Deposition of solid semiconductor compositions and novel semiconductor materials
Assignee: Westinghouse Electric Corp
•
Filing: 1973-07-23
•
Granted: 1976-09-07
•
Expires: 1993-07-23
Abstract
Abstract Solid layer semiconductor compositions are deposited by the simultaneous sputtering from a sputter target and electrically discharge a reacting gas preferably by application of an RF potential. Preferably, the method is used to make solid solution layers and most desirably solid solution epitaxial layers of at least two semiconductor materials. The method may be used to make novel metastable compositions such as (GaAs)1-xSix, (GaAs)1-xGex, (InSb)1-xSix, (InSb)1-xGex, (InAs)1-xSix and (InAs)1-xGex (where x is a number greater than about 0.01, and x + (1-x) = 1, and GaxAsySiz, GaxAsyGez, InxSbySiz, InxSbyGez, InxAsySiz, InxAsyGez and InxSbyAsz (where x, y and z are numbers greater than about 0.01, and x + y + z = 1).
Inventors
- 👤 Alexander J. Noreika
- 👤 Maurice H. Francombe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 03:46
CPC Classifications
C; C30; C30B; C30B23/00; C30B23/02; C23; C23C; C23C14/00; C23C14/0021; C23C14/0036; C30B29/00; C30B29/10; C30B29/40; C30B29/46; C30B29/48; C30B29/52; H; H10; H10D; H10D62/00; H10D62/40; H10D62/80; H10D62/83; H10D62/832; H10D62/85; H10D62/852; H10D62/86; H10D62/862; H10P; H10P14/00; H10P14/20; H10P14/22; H10P14/24; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2911; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3412; H10P14/3414; H10P14/3421; Y; Y10; Y10S; Y10S148/00; Y10S148/005; Y10S148/017; Y10S148/059; Y10S148/063; Y10S148/067; Y10S148/072; Y10S148/158; Y10S148/169; Y10S420/00; Y10S420/903
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
205 words
A method of forming a solid semiconductor layer on a substrate comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of Group IIIa-Va and Group IVa-IVa compounds and Group IIIa, Group IVa, and Group Va elements for forming material to be deposited on the substrate; B. disposing each formed sputter target and a substrate prepared for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of Group IIIa, Group IVa and Group Va elements for forming material to be deposited such that the formed sputter target or targets introduced reactive gas composition or compositions are capable of forming all the materials to be deposited on the substrate; D. sputtering the component material from at least one said sputter target to deposit material on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas composition to deposit material on the substrate, and forming on the substrate, with the material deposited by sputtering, said solid layer of semiconductor material.
Claim 2
Independent Claim
205 words
A method of forming a solid semiconductor layer on a substrate comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of Group IIIa-Va and Group IVa-IVa compounds and Group IIIa, Group IVa, and Group Va elements for forming material to be deposited on the substrate; B. disposing each formed sputter target and a substrate prepared for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of Group IIIa, Group IVa and Group Va elements for forming material to be deposited such that the formed sputter target or targets introduced reactive gas composition or compositions are capable of forming all the materials to be deposited on the substrate; D. sputtering the component material from at least one said sputter target to deposit material on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas composition to deposit material on the substrate, and forming on the substrate, with the material deposited by sputtering, said solid layer of semiconductor material.
Claim 3
Dependent Claim
44 words
A method of forming a solid semiconductor layer on a substrate as set forth in claim 1 wherein: the deposition by both sputtering and electrical discharge reacting are performed by applying an RF potential across the substrate and at least one said sputter target.
Claim 4
Dependent Claim
104 words
A method of forming a solid semiconductor layer on a substrate as set forth in claim 2 wherein; 1 in the step of forming said sputter target each said component material is selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, tin, boron nitride, aluminum nitride, gallium nitride, indium nitride, boron phosphide, aluminum phosphide, gallium phosphide, indium phosphide, aluminum arsenide, gallium arsenide, indium arsenide, aluminum antimonide, gallium antimonide and indium antimonide; 2 in the step of introducint said gas mixture each said element is selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, tin, phosphorus, arsenic and antimonv.
Claim 5
Dependent Claim
103 words
A method of forming a solid semiconductor layer on a substrate as set forth in claim 1 wherein: 1. in the step of forming said sputter target each said component material is selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, tin, boron nitride, aluminum nitride, gallium nitride, indium nitride, boron phosphide, aluminum phosphide, gallium phosphide, indium phosphide, aluminum arsenide, gallium arsenide, indium arsenide, aluminum antimonide, gallium antimonide and indium antimonide; 2. in the step of introducint said gas mixture each said element is selected from the group consisting of boron, aluminum, gallium, silicon, germanium, tin, phosphorus, arsenic and antimony.
Claim 6
Independent Claim
206 words
A method for epitaxially growing a layer of semiconductor material comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of Group IIIa-Va and Group IVa--IVa compounds and Group IIIa, Group IVa and Group Va elements for forming semiconductor material to be grown; B. disposing each formed sputter target and a substrate prepared for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the Vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of Group IIIa, Group IVa and Group Va elements for forming semiconductor material to be grown such that the formed sputter target or targets and introduced reactive gas composition or compositions are capable of forming all the semiconductor material desired in said layer of semiconductor material; D. sputtering the component material from at least one said target to deposit material on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas composition to deposit material on the substrate, and epitaxially growing on the substrate, with material deposited by sputtering, said epitaxial layer of desired semiconductor material.
Claim 7
Independent Claim
206 words
A method for epitaxially growing a layer of semiconductor material comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of Group IIIa-Va and Group IVa--IVa compounds and Group IIIa, Group IVa and Group Va elements for forming semiconductor material to be grown; B. disposing each formed sputter target and a substrate prepared for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the Vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of Group IIIa, Group IVa and Group Va elements for forming semiconductor material to be grown such that the formed sputter target or targets and introduced reactive gas composition or compositions are capable of forming all the semiconductor material desired in said layer of semiconductor material; D. sputtering the component material from at least one said target to deposit material on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas composition to deposit material on the substrate, and epitaxially growing on the substrate, with material deposited by sputtering, said epitaxial layer of desired semiconductor material.
Claim 8
Dependent Claim
43 words
A method for epitaxially growing a layer of semiconductor materials as set forth in claim 5 wherein: the deposition both by sputtering and electrical discharge reacting are performed by applying an RF potential across the substrate and at least one said sputter target.
Claim 9
Dependent Claim
105 words
A method of epitaxially growing a substantially homogenous layer of semiconductor materials as set forth in claim 6 wherein: 1. in the step of forming said sputter target each said component material is selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, tin, boron nitride, aluminum nitride, gallium nitride, indium nitride, boron phosphide, aluminum phosphide, gallium phosphide, indium phosphide, aluminum arsenide, gallium arsenide, indium arsenide, aluminum antimonide, gallium antimonide and indium antimonide; 2. in the step of introducing said gas mixture each said element is selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, tin, phosphorus, arsenic and antimony.
Claim 10
Dependent Claim
105 words
A method of epitaxially growing a substantially homogeneous layer of semiconductor materials as set forth in claim 5 wherein: 1. in the step of forming said sputter target each said component material is selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, tin, boron nitride, aluminum nitride, gallium nitride, indium nitride, boron phosphide, aluminum phosphide, gallium phosphide, indium phosphide, aluminum arsenide, gallium arsenide, indium arsenide, aluminum antimonide, gallium antimonide and indium antimonide; 2. in the step of introducing said gas mixture each said element is selected from the group consisting of boron aluminum, gallium, indium, silicon, germanium, tin, phosphorus, arsenic and antimony.
Claim 11
Independent Claim
232 words
A method for forming a substantially homogeneous layer of semiconductor material comprising the steps of: A. forming at least one sputter target containing at least one first component selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, boron nitride, aluminum nitride, gallium nitride, indium nitride, boron phosphide, aluminum phosphide, gallium phosphide, indium phosphide, aluminum arsenide, indium arsenide, aluminum antimonide, gallium antimonide, indium antimonide and silicon germanium for forming semiconductor material to be grown; B. disposing each formed sputter target and a substrate prepared for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one second component selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, nitrogen, phosphorus, arsenic and antimony for forming semiconductor material to be grown such that the formed sputter target or targets and introduced reactive gas composition or compositions are capable of forming all the semiconductor materials to be deposited on the substrate; D. sputtering the first component from at least one said sputter target to deposit said first component on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas to deposit said second component on the substrate and forming on the substrate, with said first component, said substantially homogeneous layer of semiconductor material.
Claim 12
Independent Claim
232 words
A method for forming a substantially homogeneous layer of semiconductor material comprising the steps of: A. forming at least one sputter target containing at least one first component selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, boron nitride, aluminum nitride, gallium nitride, indium nitride, boron phosphide, aluminum phosphide, gallium phosphide, indium phosphide, aluminum arsenide, indium arsenide, aluminum antimonide, gallium antimonide, indium antimonide and silicon germanium for forming semiconductor material to be grown; B. disposing each formed sputter target and a substrate prepared for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one second component selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, nitrogen, phosphorus, arsenic and antimony for forming semiconductor material to be grown such that the formed sputter target or targets and introduced reactive gas composition or compositions are capable of forming all the semiconductor materials to be deposited on the substrate; D. sputtering the first component from at least one said sputter target to deposit said first component on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas to deposit said second component on the substrate and forming on the substrate, with said first component, said substantially homogeneous layer of semiconductor material.
Claim 13
Dependent Claim
133 words
A method for forming a substantially homogeneous layer of semiconductor material as set forth in claim 9 comprising in addition: F. forming at least one second sputter target of a third component selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, boron nitride, aluminum nitride, gallium nitride, indium nitride, boron phosphide, aluminum phosphide, gallium arsenide, indium arsenide, aluminum antimonide, gallium antimonide, indium antimonide and germanium silicon; G. disposing each second sputter target in the vacuum chamber in a spaced relation with the substrate; and H. simultaneously with the steps D and E, sputtering the third component from at least one said second sputter target to deposit said third component on the substrate and forming on the substrate, with said first and second component, said substantially homogeneous layer of semiconductor material.
Claim 14
Dependent Claim
120 words
A method for forming a substantially homogeneous layer of semiconductor material as set forth in claim 9 wherein: the sputter target contains in addition a third component selected from the group consisting of boron, aluminum, gallium, indium, silicon, germanium, boron nitride, aluminum, gallium nitride, indium nitride, boron phosphide, aluminum phosphide, gallium phosphide, indium phosphide, aluminum arsenide, gallium arsenide, indium arsenide, aluminum antimonide, gallium antimonide, indium antimonide and silicon germanium; and comprises in addition: F. sputtering the third component simultaneously with the sputtering of the first component from at least one said sputter target to deposit said third component on the substrate and forming on the substrate, with the first and second components, said substantially homogeneous layer of semiconductor component material.
Claim 15
Dependent Claim
48 words
A method for forming a substantially homogeneous layer of semiconductor material as set forth in claim 9 wherein: the gas mixture contains at least two reactive gas compositions that react in step E to form a volatile by-product gas and said second component that is a semiconductor material.
Claim 16
Dependent Claim
98 words
A method for forming a substantially homogeneous layer of semiconductor material as set forth in claim 9 comprising in addition: F. introducing into the vacuum chamber in the gas mixture, with the reactive gas composition containing the second component that is a semiconductor material, a second reactive gas composition containing a third component that is semiconductor material; and G. simultaneously with steps D and E, electrically discharge reacting the second reactive gas to deposit the third component on the substrate and forming, on the substrate with the first and second component, said substantially homogeneous layer of semiconductor materials.
Claim 17
Dependent Claim
27 words
A method for forming a substantially homogeneous layer of semiconductor material as set forth in claim 9 wherein: said first and second components are each semiconductor materials.
Claim 18
Independent Claim
220 words
A method of forming an integral sputter target of at least two semiconductor materials comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of Group IIIa-Va and Group IVa-IVa compounds and Group IIIa, Group IVa and Group Va elements for forming a material to form an integral sputter target; B. disposing each formed sputter target and an electrode for forming the integral sputter target thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of Group III, Group IVa and Group Va elements for forming a material to form an integral sputter target such that the formed sputter target or targets and introduced reactive gas composition or compositions are capable of forming all materials desired for an integral sputter target; D. sputtering the component material from at least one formed target to deposit material on said electrode; and E. simultaneously with step D, electrically discharge reacting with at least one reactive gas composition to deposit material on said electrode and forming on said electrode, with the material deposited by sputtering, the integral sputter target of said at least two semiconductor materials.
Claim 19
Independent Claim
220 words
A method of forming an integral sputter target of at least two semiconductor materials comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of Group IIIa-Va and Group IVa-IVa compounds and Group IIIa, Group IVa and Group Va elements for forming a material to form an integral sputter target; B. disposing each formed sputter target and an electrode for forming the integral sputter target thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of Group III, Group IVa and Group Va elements for forming a material to form an integral sputter target such that the formed sputter target or targets and introduced reactive gas composition or compositions are capable of forming all materials desired for an integral sputter target; D. sputtering the component material from at least one formed target to deposit material on said electrode; and E. simultaneously with step D, electrically discharge reacting with at least one reactive gas composition to deposit material on said electrode and forming on said electrode, with the material deposited by sputtering, the integral sputter target of said at least two semiconductor materials.
Claim 20
Dependent Claim
44 words
A method of forming an integral sputter target of two semiconductor materials as set forth in claim 15 wherein: the depositions both by sputtering and electrical discharge reacting are performed by applying an RF potential across the substrate and at least one sputter target.
Claim 21
Independent Claim
170 words
A method of forming a solid semiconductor layer on a substrate comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of lead, tin, germanium, tellurium, selenium and compounds thereof; B. disposing each formed sputter target and a substrate proposed for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of lead, tin, germanium, tellurium and selenium such that the formed sputter target or targets, introduced reactive gas composition or compositions, or both include lead; D. sputtering the component material from at least one said sputter target to deposit material on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas composition to deposit material on the substrate, and forming on the substrate, with the material deposited by sputtering, said solid semiconductor layer.
Claim 22
Independent Claim
170 words
A method of forming a solid semiconductor layer on a substrate comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of lead, tin, germanium, tellurium, selenium and compounds thereof; B. disposing each formed sputter target and a substrate proposed for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of lead, tin, germanium, tellurium and selenium such that the formed sputter target or targets, introduced reactive gas composition or compositions, or both include lead; D. sputtering the component material from at least one said sputter target to deposit material on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas composition to deposit material on the substrate, and forming on the substrate, with the material deposited by sputtering, said solid semiconductor layer.
Claim 23
Dependent Claim
43 words
A method of forming a solid semiconductor layer on the substrate as set forth in claim 17 wherein: the deposition by both sputtering and electrical discharge reacting are performed by applying an RF potential across the substrate and at least one sputter target.
Claim 24
Independent Claim
168 words
A method of forming a solid semiconductor layer on a substrate comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of mercury, cadmium, tellurium, selenium and compounds thereof; B. disposing each formed sputter target and a substrate proposed for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of mercury, cadmium, tellurium and selenium such that the formed sputter target or targets, introduced reactive gas composition or compositions, or both include mercury; D. sputtering the component material from at least one said sputter target to deposit material on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas composition to deposit material on the substrate, and forming on the substrate, with the material deposited by sputtering, said solid semiconductor layer.
Claim 25
Independent Claim
168 words
A method of forming a solid semiconductor layer on a substrate comprising the steps of: A. forming at least one sputter target containing at least one component material selected from the group consisting of mercury, cadmium, tellurium, selenium and compounds thereof; B. disposing each formed sputter target and a substrate proposed for deposition thereon in a spaced relation in a partial vacuum chamber; C. introducing into the vacuum chamber a gas mixture containing at least one reactive gas composition containing at least one element selected from the group consisting of mercury, cadmium, tellurium and selenium such that the formed sputter target or targets, introduced reactive gas composition or compositions, or both include mercury; D. sputtering the component material from at least one said sputter target to deposit material on the substrate; and E. simultaneously with step D, electrically discharge reacting at least one said reactive gas composition to deposit material on the substrate, and forming on the substrate, with the material deposited by sputtering, said solid semiconductor layer.
Claim 26
Dependent Claim
43 words
A method of forming a solid semiconductor layer on the substrate as set forth in claim 19 wherein: the deposition by both sputtering and electrical discharge reacting are performed by applying an RF potential across the substrate and at least one sputter target.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-07 | 1980-03-08 | 1980-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-07 | 1984-03-08 | 1984-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-07 | 1988-03-08 | 1988-09-07 | $7700.00 | Window Closed / Lapsed |