Reducing capillarity of polyglycolic acid sutures
Assignee: Wyeth Holdings LLC
•
Filing: 1974-07-16
•
Granted: 1976-09-28
•
Expires: 1994-07-16
Abstract
Abstract Useful surgical elements consist of a sterile synthetic copolymer containing, by mole percent, about 15 to 85 percent glycolic acid and 85 to 15 percent lactic acid, which has enhanced tissue absorption as compared with polylactic acid and enhanced solubility in organic solvents as compared with polyglycolic acid and hence can be cast into sheets during preparation and implantation. Such surgical element may be used alone or in combination with polyglycolic acid or a coating for polyglycolic acid surgical elements. Other comonomers may be introduced into the system.
Inventors
- 👤 Edward Emil Schmitt
- 👤 Martin Epstein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:08
CPC Classifications
A; A61; A61L; A61L17/00; A61L17/06; A61L17/10; A61L17/12; A61L17/14; A61L17/145; C; C08; C08G; C08G63/00; C08G63/02; C08G63/06; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
80 words
A surgical element comprising at least one strand of polyglycolic acid insoluble in each of xylene, toluene and chloroform having thereon a stiffening and capillarity reducing quantity of a copolymer of 15 to 85 mole percent glycolic acid and 85 to 15 mole percent lactic acid, said copolymer being soluble in each of xylene, toluene and chloroform, and having a melting point sufficiently below the melting point of polyglycolic acid to permit extrusion coating without melting of the polyglycolic acid.
Claim 2
Dependent Claim
80 words
A surgical element comprising at least one strand of polyglycolic acid insoluble in each of xylene, toluene and chloroform having thereon a stiffening and capillarity reducing quantity of a copolymer of 15 to 85 mole percent glycolic acid and 85 to 15 mole percent lactic acid, said copolymer being soluble in each of xylene, toluene and chloroform, and having a melting point sufficiently below the melting point of polyglycolic acid to permit extrusion coating without melting of the polyglycolic acid.
Claim 3
Dependent Claim
43 words
The surgical element of claim 1 wherein said element is a polyglycolic acid suture having thereon a thin but stiffening and capillarity reducing quantity of a copolymer of 15 to 85 mole percent glycolic acid and 85 to 15 mole percent lactic acid.
Claim 4
Dependent Claim
32 words
The suture of claim 2 in which the suture consists of a plurality of filaments of polyglycolic acid twisted into a strand, and coated with a twist retaining coating of said copolymer.
Claim 5
Independent Claim
106 words
A method of retaining living mammalian tissue in a desired location and relationship during a healing process which comprises positioning and impacting said living tissue with a surgical element comprising at least one strand of polyglycolic acid insoluble in each of xylene, toluene and chloroform having thereon a stiffening and capillarity reducing quantity of a copolymer of 15 to 85 mole percent glycolic acid and 85 to 15 mole percent lactic acid, said copolymer being soluble in each of xylene, toluene and chloroform, and having a melting point sufficiently below the melting point of polyglycolic acid to permit extrusion coating without melting of the polyglycolic acid.
Claim 6
Independent Claim
106 words
A method of retaining living mammalian tissue in a desired location and relationship during a healing process which comprises positioning and impacting said living tissue with a surgical element comprising at least one strand of polyglycolic acid insoluble in each of xylene, toluene and chloroform having thereon a stiffening and capillarity reducing quantity of a copolymer of 15 to 85 mole percent glycolic acid and 85 to 15 mole percent lactic acid, said copolymer being soluble in each of xylene, toluene and chloroform, and having a melting point sufficiently below the melting point of polyglycolic acid to permit extrusion coating without melting of the polyglycolic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-28 | 1980-03-29 | 1980-09-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-28 | 1984-03-29 | 1984-09-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-28 | 1988-03-29 | 1988-09-28 | $7700.00 | Window Closed / Lapsed |