Lightweight cellular cement compositions and methods of casting the same
Assignee: TRI-SEAL INTERNATIONAL Inc A CORP OF NY
•
Filing: 1975-05-05
•
Granted: 1976-09-07
•
Expires: 1995-05-05
Abstract
Abstract The present invention relates to novel lightweight cellular cement compositions, methods of preparing such compositions and methods of casting the compositions into lightweight high strength structural members.
Inventors
- 👤 David L. Sutton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:06
CPC Classifications
B; B28; B28B; B28B1/00; B28B1/008; B28B1/50; B28C; B28C5/00; B28C5/38; B28C5/381; B28C5/386; B28C5/388; C; C04; C04B; C04B28/00; C04B28/02
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
163 words
A method of producing an integral lightweight high strength cement composition having at least one high strength densified layer adjacent at least on lightweight cellular layer comprising mixing hydraulic cement; water added in an amount of about 23-80% by weight of said dry cement; a foam stabilizer added in an amount 0.25-5% by weight of dry cement selected from organic surfactants, inorganic lamellar particulate and mixtures thereof; a dispersing agent selected and added to facilitate formation of a high strength densified layer prior to setting of said composition; and air added in an amount sufficient to reduce density to less than about 80 pounds per cubic foot; forming said cement composition into the desired shape; positioning an air and water permeable material adjacent the cement composition; promoting and controlling formation of said high strength densified layer by establishing a pressure differential across said permeable material causing air and water to flow from the layer to be densified and allowing said composition to set.
Claim 2
Independent Claim
163 words
A method of producing an integral lightweight high strength cement composition having at least one high strength densified layer adjacent at least on lightweight cellular layer comprising mixing hydraulic cement; water added in an amount of about 23-80% by weight of said dry cement; a foam stabilizer added in an amount 0.25-5% by weight of dry cement selected from organic surfactants, inorganic lamellar particulate and mixtures thereof; a dispersing agent selected and added to facilitate formation of a high strength densified layer prior to setting of said composition; and air added in an amount sufficient to reduce density to less than about 80 pounds per cubic foot; forming said cement composition into the desired shape; positioning an air and water permeable material adjacent the cement composition; promoting and controlling formation of said high strength densified layer by establishing a pressure differential across said permeable material causing air and water to flow from the layer to be densified and allowing said composition to set.
Claim 3
Dependent Claim
51 words
A method of claim 1 for producing an integral lightweight high strength cement composition having at least two high strength densified layers adjacent at least one lightweight cellular layer, wherein said cement composition is formed into the desired shape by at least two walls of said air and water permeable material.
References Cited (Backward Citations)
US2046867A
Cited
US2167200A
Cited
US3506747A
Cited
US3679445A
Cited
US3729328A
Cited
US3782983A
Cited
US3758319A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-09-07 | 1980-03-08 | 1980-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-09-07 | 1984-03-08 | 1984-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-09-07 | 1988-03-08 | 1988-09-07 | $7700.00 | Window Closed / Lapsed |