Abstract
Abstract A polyethylene composition consisting of: (A) a high density polyethylene with a viscosity-average molecular weight of 10 x 104 to 20 x 104, a number average molecular weight of 1 x 104 or greater and a ratio between weight average molecular weight and number average molecular weight of 20 or less; (B) at least one inorganic calcium compound selected from a group consisting of calcium sulfite, calcium sulfate and calcium carbonate; and (C) a solid lubricant, if desired, the composition produces a film or sheet whose internal tearing resistance is high and equal in both longitudinal and lateral directions and the processibility of the resin composition may be extremely improved by incorporating as a fourth component, within a range of 1:5 to 5:1 in weight ratio with respect to the aforementioned high density polyethylene, a different high density polyethylene with a melt index of 0.1 to 1.0.
Inventors
- 👤 Hidehiko Kaji
- 👤 Takeshi Matsumoto
- 👤 Norio Sugi
- 👤 Atsuo Ikenaga
- 👤 Shoichi Iwata
- 👤 Masami Tomikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 16:21
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/30; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08L2205/00; C08L2205/02; C08L2205/025
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
232 words
A calendered filled polyethylene sheet material obtained by kneading together under a temperature within the range of about 140°-170°C and then calendering into sheet form a polyethylene resin composition consisting essentially of: a. a first high density polyethylene having a viscosity-average molecular weight of 10 × 10 4 to 20 × 10 4 , a number average molecular weight of 1 ×10 4 or greater and a ratio between weight average molecular weight and a number average molecular weight of 20 or less, and a melt index of about 0.01-0.09; b. a second high density polyethylene distinct from said first polyethylene (a) having a viscosity-average molecular weight of 5-10 ×10 4 , a number average molecular weight of 0.5-1.0 ×10 4 and a melt index of 0.1 to 1.0; c. at least one inorganic calcium compound having a particle size of about 0.1-10 μ and selected from a group consisting of calcium sulfite, calcium sulfate and calcium carbonate in an amount sufficient to give a weight ratio relative to the aggregate of said polyethylene being 3:7 to 8:2, and d. about 0.3 to 5.0% by weight of a solid waxy lubricant with respect to the total quantity of (a) and (b), the second polyethylene (b) being present in an amount sufficient to render the composition workable by kneading and calendering up to a ratio of 5:1 relative to said first polyethylene (a).
Claim 2
Dependent Claim
232 words
A calendered filled polyethylene sheet material obtained by kneading together under a temperature within the range of about 140°-170°C and then calendering into sheet form a polyethylene resin composition consisting essentially of: a. a first high density polyethylene having a viscosity-average molecular weight of 10 × 10 4 to 20 × 10 4 , a number average molecular weight of 1 ×10 4 or greater and a ratio between weight average molecular weight and a number average molecular weight of 20 or less, and a melt index of about 0.01-0.09; b. a second high density polyethylene distinct from said first polyethylene (a) having a viscosity-average molecular weight of 5-10 ×10 4 , a number average molecular weight of 0.5-1.0 ×10 4 and a melt index of 0.1 to 1.0; c. at least one inorganic calcium compound having a particle size of about 0.1-10 μ and selected from a group consisting of calcium sulfite, calcium sulfate and calcium carbonate in an amount sufficient to give a weight ratio relative to the aggregate of said polyethylene being 3:7 to 8:2, and d. about 0.3 to 5.0% by weight of a solid waxy lubricant with respect to the total quantity of (a) and (b), the second polyethylene (b) being present in an amount sufficient to render the composition workable by kneading and calendering up to a ratio of 5:1 relative to said first polyethylene (a).
Claim 3
Dependent Claim
34 words
The sheet material according to claim 1 wherein said second polyethylene (b) is present in an amount equal to a ratio of 1:5 to 5:1 relative to the amount of said first polyethylene (a).
Claim 4
Dependent Claim
14 words
The sheet material according to claim 1 wherein said calcium compound is calcium sulfite.
Claim 5
Dependent Claim
19 words
The sheet material according to claim 1 wherein at least about 0.3% by weight of said lubricant is present.
Claim 6
Independent Claim
223 words
A method of making a polyethylene sheet material which comprises kneading under a temperature within the range of about 140°-170°C and then calendering into sheet form a mixture consisting essentially of: (a) a first high density polyethylene having a viscosity-average molecular weight of 10 × 10 4 to 20 ×10 4 , a number average molecular weight of 1 × 10 4 or greater and a ratio between weight average molecular weight and a number average molecular weight of 20 or less and a melt index of 0.01 0.09; b. a second high density polyethylene distinct from said first polyethylene (a) having a viscosity-average molecular weight of 5-10 × 10 4 , a number average molecular weight of 0.5-1.0 ×10 4 , and a melt index of 0.1 to 1.0; c. at least one inorganic calcium compound selected from a group consisting of calcium sulfite, calcium sulfate and calcium carbonate in an amount sufficient to give a weight ratio relative to the aggregate of said polyethylene being 3:7 to 8:2; and d. about 0.3 to 5.0% by weight of a solid lubricant with respect to the total quantity of (a) and (b), the second polyethylene (b) being present in an amount sufficient to render the composition workable by kneading and calendering up to a ratio of 5:1 relative to said first polyethylene (a).
Claim 7
Independent Claim
223 words
A method of making a polyethylene sheet material which comprises kneading under a temperature within the range of about 140°-170°C and then calendering into sheet form a mixture consisting essentially of: (a) a first high density polyethylene having a viscosity-average molecular weight of 10 × 10 4 to 20 ×10 4 , a number average molecular weight of 1 × 10 4 or greater and a ratio between weight average molecular weight and a number average molecular weight of 20 or less and a melt index of 0.01 0.09; b. a second high density polyethylene distinct from said first polyethylene (a) having a viscosity-average molecular weight of 5-10 × 10 4 , a number average molecular weight of 0.5-1.0 ×10 4 , and a melt index of 0.1 to 1.0; c. at least one inorganic calcium compound selected from a group consisting of calcium sulfite, calcium sulfate and calcium carbonate in an amount sufficient to give a weight ratio relative to the aggregate of said polyethylene being 3:7 to 8:2; and d. about 0.3 to 5.0% by weight of a solid lubricant with respect to the total quantity of (a) and (b), the second polyethylene (b) being present in an amount sufficient to render the composition workable by kneading and calendering up to a ratio of 5:1 relative to said first polyethylene (a).
Claim 8
Dependent Claim
33 words
The method according to claim 5 wherein said second polyethylene (b) is present in an amount equal to a ratio of 1:5 to 5:1 relative to the amount of said first polyethylene (a).
Claim 9
Dependent Claim
13 words
The method according to claim 5 wherein said calcium compound is calcium sulfite.
References Cited (Backward Citations)
US3278471A
Cited
US3409574A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-24 | 1980-02-23 | 1980-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-24 | 1984-02-23 | 1984-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-24 | 1988-02-23 | 1988-08-24 | $7700.00 | Window Closed / Lapsed |