Abstract The present invention relates to a process for producing an anti-pilling acrylic fiber which has excellent level dyeing properties. This process involves dissolving an acrylonitrile in an inorganic solvent to prepare a spinning solution, wherein the inorganic solvent in the spinning solution is 40-70%, subjecting the spinning solution to wet-spinning by extrusion through spinneret orifices into a coagulation bath containing an inorganic solvent in an amount of 50-70% of that in the spinning solution, while maintaining the linear velocity ratio of free extrusion at 1 or higher and the jet stretch ratio 1.5 or higher, stretching the formed gel fibers 3-7 times the length in hot water or in a heated steam medium at 80°-120°C, drying the stretched fibers and then subjecting the fibers to a relaxation treatment in a hot air current at a temperature of 150°C or lower or in a wet heat atmosphere at a temperature of 120°C or lower. The jet stretch ratio is defined as being the quotient obtained by dividing the takeup speed of the coagulated filaments from the coagulation step by the linear velocity of extrusion of the spinning solution through the spinneret orifices.
A process for producing an anti-pilling acrylic fiber which comprises dissolving an acrylonitrile polymer in a rhodanide solvent to prepare a spinning solution, wherein a rhodanide solvent in the spinning solution is 40-70%, subjecting the spinning solution to wet-spinning by extrusion through spinneret orifices into a coagulation bath containing a rhodanide solvent in an amount of 50-70% of that in the spinning solution, while maintaining the linear velocity ratio of free extrusion at 1 or higher, and the jet stretch ratio 1.5 or higher, stretching the formed gel fibers 3-7 times the length in hot water or in a heated steam medium at 80°-120°C, drying the stretched fibers and then subjecting the fibers to a relaxation treatment in a hot air current at a temperature of 150°C or lower or in a wet heat atmosphere at a temperature of 120°C or lower, said jet stretch ratio being the quotient obtained by dividing the takeup speed of the coagulated filaments from the coagulation step by the linear velocity of extrusion of the spinning solution through the spinneret orifices.
Claim 2
Dependent Claim
177 words
A process for producing an anti-pilling acrylic fiber which comprises dissolving an acrylonitrile polymer in a rhodanide solvent to prepare a spinning solution, wherein a rhodanide solvent in the spinning solution is 40-70%, subjecting the spinning solution to wet-spinning by extrusion through spinneret orifices into a coagulation bath containing a rhodanide solvent in an amount of 50-70% of that in the spinning solution, while maintaining the linear velocity ratio of free extrusion at 1 or higher, and the jet stretch ratio 1.5 or higher, stretching the formed gel fibers 3-7 times the length in hot water or in a heated steam medium at 80°-120°C, drying the stretched fibers and then subjecting the fibers to a relaxation treatment in a hot air current at a temperature of 150°C or lower or in a wet heat atmosphere at a temperature of 120°C or lower, said jet stretch ratio being the quotient obtained by dividing the takeup speed of the coagulated filaments from the coagulation step by the linear velocity of extrusion of the spinning solution through the spinneret orifices.
Claim 3
Dependent Claim
30 words
A process according to claim 1 wherein the fibers are introduced into a second extrusion bath which contains a rhodanide solvent in amounts 20-35% of that in the spinning solution.
Claim 4
Dependent Claim
28 words
A process according to claim 1, wherein the rhodanide solvent is selected from the group consisting of sodium rhodanide, potassium rhodanide, ammonium rhodanide, calcium rhodanide and mixtures thereof.