Powdered coating materials
Assignee: Hoechst AG
•
Filing: 1974-07-01
•
Granted: 1976-09-14
•
Expires: 1994-07-01
Abstract
Abstract A process for the manufacture of a powdered coating material having a basis of hardenable synthetic resins, hardeners and pigments selected from the group consisting of metals, metal alloys, and mica for coatings with a metallic appearance wherein the single components are mixed in a finely divided state under an atmosphere of a protective gas and wherein the mixture is plasticized, under homogenization, at a temperature at which the viscosity of the synthetic resin is higher than the drop viscosity, but at most sufficiently high as to guarantee the flow, is homogenized by shearing stress and transformed into a powdered state, a powdered coating material prepared by said process and an article being coated with said coating material.
Inventors
- 👤 Gerhard Johannes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:13
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/03; C09D5/032; C08; C08J; C08J3/00; C08J3/20; C08J3/203
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
188 words
A process for producing a powdered fusible coating material comprising the steps of: 1. mixing under a protective gaseous atmosphere a mixture comprising finely divided particles of: A. a hardenable synthetic resin selected from the group consisting of epoxy resins, alkyd melamine precondensates, polyester resins, polyurethane resins, acrylic resins and mixtures thereof wherein the synthetic resin has a particle size up to 5 mm B. a hardener for said hardenable synthetic resin having a particle size in the range of 1 to 50 μ C. a pigment selected from the group consisting of aluminum, copper, copper-zinc alloy, mica and a mixture of mica and titanium dioxide having a particle size of 1 to 50 μ and being present in an amount equaling 1 to 30 percent by weight of the mixture D. a flow agent selected from the group consisting of polyacrylates, silicone oil, silicone greases and plasticizers 2. plasticising the mixture at a temperature of 100°C to 140°C to produce a viscous plasticised mixture, and 3. homogenizing the plasticised mixture at a temperature of 100° to 160°C under shearing forces to produce a powdered fusible coating material.
Claim 2
Dependent Claim
188 words
A process for producing a powdered fusible coating material comprising the steps of: 1. mixing under a protective gaseous atmosphere a mixture comprising finely divided particles of: A. a hardenable synthetic resin selected from the group consisting of epoxy resins, alkyd melamine precondensates, polyester resins, polyurethane resins, acrylic resins and mixtures thereof wherein the synthetic resin has a particle size up to 5 mm B. a hardener for said hardenable synthetic resin having a particle size in the range of 1 to 50 μ C. a pigment selected from the group consisting of aluminum, copper, copper-zinc alloy, mica and a mixture of mica and titanium dioxide having a particle size of 1 to 50 μ and being present in an amount equaling 1 to 30 percent by weight of the mixture D. a flow agent selected from the group consisting of polyacrylates, silicone oil, silicone greases and plasticizers 2. plasticising the mixture at a temperature of 100°C to 140°C to produce a viscous plasticised mixture, and 3. homogenizing the plasticised mixture at a temperature of 100° to 160°C under shearing forces to produce a powdered fusible coating material.
Claim 3
Dependent Claim
77 words
The process of claim 1 wherein the hardenable synthetic resin is selected from the group consisting of an epoxy resin of diphenylolpropane and epichlorohydrin, a polyurethane, a polyester of terephthalic acid and trimellitic anhydride, a polyacrylate and mixtures thereof and wherein a plasticiser is used selected from the group consisting of C 8 to C 10 phthalates, dicyclohexyl phthalates, dioctylsebacate, diisodecyladipate and stearic acid, and the mixture consists of 3 to 12 percent by weight of pigment.
Claim 4
Dependent Claim
10 words
The process of claim 1 wherein the pigment is aluminum.
Claim 5
Dependent Claim
32 words
A process as claimed in claim 1 wherein the shearing stress is controlled by at least one of (a) agitation velocity, (b) feeding velocity and (c) apparatus temperature of the processing apparatus.
Claim 6
Dependent Claim
13 words
A process as claimed in claim 1 wherein the process is performed continuously.
Claim 7
Dependent Claim
22 words
A process as claimed in claim 1, wherein the average particle size of the synthetic resin is between 1 and 5 mm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-14 | 1980-03-15 | 1980-09-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-14 | 1984-03-15 | 1984-09-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-14 | 1988-03-15 | 1988-09-14 | $7700.00 | Window Closed / Lapsed |