Method of making a set water-in-oil emulsion including a continuous resin phase
Assignee: Wood Research and Dev Corp
•
Filing: 1971-07-01
•
Granted: 1976-09-21
•
Expires: 1991-07-01
Abstract
Abstract Cavities such as cracks and various other voids in subsurface formations are sealed such as for example, to stop lost circulation of drilling fluid in a well bore by a process wherein an emulsion having a continuous phase containing a polymerizable component, a discontinuous phase of water, and a catalyst system for the polymerizable component is forced into and allowed to set within the cavity. The catalyst and inhibitor therefor within the catalyst system are selected so that the emulsion begins to gel and set up only after the emulsion reaches the cavity which is to be plugged. The emulsion will set up in the presence of formation fluids and yield a very hard, high strength cement-like material. The resulting hardened cement-like material contains at least about 60% water dispersed therein, and can be penetrated by a drill bit without cracking or chipping.
Inventors
- 👤 John C. van Dyke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:04
CPC Classifications
C; C09; C09K; C09K8/00; C09K8/50; C09K8/502; C08; C08F; C08F299/00; C08F299/02; C08F299/04; C08F299/0407; C08F299/0414; C09K8/42; E; E21; E21B; E21B33/00; E21B33/10; E21B33/13; E21B33/138
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
184 words
A method of making a set water-in-oil emulsion including a continuous resin phase which comprises from about 40 to about 20 weight percent thereof and a discontinuous water phase which comprises from about 60 to about 80 weight percent thereof from first and second fluids comprising: a. forming said first fluid which forms said continuous resin phase, said first fluid consisting essentially of an unsaturated polyester resin of an ethylenically unsaturated aliphatic dicarboxylic acid and a saturated aliphatic glycol, an ethylenically unsaturated monomer selected from the group consisting of acrylonitrile, styrene, and methyl methacrylate, and having an effective amount of a catalyst promoter therefor mixed thoroughly therewith; b. forming said second fluid consisting essentially of water with from about 0.5 to about 5 weight percent based on the total weight of said first and second fluids of a nonionic colloidal suspension agent thoroughly admixed therein, and an effective amount of a catalyst for said polymerizable component, thoroughly admixed therein; and c. thoroughly admixing said first and second fluids to form an emulsion and allowing said emulsion to set to form said set water-in-oil emulsion.
Claim 2
Independent Claim
184 words
A method of making a set water-in-oil emulsion including a continuous resin phase which comprises from about 40 to about 20 weight percent thereof and a discontinuous water phase which comprises from about 60 to about 80 weight percent thereof from first and second fluids comprising: a. forming said first fluid which forms said continuous resin phase, said first fluid consisting essentially of an unsaturated polyester resin of an ethylenically unsaturated aliphatic dicarboxylic acid and a saturated aliphatic glycol, an ethylenically unsaturated monomer selected from the group consisting of acrylonitrile, styrene, and methyl methacrylate, and having an effective amount of a catalyst promoter therefor mixed thoroughly therewith; b. forming said second fluid consisting essentially of water with from about 0.5 to about 5 weight percent based on the total weight of said first and second fluids of a nonionic colloidal suspension agent thoroughly admixed therein, and an effective amount of a catalyst for said polymerizable component, thoroughly admixed therein; and c. thoroughly admixing said first and second fluids to form an emulsion and allowing said emulsion to set to form said set water-in-oil emulsion.
Claim 3
Dependent Claim
17 words
The method of claim 1 further comprising admixing an inhibitor for said catalyst in said first fluid.
Claim 4
Dependent Claim
27 words
The method of claim 1 wherein said first and second fluids are admixed by adding said second fluid to said first fluid while stirring the mixture thereof.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein said polymerizable component consists essentially of an unsaturated polyester resin of 1,2-propanediol and maleic acid, and styrene.
Claim 6
Dependent Claim
16 words
The method of claim 4 wherein said catalyst comprises benzoyl peroxide and said promoter comprises dimethyltoluidine.
Claim 7
Dependent Claim
22 words
The method of claim 4 wherein said catalyst comprises ketone peroxide and hydrogen peroxide and said promoter comprises cobalt octoate and dimethylaniline.
Claim 8
Dependent Claim
28 words
The method of claim 1 further comprising admixing a particulate inert nonionic filler having a particle size in the range of 4 to 20 microns with said emulsion.
Claim 9
Dependent Claim
28 words
The method of claim 7 wherein from 1 to 100 parts by weight of said filler material are added to each 100 parts by weight of said emulsion.
Claim 10
Dependent Claim
15 words
The method of claim 8 wherein said particulate inert nonionic filler material is iron oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-21 | 1980-03-22 | 1980-09-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-21 | 1984-03-22 | 1984-09-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-21 | 1988-03-22 | 1988-09-21 | $7700.00 | Window Closed / Lapsed |