Method for production of cement-bonded molded articles particularly lightweight fiber boards
Assignee: Osterreichisch Amerikanische Magnesit AG
•
Filing: 1973-12-11
•
Granted: 1976-09-21
•
Expires: 1993-12-11
Abstract
Abstract Method for the production of cement-bonded molded articles, particularly lightweight boards of wood fiber, wood chips or other lignocelluloses, of mineral fibers, glass fibers, plastic chips and fibers or various lightweight materials, like expanded silicates, expanded clay or expanded glass or granules of foamed plastics as a base material and portland cement as a binder, characterized in that the molded articles are produced in a heated molding duct formed of endless moving belts, for example, steel belts, using a portland cement as a binder in the molding compound which contains 1 to 30% by weight, perferably 15 to 25% by weight, of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX.sub. 2 wherein X is any halogen. The cement with added calcium-halogen aluminate has such a short setting time, which is further accelerated by heating during molding, that boards may be successfully made on a continuous basis using a belt-molding machine.
Inventors
- 👤 Fridolin Pletzer
- 👤 Hubert Strasser
- 👤 Hans Tschernuth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 11:02
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; C04B7/00; C04B7/36; C04B7/38; C04B7/42
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
121 words
Method for the production of cement-bonded molded articles comprising the steps of: a. feeding to a heated molding duct formed of endless belts a molding composition comprising a base material selected from the group consisting of wood fiber, wood chips, lignocelluloses, mineral fibers, glass fibers, plastic chips, expanded silicates, expanded glass and granules of foamed plastics and a binder consisting essentially of a portland cement which contains 1 to 30% by weight of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX 2 , wherein X is any halogen; b. heating the molding composition in the molding duct to cause the binder to set and form a molded article, and c. removing the molded article from the molding duct.
Claim 2
Dependent Claim
121 words
Method for the production of cement-bonded molded articles comprising the steps of: a. feeding to a heated molding duct formed of endless belts a molding composition comprising a base material selected from the group consisting of wood fiber, wood chips, lignocelluloses, mineral fibers, glass fibers, plastic chips, expanded silicates, expanded glass and granules of foamed plastics and a binder consisting essentially of a portland cement which contains 1 to 30% by weight of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX 2 , wherein X is any halogen; b. heating the molding composition in the molding duct to cause the binder to set and form a molded article, and c. removing the molded article from the molding duct.
Claim 3
Dependent Claim
22 words
Method according to claim 1 wherein the molding compound in the molding duct is heated to a temperature of 45° to 120°C.
Claim 4
Dependent Claim
162 words
Method for the continuous production of cement-bonded molded articles comprising the steps of: a. continuously feeding to a heated molding duct formed of endless belts a molding composition comprising a base material selected from the group consisting of wood fiber, wood chips, lignocelluloses, mineral fibers, glass fibers, plastic chips, plastic fibers, expanded silicates, expanded glass and granules of foamed plastics and a binder consisting essentially of a portland cement which contains (i) 1 to 30% by weight of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX 2 wherein X is any halogen and (ii) 1 to 12% by weight SO 3 in the form of sulphates selected from the group consisting of calcium sulphate, plaster of paris, gypsum, or mixtures thereof; b. heating the molding composition in the molding duct to a temperature of 45° to 120°C. to cause the binder to set and to form a molded article; and c. removing the molded article from the molding duct.
Claim 5
Dependent Claim
162 words
Method for the continuous production of cement-bonded molded articles comprising the steps of: a. continuously feeding to a heated molding duct formed of endless belts a molding composition comprising a base material selected from the group consisting of wood fiber, wood chips, lignocelluloses, mineral fibers, glass fibers, plastic chips, plastic fibers, expanded silicates, expanded glass and granules of foamed plastics and a binder consisting essentially of a portland cement which contains (i) 1 to 30% by weight of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX 2 wherein X is any halogen and (ii) 1 to 12% by weight SO 3 in the form of sulphates selected from the group consisting of calcium sulphate, plaster of paris, gypsum, or mixtures thereof; b. heating the molding composition in the molding duct to a temperature of 45° to 120°C. to cause the binder to set and to form a molded article; and c. removing the molded article from the molding duct.
Claim 6
Dependent Claim
181 words
Method for the continuous production of cement-bonded molded articles comprising the steps of: a. continuously feeding to a heated molded duct formed of endless belts a molding composition comprising a base material selected from the groups consisting of wood fiber, wood chips, lignocelluloses, mineral fibers, glass fibers, plastic chips, plastic fibers, expanded silicates, expanded glass or granules of foamed plastics and a binder consisting essentially of a portland cement which contains (i) 1 to 30% by weight of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX 2 , wherein X is any halogen, (ii) 1 to 12% by weight SO 3 in the form of sulphates selected from the group consisting of calcium sulphate, plaster of paris, gypsum, or mixtures thereof and (iii) one or more substances which reduce the calcium ion concentration in the liquid phase or bind calcium ions; b. heating the molding composition in the molding duct to a temperature of 45° to 120°C. to cause the binder to set and form a molded article; and c. removing the molded article from the molding duct.
Claim 7
Dependent Claim
181 words
Method for the continuous production of cement-bonded molded articles comprising the steps of: a. continuously feeding to a heated molded duct formed of endless belts a molding composition comprising a base material selected from the groups consisting of wood fiber, wood chips, lignocelluloses, mineral fibers, glass fibers, plastic chips, plastic fibers, expanded silicates, expanded glass or granules of foamed plastics and a binder consisting essentially of a portland cement which contains (i) 1 to 30% by weight of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX 2 , wherein X is any halogen, (ii) 1 to 12% by weight SO 3 in the form of sulphates selected from the group consisting of calcium sulphate, plaster of paris, gypsum, or mixtures thereof and (iii) one or more substances which reduce the calcium ion concentration in the liquid phase or bind calcium ions; b. heating the molding composition in the molding duct to a temperature of 45° to 120°C. to cause the binder to set and form a molded article; and c. removing the molded article from the molding duct.
Claim 8
Dependent Claim
38 words
Method according to claim 4 wherein the substances (iii) are selected from the group consisting of natural pozzoulana, synthetic pozzoulana, flue dust, fine-grained blast furnace slag, sodium fluoride, magnesium silico-fluoride, waterglass, caustic soda, sodium carbonate and sodium bicarbonate.
Claim 9
Dependent Claim
145 words
Method for the continuous production of lightweight cement-bonded boards comprising the steps of: a. continuously feeding to a heated molding duct formed of endless steel belts a molding composition comprising a base material selected from the group consisting of wood fiber, wood chips, lignocelluloses, mineral fibers, glass fibers, plastic chips, plastic fibers, expanded silicates, expanded clay, expanded glass and granules of foamed plastics, and a binder consisting essentially of a portland cement which contains 15 to 25% by weight of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX 2 , wherein X is any halogen; b. heating the molding composition in the molding duct by heating gases to a temperature of 70° to 90°C. for a period of about 6 minutes or less to cause the binder to set and form the boards; and c. removing the boards from the molding duct.
Claim 10
Dependent Claim
145 words
Method for the continuous production of lightweight cement-bonded boards comprising the steps of: a. continuously feeding to a heated molding duct formed of endless steel belts a molding composition comprising a base material selected from the group consisting of wood fiber, wood chips, lignocelluloses, mineral fibers, glass fibers, plastic chips, plastic fibers, expanded silicates, expanded clay, expanded glass and granules of foamed plastics, and a binder consisting essentially of a portland cement which contains 15 to 25% by weight of a calcium-halogen aluminate of the composition 11CaO.7Al 2 O 3 .CaX 2 , wherein X is any halogen; b. heating the molding composition in the molding duct by heating gases to a temperature of 70° to 90°C. for a period of about 6 minutes or less to cause the binder to set and form the boards; and c. removing the boards from the molding duct.
Claim 11
Dependent Claim
38 words
Method according to claim 6 wherein the portland cement additionally contains 1 to 12% by weight SO 3 in the form of sulphates selected from the group consisting of calcium sulphate, plaster of paris, gypsum, or mixtures thereof.
Claim 12
Dependent Claim
14 words
A method according to claim 1 in which the base material is expanded clay.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-21 | 1980-03-22 | 1980-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-21 | 1984-03-22 | 1984-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-21 | 1988-03-22 | 1988-09-21 | $7700.00 | Window Closed / Lapsed |