Process for the production of polyamidocarboxylic acids
Assignee: Akzona Inc
•
Filing: 1974-11-07
•
Granted: 1976-09-21
•
Expires: 1994-11-07
Abstract
Abstract A process for the producing a polyamidocarboxylic acid, or so-called polyamic acid, which is the prepolymer in forming a polyamide and which requires the reaction of a tetracarboxylic acid dianhydride with a diprimary diamine below about 50 DEG C. in an anhydrous, polar, aprotic organic solvent, characterized by an initial treatment of the dianhydride by only wetting with an inert organic solvent or by at least wetting this dianhydride with the polar, aprotic solvent and thereafter adding to the wetted dianhydride a solution of the diamine in the polar, aprotic solvent under thorough mixing, preferably within a very short period of time after treating the dianhydride. Stable polyamic acid solutions formed in this manner are useful intermediates in preparing films, filaments or other shaped polyimide products.
Inventors
- 👤 Gerhard Meyer
- 👤 Anton Toth
- 👤 Dieter Laudien
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:37
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1007; C08G73/1028; C08G73/1032
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
149 words
In a process for the production of a polyamic acid as the prepolymer in the formation of a polyimide by the reaction of approximately equimolar amounts of a tetracarboxylic acid dianhydride with a diprimary diamine at a temperature below about 50°C. and under substantially water-free conditions in an anhydrous, polar, aprotic organic solvent, the improvement which comprises: first treating the dianhydride reactant in the form of solid fine particles by adding thereto a limited amount of a solvent, using (a) an inert organic solvent in an amount sufficient only to wet said dianhydride or (b) a polar, aprotic organic solvent in an amount at least sufficient to wet said dianhydride up to an amount which forms the dianhydride into a paste or suspension; and then adding a solution of said diamine in the polar, aprotic organic solvent continuously or in portions to the thus treated dianhydride under thorough mixing.
Claim 2
Dependent Claim
149 words
In a process for the production of a polyamic acid as the prepolymer in the formation of a polyimide by the reaction of approximately equimolar amounts of a tetracarboxylic acid dianhydride with a diprimary diamine at a temperature below about 50°C. and under substantially water-free conditions in an anhydrous, polar, aprotic organic solvent, the improvement which comprises: first treating the dianhydride reactant in the form of solid fine particles by adding thereto a limited amount of a solvent, using (a) an inert organic solvent in an amount sufficient only to wet said dianhydride or (b) a polar, aprotic organic solvent in an amount at least sufficient to wet said dianhydride up to an amount which forms the dianhydride into a paste or suspension; and then adding a solution of said diamine in the polar, aprotic organic solvent continuously or in portions to the thus treated dianhydride under thorough mixing.
Claim 3
Dependent Claim
23 words
A process as claimed in claim 1 wherein the polar, aprotic solvent is selected from the group consisting of dimethylformamide, dimethylacetamide and N-methylpyrrolidone.
Claim 4
Dependent Claim
31 words
A process as claimed in claim 1 wherein the inert organic solvent is selected from the group consisting of acetone, methyl ethyl ketone, acetonitrile, benzene, toluene, xylene, hexane, cyclohexane and benzine.
Claim 5
Dependent Claim
63 words
A process as claimed in claim 1 wherein the total amount of the polar, aprotic organic solvent is at least 60% by weight up to about 99% by weight, with reference to the polyamic acid being formed, while the amount of the inert organic solvent is up to about 33% by weight, with reference to the amount of the polar, aprotic organic solvent.
Claim 6
Dependent Claim
47 words
A process as claimed in claim 4 wherein said polar, aprotic solvent is selected from the group consisting of dimethylformamide, dimethylacetamide and N-methylpyrrolidone and said inert organic solvent is selected from the group consisting of acetone, methyl ethyl ketone, acetonitrile, benzene, toluene, xylene, hexane, cyclohexane and benzine.
Claim 7
Dependent Claim
58 words
A process as claimed in claim 1 wherein the total amount of the polar, aprotic organic solvent is about 70 to 90% by weight, with reference to the polyamic acid being formed, while the amount of the inert organic solvent is up to about 25% by weight, with reference to the amount of the polar, aprotic organic solvent.
Claim 8
Dependent Claim
33 words
A process as claimed in claim 6 wherein the amount of the inert organic solvent is about 1 - 20% by weight, with reference to the amount of the polar, aprotic organic solvent.
Claim 9
Dependent Claim
47 words
A process as claimed in claim 7 wherein said polar, aprotic solvent is selected from the group consisting of dimethylformamide, dimethylacetamide and N-methylpyrrolidone and said inert organic solvent is selected from the group consisting of acetone, methyl ethyl ketone, acetonitrile, benzene, toluene, xylene, hexane, cyclohexane and benzine.
Claim 10
Dependent Claim
48 words
A process as claimed in claim 1 wherein the wetting of the dianhydride reactant proceeds at about 5°C. to 20°C. for a period of not more than about 5 minutes, after which the diamine solution is immediately added to form said polyamic acid by reaction with said dianhydride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-21 | 1980-03-22 | 1980-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-21 | 1984-03-22 | 1984-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-21 | 1988-03-22 | 1988-09-21 | $7700.00 | Window Closed / Lapsed |