Steam-activated olefin disproportionation catalysts
Assignee: Phillips Petroleum Co
•
Filing: 1975-01-20
•
Granted: 1976-08-10
•
Expires: 1995-01-20
Abstract
Abstract Molybdenum or rhenium containing olefin disproportionation catalysts exhibit marked increase in olefin disproportionation activity when thermally activated by heating in the presence of water or water vapor.
Inventors
- 👤 Donald H. Kubicek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:30
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/84; B01J23/889; B01J23/8898; B01J23/16; B01J37/00; B01J37/08; B01J37/10
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
134 words
A method for activating a supported molybdenum oxide or rhenium oxide catalyst composition which comprises treating said supported composition under thermal activation conditions at elevated temperatures with water or water vapor, and therefter calcining said thermally treated catalyst composition in the presence of molecular oxygen-containing gases, wherein said support is silica-containing alumina-containing, or mixtures of silica and alumina, and wherein when said supported catalyst composition is said supported molybdenum oxide, said molybdenum oxide catalyst composition further can contain a cobalt component in the range of up to 20 weight percent expressed as CoO relative to the weight of the total catalyst, and wherein said thermal activation conditions at elevated temperatures with water or water vapor are conducted at elevated temperatures of at least about 700° F. in the substantial absence of molecular oxygen-containing gases.
Claim 2
Independent Claim
134 words
A method for activating a supported molybdenum oxide or rhenium oxide catalyst composition which comprises treating said supported composition under thermal activation conditions at elevated temperatures with water or water vapor, and therefter calcining said thermally treated catalyst composition in the presence of molecular oxygen-containing gases, wherein said support is silica-containing alumina-containing, or mixtures of silica and alumina, and wherein when said supported catalyst composition is said supported molybdenum oxide, said molybdenum oxide catalyst composition further can contain a cobalt component in the range of up to 20 weight percent expressed as CoO relative to the weight of the total catalyst, and wherein said thermal activation conditions at elevated temperatures with water or water vapor are conducted at elevated temperatures of at least about 700° F. in the substantial absence of molecular oxygen-containing gases.
Claim 3
Dependent Claim
40 words
The process according to claim 1 wherein said supported molybdenum or rhenium catalyst composition contains about 0.5 to 30 weight percent of molybdenum or rhenium expressed as the most stable oxide thereof relative to the total catalyst composition including support.
Claim 4
Dependent Claim
21 words
The process according to claim 2 wherein said catalyst composition is a supported molybdenum oxide catalyst and incorporates said cobalt component.
Claim 5
Dependent Claim
45 words
The method according to claim 2 wherein said thermal activation step is conducted with steam at a temperature in the range of about 700° to 1300°F., at a pressure of about 0 to 1000 psig, for a contacting time of up to about 6 hours.
Claim 6
Dependent Claim
64 words
The method according to claim 1 wherein said thermal activation step is conducted by treating said supported molybdenum or rhenium catalyst composition with liquid water, thereafter applying sufficient heat to convert said liguid water substantially to steam, and maintaining contact with said steam for up to about 6 hours at a pressure of 0 to 1000 psig and a temperature of 700 to 1300°F.
Claim 7
Dependent Claim
14 words
The method of claim 1 wherein said thermal activation is conducted in closed means.
Claim 8
Dependent Claim
15 words
The method according to claim 1 wherein said supported composition is molybdenum oxide on alumina.
Claim 9
Dependent Claim
15 words
The method according to claim 1 wherein said supported composition is cobalt molybdate on alumina.
Claim 10
Dependent Claim
9 words
The catalyst prepared by the method of claim 1.
Claim 11
Dependent Claim
9 words
The catalyst prepared by the method of claim 8.
Claim 12
Dependent Claim
120 words
In a process of preparing a catalyst composition, the steps comprising: a. admixing at least one molybdenum or rhenium compound with a support, wherein said compound is the oxide or compound convertible to the oxide on calcination in a molecular oxygen-containing atmosphere, wherein said support is silica-containing, alumina-containing, or mixtures of silica and alumina, and wherein when said molybdenum compound is employed, optionally further employing a cobalt compound which is the oxide or compound convertible thereto on calcination, b. thermally activating the resulting admixture with water or water vapor at elevated temperatures of at least about 700° F. in the substantial absence of molecular oxygen-containing gases, and c. calcining the thermally activated admixture in contact with a molecular oxygen-containing gas.
Claim 13
Dependent Claim
120 words
In a process of preparing a catalyst composition, the steps comprising: a. admixing at least one molybdenum or rhenium compound with a support, wherein said compound is the oxide or compound convertible to the oxide on calcination in a molecular oxygen-containing atmosphere, wherein said support is silica-containing, alumina-containing, or mixtures of silica and alumina, and wherein when said molybdenum compound is employed, optionally further employing a cobalt compound which is the oxide or compound convertible thereto on calcination, b. thermally activating the resulting admixture with water or water vapor at elevated temperatures of at least about 700° F. in the substantial absence of molecular oxygen-containing gases, and c. calcining the thermally activated admixture in contact with a molecular oxygen-containing gas.
Claim 14
Dependent Claim
21 words
The process according to claim 11 wherein said thermal activation elevated temperature is in the range of about 700°F. to 1300°F.
Claim 15
Dependent Claim
30 words
The process according to claim 12 wherein said thermal activation is conducted at a pressure of about 0 to 1000 psig for a time of up to about 6 hours.
Claim 16
Dependent Claim
39 words
The process according to claim 11 wherein said supported composition contains about 0.5 to 30 weight percent molybdenum oxide or rhenium oxide based on the total catalyst composition, said molybdenum or rhenium calculated as the most stable oxide thereof.
Claim 17
Dependent Claim
34 words
The process according to claim 14 wherein said supported composition is said supported molybdenum catalyst and further contains said cobalt component in the range of up to 20 weight percent expressed as cobalt oxide.
Claim 18
Dependent Claim
16 words
The process according to claim 11 wherein said supported composition is supported rhenium oxide catalyst composition.
Claim 19
Dependent Claim
9 words
The catalyst prepared by the process of claim 11.
Claim 20
Dependent Claim
89 words
In a process for preparing a rhenium catalyst, the steps comprising: a. admixing a rhenium compound, which is the oxide or compound convertible to the oxide on calcination in a molecular oxygen-containing atmosphere, with a support, which is silica, alumina, or silica- or alumina-containing support, b. thermally activating said admixture in contact with water or water vapor under thermal activation conditions at a temperature of at least about 700°F., and c. calcining said thermally activated admixture in contact with a molecular oxygen-containing gas, thereby preparing an activated rhenium catalyst.
Claim 21
Dependent Claim
89 words
In a process for preparing a rhenium catalyst, the steps comprising: a. admixing a rhenium compound, which is the oxide or compound convertible to the oxide on calcination in a molecular oxygen-containing atmosphere, with a support, which is silica, alumina, or silica- or alumina-containing support, b. thermally activating said admixture in contact with water or water vapor under thermal activation conditions at a temperature of at least about 700°F., and c. calcining said thermally activated admixture in contact with a molecular oxygen-containing gas, thereby preparing an activated rhenium catalyst.
Claim 22
Dependent Claim
19 words
The process according to claim 18 wherein said thermal activation is conducted at temperatures of about 700°F. to 1300°F.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-10 | 1980-02-09 | 1980-08-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-10 | 1984-02-09 | 1984-08-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-10 | 1988-02-09 | 1988-08-10 | $7700.00 | Window Closed / Lapsed |