Water in oil emulsion process for preparing gel-free polyelectrolyte particles

Claim 2

An inverse emulsion polymerization process for preparing polymer particles which form gel-free aqueous solutions which process comprises: a. refluxing with vigorous agitation an azeotropic emulsion mixture consisting essentially of a major amount of oil and a minor amount of water and an emulsifier; and b. continuously adding to the agitated, refluxing emulsion mixture an aqueous solution containing a polymerization initiator and at least about 50 percent by weight of the solution of at least one water-soluble, oil insoluble ethylenically unsaturated monomer adapted to polymerize under reflux conditions whereby the said monomer polymerizes essentially immediately in particulate form.

Claim 3

The process of claim 1 wherein the oil is toluene.

Claim 4

The process of claim 2 wherein at least one water-soluble monomer is acrylamide and wherein the aqueous solution further contains a minor amount of a gel inhibitor.

Claim 5

The process of claim 3 wherein the aqueous monomer solution is added to the refluxing water-in-oil emulsion at a temperature of from about 85° to about 110°C. and at substantially atmospheric pressure.

Claim 6

The process of claim 4 wherein the gel inhibitor is 1,3-butylene glycol.

Claim 7

The process of claim 5 wherein the emulsifier is sorbitan monooleate.

Claim 8

An inverse emulsion polymerization process for preparing polyacrylamide particles which process comprises: a. heating to reflux an azeotropic water-in-toluene emulsion wherein the water-in-toluene emulsion consists essentially of from about 36 to about 95 percent by weight toluene, from about 0.1 to about 35 percent by weight water, and from about 1.0 to about 10.0 percent by weight emulsifier based on the total weight of the reaction mixture; b. vigorously agitating said refluxing azeotropic water-in-toluene emulsion; c. continuously adding to said agitated, refluxing azeotropic water-in-toluene emulsion a concentrated aqueous solution of acrylamide with small amounts of ammonium persulfate and 1,3-butylene glycol wherein said aqueous acrylamide solution contains from about 50 to about 70 percent by weight acrylamide, from about 30 to about 50 percent by weight water, from about 0.001 to about 0.05 percent by weight polymerization initiator, and from about 0.1 to about 3.0 percent by weight 1,3-butylene glycol based on the total weight of the aqueous solution whereby the said monomer polymerizes essentially immediately forming particulate polymers; and d. recovering said particulate acrylamide polymers from said polymerization medium.

Claim 9

An inverse emulsion polymerization process for preparing polyacrylamide particles which process comprises: a. heating to reflux an azeotropic water-in-toluene emulsion wherein the water-in-toluene emulsion consists essentially of from about 36 to about 95 percent by weight toluene, from about 0.1 to about 35 percent by weight water, and from about 1.0 to about 10.0 percent by weight emulsifier based on the total weight of the reaction mixture; b. vigorously agitating said refluxing azeotropic water-in-toluene emulsion; c. continuously adding to said agitated, refluxing azeotropic water-in-toluene emulsion a concentrated aqueous solution of acrylamide with small amounts of ammonium persulfate and 1,3-butylene glycol wherein said aqueous acrylamide solution contains from about 50 to about 70 percent by weight acrylamide, from about 30 to about 50 percent by weight water, from about 0.001 to about 0.05 percent by weight polymerization initiator, and from about 0.1 to about 3.0 percent by weight 1,3-butylene glycol based on the total weight of the aqueous solution whereby the said monomer polymerizes essentially immediately forming particulate polymers; and d. recovering said particulate acrylamide polymers from said polymerization medium.

Claim 10

The process of claim 7 wherein said aqueous acrylamide solution also contains another ethylenically unsaturated comonomer wherein the weight ratio of acrylamide to the other monomer is from about 20:1 to about 1:1.

Claim 11

The process of claim 7 wherein the water-in-toluene emulsion contains from about 50 to about 85 percent by weight toluene, from about 0.5 to about 20 percent by weight water, and from about 1.5 to about 6.0 percent by weight emulsifier based on the total weight of the reaction mixture, and wherein said aqueous acrylamide solution contains from about 55 to about 65 percent by weight acrylamide, from about 35 to about 45 percent by weight water, from about 0.005 to about 0.04 percent by weight polymerization initiator, and from about 0.15 to about 2.5 percent by weight 1,3-butylene glycol based on the total weight of the aqueous solution,

Claim 12

The process of claim 8 wherein the aqueous acrylamide solution is added to the water-in-toluene emulsion at a temperature of from about 87° to about 105°C. and at substantially atmospheric pressure.

Claim 13

The process of claim 8 wherein the polyacrylamide particles are dried by azeotropically removing the water and the polyacrylamide particles are further dried by suction filtration.

Claim 14

An inverse emulsion polymerization process for preparing polymer particles which process comprises: a. refluxing an azeotropic water-in-toluene emulsion consisting essentially of from about 0.9 to about 12 percent by weight of water, from about 60 to about 75 percent by weight of toluene, and from about 2.0 to about 4.0 percent by weight of an emulsifying agent based upon the total weight of the reaction mixture; b. vigorously agitating said refluxing water-in-toluene emulsion; c. continuously adding to the agitated, refluxing azeotropic water-in-toluene emulsion a concentrated aqueous solution of from about 60 to about 64 percent by weight of at least one ethylenically unsaturated monomer, from about 36 to about 40 percent by weight of water, from about 0.008 to about 0.03 percent by weight of a polymerization initiator and from about 0.20 to about 2.0 percent by weight of a gel inhibitor based upon the total weight of the aqueous solution at a temperature of from about 90° to about 95°C. and at substantially atmospheric pressure thereby polymerizing said monomer essentially immediately, and d. recovering said polymerized product.

Claim 15

An inverse emulsion polymerization process for preparing polymer particles which process comprises: a. refluxing an azeotropic water-in-toluene emulsion consisting essentially of from about 0.9 to about 12 percent by weight of water, from about 60 to about 75 percent by weight of toluene, and from about 2.0 to about 4.0 percent by weight of an emulsifying agent based upon the total weight of the reaction mixture; b. vigorously agitating said refluxing water-in-toluene emulsion; c. continuously adding to the agitated, refluxing azeotropic water-in-toluene emulsion a concentrated aqueous solution of from about 60 to about 64 percent by weight of at least one ethylenically unsaturated monomer, from about 36 to about 40 percent by weight of water, from about 0.008 to about 0.03 percent by weight of a polymerization initiator and from about 0.20 to about 2.0 percent by weight of a gel inhibitor based upon the total weight of the aqueous solution at a temperature of from about 90° to about 95°C. and at substantially atmospheric pressure thereby polymerizing said monomer essentially immediately, and d. recovering said polymerized product.

Claim 16

The process of claim 12 wherein said ethylenically unsaturated monomer comprises acrylamide and at least one other ethylenically unsaturated comonomer in a weight ratio of acrylamide to the other monomer of from about 10:1 to about 1.5:1.

Claim 17

The process of claim 13 wherein said gel inhibitor is 1,3-butylene glycol and said polymerization inhibitor is ammonium persulfate.