Manufacture of polymers of net-shaped structure
Assignee: BASF SE
•
Filing: 1974-09-09
•
Granted: 1976-08-17
•
Expires: 1994-09-09
Abstract
Abstract A process for the manufacture of polymers of net-shaped crosslinked structure and with uniform length of the crosslinks. In this process, polyfunctional organoalkali metal compounds which have been manufactured by reaction of divinylbenzene with low molecular weight organoalkali metal compounds, are reacted direct, or after prior reaction with anionically polymerizable monomers, with bifunctional or polyfunctional coupling agents. The polymers of net-shaped crosslinked structure have macroporous properties and can be employed, for example, as gels in gel permeation chromatography or as carriers in the synthesis of peptides.
Inventors
- 👤 Walther Burchard
- 👤 Helmut Eschwey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:24
CPC Classifications
C; C08; C08G; C08G81/00; C08G81/02; C08G81/021; B; B01; B01J; B01J20/00; B01J20/22; C08F; C08F257/00
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
182 words
A process for the manufacture of polymers of net-shaped crosslinked structure and with uniform length of crosslinks, by reaction of low molecular weight organoalkali metal compounds with bifunctional or polyfunctional coupling agents, wherein I. a. mixtures of divinylbenzene with monovinyl-aromatic compounds and having a divinylbenzene content of from 10 to 80% by weight and b. low molecular weight organoalkali metal compounds with up to 50 carbon atoms in the organic radical are reacted with one another in an inert organic solvent, the content of divinylbenzene in the reaction mixture not exceeding 2.5 percent by weight, based on the reaction mixture, and the molar ratio of divinylbenzene to the alkali metal content of the low molecular weight organoalkali metal compound being from 0.5 : 1 to 20 : 1, and thereafter Ii. the polymeric polyfunctional organoalkali metal compounds thus obtained are reacted, with bifunctional or polyfunctional coupling agents such as divinylbenzene, diisopropenylbenzene, divinylanthracene, terephthalic acid dimethyl ester, methylene chloride and 1,2-dibromoethane in a molar ratio of coupling agent to alkali metal content of the polymeric polyfunctional organoalkali metal compound of less than 1:1.
Claim 2
Dependent Claim
182 words
A process for the manufacture of polymers of net-shaped crosslinked structure and with uniform length of crosslinks, by reaction of low molecular weight organoalkali metal compounds with bifunctional or polyfunctional coupling agents, wherein I. a. mixtures of divinylbenzene with monovinyl-aromatic compounds and having a divinylbenzene content of from 10 to 80% by weight and b. low molecular weight organoalkali metal compounds with up to 50 carbon atoms in the organic radical are reacted with one another in an inert organic solvent, the content of divinylbenzene in the reaction mixture not exceeding 2.5 percent by weight, based on the reaction mixture, and the molar ratio of divinylbenzene to the alkali metal content of the low molecular weight organoalkali metal compound being from 0.5 : 1 to 20 : 1, and thereafter Ii. the polymeric polyfunctional organoalkali metal compounds thus obtained are reacted, with bifunctional or polyfunctional coupling agents such as divinylbenzene, diisopropenylbenzene, divinylanthracene, terephthalic acid dimethyl ester, methylene chloride and 1,2-dibromoethane in a molar ratio of coupling agent to alkali metal content of the polymeric polyfunctional organoalkali metal compound of less than 1:1.
Claim 3
Dependent Claim
50 words
A process as set forth in claim 1 wherein said polymeric polyfunctional organoalkali metal compound has an intrinsic viscosity [η] of less than 50 cm 3 /g and wherein said coupling agent is selected from the group consisting of divinylbenzene, diisopropenylbenzene, divinylanthracene, terephthalic acid dimethyl ester, methylene chloride and 1,2-dibromoethane.
Claim 4
Dependent Claim
53 words
A process as set forth in claim 1 wherein said polymeric polyfunctional organoalkali metal compounds obtained are, after prior reaction with anionically polymerizable monomers, reacted with said bifunctional or polyfunctional coupling agents in a molar ratio of coupling agent to alkali metal content of the polyfunctional organoalkali metal compound of less than 1:1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-17 | 1980-02-16 | 1980-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-17 | 1984-02-16 | 1984-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-17 | 1988-02-16 | 1988-08-17 | $7700.00 | Window Closed / Lapsed |