Method of joining braze alloy to a parent metal part
Assignee: United Aircraft Products Inc
•
Filing: 1974-08-01
•
Granted: 1976-10-12
•
Expires: 1994-08-01
Abstract
Abstract A method including the step of applying braze alloy in sheet-like form to a part made of a brazeable parent metal. Pressure is exerted to place the braze alloy in intimately contacting relation to the part. For a predetermined period of time, while the exerted pressure is maintained, heat is applied at a temperature value which is just below the melting point of the braze alloy. Diffusion bonding occurs and, in accordance with an optional practice of the invention, a catalyst may be introduced which at a temperature below the applied temperature liquifies and speeds up the diffusion process.
Inventors
- 👤 Edward B. Gempler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:03
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/001; B23K1/00; B23K1/20; B23P; B23P15/00; B23P15/26; B23K2103/00; B23K2103/08; B23K2103/10
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
140 words
A method of joining braze alloy to at least selected surfaces of a rigid irregularly shaped part later to be united with other parts in a brazing process, said part being comprised of a brazeable parent metal, including the steps of superimposing braze alloy in solid form on said selected surfaces of said part as a cladding using applied external pressure to obtain an intimately contacting relation of said cladding with said part, and in an interval during which said applied pressure is maintained subjecting the assembly comprising said part and said cladding to an elevated temperature which is below the melting point of the parent material of said part and which approaches but is less than the melting point of the braze alloy to join the braze alloy to said part while retaining its individual character as a cladding.
Claim 2
Independent Claim
140 words
A method of joining braze alloy to at least selected surfaces of a rigid irregularly shaped part later to be united with other parts in a brazing process, said part being comprised of a brazeable parent metal, including the steps of superimposing braze alloy in solid form on said selected surfaces of said part as a cladding using applied external pressure to obtain an intimately contacting relation of said cladding with said part, and in an interval during which said applied pressure is maintained subjecting the assembly comprising said part and said cladding to an elevated temperature which is below the melting point of the parent material of said part and which approaches but is less than the melting point of the braze alloy to join the braze alloy to said part while retaining its individual character as a cladding.
Claim 3
Dependent Claim
26 words
A method according to claim 1, wherein said braze alloy has a sheet-like form and is cut and sized precisely to fit contours of said part.
Claim 4
Dependent Claim
39 words
A method according to claim 1, wherein pressure and elevated temperature are applied for a time sufficient to effect solid state diffusion of constituents in the braze alloy into the parent metal of said part at the interface therebetween.
Claim 5
Dependent Claim
24 words
A method according to claim 3, wherein the applied temperature has a value just below the temperature value at which said braze alloy melts.
Claim 6
Dependent Claim
74 words
A method according to claim 4, wherein said part is made of an aluminous material melting in a temperature range on the order of 1100°-1200° F. and said braze alloy is made of an aluminous material melting in a temperature range on the order of 1070° F. to 1080° F., the temperature to which said assembly comprising said part and said cladding is subjected being in the range of 1060° F. to 1065° F.
Claim 7
Dependent Claim
31 words
A method according to claim 5, wherein pressure applied to said assembly to obtain initimate contact of said braze alloy with said part is on the order of 0.75 psi minimum.
Claim 8
Dependent Claim
30 words
A method according to claim 5, wherein said assembly is heated under conditions of reduced atmospheric pressure for a period of time on the order of 7 to 8 minutes.
Claim 9
Dependent Claim
35 words
A method according to claim 7, wherein said assembly is heated under an applied vacuum on the order of 1.5 to 2.0 × 10 - 4 torr or better maintained during said period of time.
Claim 10
Dependent Claim
48 words
A method according to claim 5, wherein said assembly is heated in a vacuum furnace, characterized by the step of adding to the furnace metallic means having a melting temperature on the order of 1030° F. and in liquid form speeding up the diffusion process at said interface.
Claim 11
Dependent Claim
38 words
A method according to claim 3, characterized by the step of introducing a catalyst which melts at a temperature lower than said elevated temperature to speed up the diffusion process by forming pockets of liquid at said interface.
Claim 12
Dependent Claim
70 words
A method according to claim 3, wherein said part is heated in an enclosed environment, characterized by the step of introducing into said environment a material vaporizable at a temperature below said elevated temperature to wet the interface between the braze alloy and the parent metal to utilize limited liquid diffusion in conjunction with solid state diffusion to reduce the time-at-temperature at which said part is required to be held.
Claim 13
Dependent Claim
47 words
A method according to claim 11, wherein said introduced material at said lower temperature releases vapor into said environment to penetrate minute voids and to migrate by diffusion to appear in small quantities at the interface between the braze alloy and the parent metal of the part.
Claim 14
Dependent Claim
114 words
A method according to claim 12, wherein said irregularly shaped part is composed in the main of substantially pure aluminum with minor amounts of other metals and melts at a temperature in the range of 1100° F. to 1204° F., said braze alloy being comprised in the main of substantially pure aluminum with somewhat more significant amounts of other metals and melting at a temperature in the range of 1070° F. to 1080° F., said vaporizable material being magnesium and melting at a temperature of about 1030° F., the method subjecting said part to a rising temperature held at a high level to a value in the range of 1060° F. to 1065° F.
Claim 15
Dependent Claim
18 words
A method according to claim 13, wherein said magnesium is introduced as a constituent of said braze alloy.
Claim 16
Dependent Claim
30 words
A method according to claim 13, wherein said enclosed environment is provided by a vacuum furnace, said magnesium being introduced therein in the form of chips external to said part.
Claim 17
Independent Claim
177 words
A method of preparing a header plate for the brazing of tubes thereto, said plate being irregularly configured, including the steps of superimposing on at least one of oppositely presented faces of said plate braze alloy in sheet form, said braze alloy having a melting point which is lower than that of the material of said header plate, placing the header plate with superimposing braze alloy in a furnace while using applied external pressure to obtain an intimately contacting relation of said braze alloy with said header plate, while maintaining said applied pressure raising the temperature in said furnace to a value which is below the melting temperature of the material of said header plate and which approaches but is less than the melting temperature of said braze alloy and holding the temperature at said value for a selected interval during which said braze alloy is joined to said header plate as a cladding thereon, removing the header plate from the furnace, and drilling tube accommodating holes through said plate and through the braze alloy cladding thereon.
Claim 18
Independent Claim
177 words
A method of preparing a header plate for the brazing of tubes thereto, said plate being irregularly configured, including the steps of superimposing on at least one of oppositely presented faces of said plate braze alloy in sheet form, said braze alloy having a melting point which is lower than that of the material of said header plate, placing the header plate with superimposing braze alloy in a furnace while using applied external pressure to obtain an intimately contacting relation of said braze alloy with said header plate, while maintaining said applied pressure raising the temperature in said furnace to a value which is below the melting temperature of the material of said header plate and which approaches but is less than the melting temperature of said braze alloy and holding the temperature at said value for a selected interval during which said braze alloy is joined to said header plate as a cladding thereon, removing the header plate from the furnace, and drilling tube accommodating holes through said plate and through the braze alloy cladding thereon.
Claim 19
Dependent Claim
70 words
A method according to claim 16, characterized by the step of introducing into the environment of said furnace a material vaporizable therein in the course of raising the furnace temperature and which in having access in vapor form to the interface between said braze alloy and said header plate and wetting said interface brings about a two-phase condition in which both solid and liquid diffusion takes place at said interface.
References Cited (Backward Citations)
CA692778A
Cited
US2298996A
Cited
US2834102A
Cited
US3133346A
Cited
US3370343A
Cited
US3384951A
Cited
US3550254A
Cited
US3581382A
Cited
US3673678A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-10-12 | 1980-04-12 | 1980-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-10-12 | 1984-04-12 | 1984-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-10-12 | 1988-04-12 | 1988-10-12 | $7700.00 | Window Closed / Lapsed |