Thermally stable polyurethane elastomers produced from poly(oxypropylene)-poly(oxyethylene)glycols of high oxyethylene group content
Assignee: Uniroyal Chemical Co Inc
•
Filing: 1975-09-11
•
Granted: 1976-09-28
•
Expires: 1995-09-11
Abstract
Abstract Flexible automobile exterior body parts are molded from a polyurethane elastomer prepared from a reaction mixture comprising: A. a poly(oxypropylene)-poly(oxyethylene) glycol of molecular weight of from about 1750 to about 4000 containing 15 to 50% by weight oxyethylene groups; B. methylenebis(4-phenylisocyanate); C. 1,4-butanediol. The invention also relates to this polyurethane elastomer.
Inventors
- 👤 Francis X. O'Shea
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 08:14
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6674; B; B62; B62D; B62D29/00; B62D29/04; C08G18/08; C08G18/10; C08G18/40; C08G18/48; C08G18/4833; C08G18/4837; Y; Y10; Y10S; Y10S528/00; Y10S528/906
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
138 words
A thermally stable polyurethane elastomer which is a reaction product of: (a) a poly(oxypropylene)-poly(oxyethylene) glycol of molecular weight from about 1750 to about 4000 and containing 15 to 50% by weight oxyethylene groups; (b) methylenebis(4-phenylisocyanate); and (c) 1,4-butanediol; the NCO/OH equivalents ratio being from 0.95 to 1.2 and the molar ratio of (c) to (a) being from 3/1 to 12/1, said elastomer having a hardness of about 40 to 55 Shore D, an elongation of greater than 270%, an ultimate tensile strength of at least 2700 psi and a Die C tear strength of at least 500 pli, said elastomer displaying improved thermal stability as evidenced by its ability to retain at least twice as much of its original tensile strength, after exposure to a temperature of 415°F. for 20 minutes, as an otherwise similar elastomer in which
Claim 2
Dependent Claim
138 words
A thermally stable polyurethane elastomer which is a reaction product of: (a) a poly(oxypropylene)-poly(oxyethylene) glycol of molecular weight from about 1750 to about 4000 and containing 15 to 50% by weight oxyethylene groups; (b) methylenebis(4-phenylisocyanate); and (c) 1,4-butanediol; the NCO/OH equivalents ratio being from 0.95 to 1.2 and the molar ratio of (c) to (a) being from 3/1 to 12/1, said elastomer having a hardness of about 40 to 55 Shore D, an elongation of greater than 270%, an ultimate tensile strength of at least 2700 psi and a Die C tear strength of at least 500 pli, said elastomer displaying improved thermal stability as evidenced by its ability to retain at least twice as much of its original tensile strength, after exposure to a temperature of 415°F. for 20 minutes, as an otherwise similar elastomer in which
Claim 3
Dependent Claim
25 words
A thermally stable polyurethane elastomer as in claim 1 in which the molecular weight of (a) is about 2000 and the oxyethylene group content is
Claim 4
Dependent Claim
51 words
A shaped article prepared from the thermally stable polyurethane elastomer of claim 1 and characterized, when having a thickness of 0.08 inch, by remaining intact under a 5 mile per hour impact at -20°F. and by having a sag of less than 2 inches as determined by the Heat Test O'S.
References Cited (Backward Citations)
US3915937A
Cited
US3901852A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-28 | 1980-03-29 | 1980-09-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-28 | 1984-03-29 | 1984-09-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-28 | 1988-03-29 | 1988-09-28 | $7700.00 | Window Closed / Lapsed |