically unsaturated material.
Claim 21
Dependent Claim
210 words
In the process for polymerizing ethylenically unsaturated material susceptible to polymerization with free radical type initiators in an aqueous or bulk polymerization medium, the improvement which comprises conducting said polymerization in the presence of an initiator system comprising, in combination, a. alkaline reagent, b. from 0.01 to about 1 weight percent, based on ethylenically unsaturated material, of organic acid anhydride representable by the general formula: ##STR12## wherein R 3 is selected from the group consisting of C 1 - C 12 alkyl radicals, c. organic peroxy acid representable by the general formula: ##STR13## wherein R 4 is selected from the group consisting of C 1 - C 12 alkyl radicals, and d. from 0.01 to about 1 weight percent, based on ethylenically unsaturated material, of dialkyl pyrocarbonate representable by the general formula: ##STR14## wherein R 1 and R 2 are each selected from the group consisting of C 1 - C 12 alkyl radicals, C 6 - C 10 cycloalkyl, phenyl and benzyl, the mole ratio of dialkyl pyrocarbonate to acid anhydride being between about 0.2:1 and about 1:1, the mole ratio of peroxy acid to the sum of the moles of acid anhydride and dialkyl pyrocarbonate being from about 0.2:1 to about 10:1, thereby polymerizing the ethylenically unsaturated material.
Claim 22
Dependent Claim
65 words
The process of claim 18 wherein the acid anhydride is isobutyric anhydride, propionic anhydride, acetic anhydride, pivalic anhydride, or mixtures of such anhydrides, the peroxy acid is peracetic acid and the dialkyl pyrocarbonate is dimethyl pyrocarbonate, diethyl pyrocarbonate, di-n-propyl pyrocarbonate, diisopropyl pyrocarbonate, di-n-butyl pyrocarbonate, diisobutyl pyrocarbonate, disecondarybutyl pyrocarbonate, ditertiarybutyl pyrocarbonate, di-2-ethylhexyl pyrocarbonate, dicyclohexyl pyrocarbonate, di-4-tertiarybutylcyclohexyl pyrocarbonate, diphenyl pyrocarbonate, dibenzyl pyrocarbonate, or mixtures of such pyrocarbonates.
Claim 23
Dependent Claim
27 words
The process of claim 19 wherein the mole ratio of peroxy acid to the sum of the moles of acid anhydride and dialkyl pyrocarbonate is about 1:1.
Claim 24
Dependent Claim
28 words
The process of claim 14 wherein the polymerization is conducted in an aqueous medium and the temperature of the polymerization is from about 20° to about 70° C.
Claim 25
Dependent Claim
12 words
The process of claim 14 wherein the unsaturated material is vinyl chloride.
Claim 26
Dependent Claim
16 words
The process of claim 22 wherein the alkaline reagent is sodium bicarbonate or quaternary ammonium hydroxide.
Claim 27
Dependent Claim
187 words
In the process for polymerizing vinyl chloride in an aqueous or bulk polymerization medium at temperatures of between about 20° and about 70° C., the improvement which comprises conducting said polymerization in the presence of an initiator system comprising, in combination, a. alkaline buffering reagent, b. from 0.01 to about 1 weight percent, based on vinyl chloride, of acid anhydride selected from the group isobutyric anhydride, propionic anhydride, acetic anhydride, pivalic anhydride, and mixtures of such anhydrides, c. from 0.01 to about 1 weight percent, based on vinyl chloride, of dialkyl pyrocarbonate selected from dimethyl pyrocarbonate, diethyl pyrocarbonate, di-n-propyl pyrocarbonate, diisopropyl pyrocarbonate, di-n-butyl pyrocarbonate, diisobutyl pyrocarbonate, disecondarybutyl pyrocarbonate, ditertiarybutyl pyrocarbonate, di-2-ethylhexyl pyrocarbonate, dicyclohexyl pyrocarbonate, di-4-tertiarybutyl cyclohexyl pyrocarbonate, diphenyl pyrocarbonate, dibenzyl pyrocarbonate, or mixtures of such pyrocarbonates, and d. peroxygen compound selected from peracetic acid and hydrogen peroxide, the mole ratio of dialkyl pyrocarbonate to acid anhydride being between 0.2:1 and 1:1, the mole ratio of peracetic acid and hydrogen peroxide to the sum of the mole of acid anhydride and dialkyl pyrocarbonate between about 1:1 and from 0.2:1 to about 2.0:1 respectively, thereby polymerizing said vinyl chloride.
Claim 28
Dependent Claim
187 words
In the process for polymerizing vinyl chloride in an aqueous or bulk polymerization medium at temperatures of between about 20° and about 70° C., the improvement which comprises conducting said polymerization in the presence of an initiator system comprising, in combination, a. alkaline buffering reagent, b. from 0.01 to about 1 weight percent, based on vinyl chloride, of acid anhydride selected from the group isobutyric anhydride, propionic anhydride, acetic anhydride, pivalic anhydride, and mixtures of such anhydrides, c. from 0.01 to about 1 weight percent, based on vinyl chloride, of dialkyl pyrocarbonate selected from dimethyl pyrocarbonate, diethyl pyrocarbonate, di-n-propyl pyrocarbonate, diisopropyl pyrocarbonate, di-n-butyl pyrocarbonate, diisobutyl pyrocarbonate, disecondarybutyl pyrocarbonate, ditertiarybutyl pyrocarbonate, di-2-ethylhexyl pyrocarbonate, dicyclohexyl pyrocarbonate, di-4-tertiarybutyl cyclohexyl pyrocarbonate, diphenyl pyrocarbonate, dibenzyl pyrocarbonate, or mixtures of such pyrocarbonates, and d. peroxygen compound selected from peracetic acid and hydrogen peroxide, the mole ratio of dialkyl pyrocarbonate to acid anhydride being between 0.2:1 and 1:1, the mole ratio of peracetic acid and hydrogen peroxide to the sum of the mole of acid anhydride and dialkyl pyrocarbonate between about 1:1 and from 0.2:1 to about 2.0:1 respectively, thereby polymerizing said vinyl chloride.
Claim 29
Dependent Claim
47 words
The process of claim 24 wherein the alkaline buffering reagent is selected from alkali metal or alkaline earth metal carbonates and bicarbonates, and quaternary ammonium hydroxides and the amount of alkaline buffering reagent is from about 0.01 to about 10 percent by weight based on vinyl chloride.
Claim 30
Dependent Claim
14 words
The process of claim 25 wherein the polymerization is conducted in an aqueous medium.
Claim 31
Dependent Claim
35 words
The process of claim 26 wherein the alkaline buffering reagent is sodium bicarbonate, the acid anhydride is isobutyric anhydride, the dialkyl pyrocarbonate is dimethyl pyrocarbonate or diethyl pyrocarbonate, and the peroxygen compound is hydrogen peroxide.
Claim 32
Dependent Claim
19 words
The process of claim 23 wherein the peroxygen compound (d) is a mixture of peracetic acid and hydrogen peroxide.
References Cited (Backward Citations)
US3022281A
Cited
US3108093A
Cited
US3326958A
Cited
US3420807A
Cited
US3575945A
Cited
US3580955A
Cited
US3637633A
Cited
US3821273A
Cited
US3857828A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-12 | 1980-04-12 | 1980-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-12 | 1984-04-12 | 1984-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-12 | 1988-04-12 | 1988-10-12 | $7700.00 | Window Closed / Lapsed |