Bicomponent polyester filaments and process for making same
Assignee: Rhone Poulenc Textile SA
•
Filing: 1975-03-18
•
Granted: 1976-08-03
•
Expires: 1995-03-18
Abstract
Abstract Bicomponent polyester filaments are disclosed, wherein the filaments are made of at least two different, substantially unmixed components, each present in an amount of at least 20% by weight of the total filament, one component being polyethylene terephthalate and the other component being polybutylene terephthalate which has been sparingly crosslinked with trimethylolpropane. The bicomponent polyester filaments of the present invention have excellent physical properties and especially improved permanency of crimping. The filaments may be used to manufacture woven and knit materials, and are especially useful in the manufacture of hosiery, wherein the resulting hosiery articles have excellent wear properties.
Inventors
- 👤 Gerard Barbe
- 👤 Robert Habault
- 👤 Jean-Louis Tamet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:21
CPC Classifications
D; D01; D01F; D01F8/00; D01F8/04; D01F8/14; D01D; D01D5/00; D01D5/28; D01D5/30; D01D5/32; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2922; Y10T428/2924; Y10T428/2933; Y10T428/2964; Y10T428/2967
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
86 words
Helically crimped bicomponent polyester filaments of improved elasticity and substantially permanent crimping, said filaments comprising at least 20% by weight of two different, substantially unmixed components in a side-by-side assembly along the length of said filaments, one component being polyethylene terephthalate and the other component being sparingly crosslinked polybutylene terephthalate having at least 0.20 mole percent of crosslinking agent, based on the terephthalic acid content of the polybutylene terephthalate, wherein the sparingly crosslinked polybutylene terephthalate has a viscosity value IV of about 1000 of about 1500.
Claim 2
Dependent Claim
86 words
Helically crimped bicomponent polyester filaments of improved elasticity and substantially permanent crimping, said filaments comprising at least 20% by weight of two different, substantially unmixed components in a side-by-side assembly along the length of said filaments, one component being polyethylene terephthalate and the other component being sparingly crosslinked polybutylene terephthalate having at least 0.20 mole percent of crosslinking agent, based on the terephthalic acid content of the polybutylene terephthalate, wherein the sparingly crosslinked polybutylene terephthalate has a viscosity value IV of about 1000 of about 1500.
Claim 3
Dependent Claim
28 words
Product of claim 1 wherein the polybutylene terephthalate contains about 0.20 to about 0.60 mole % of trimethylolpropane, based on the terephthalic acid content of the polybutylene terephthalate.
Claim 4
Dependent Claim
24 words
Product of claim 1 wherein the polyethylene terephthalate has a melted state viscosity VF of about 800 to about 2500 poises at 290° C.
Claim 5
Dependent Claim
20 words
The product of claim 3 wherein the polyethylene terephthalate has a viscosity value IV of about 450 to about 800.
Claim 6
Dependent Claim
26 words
Product of claim 1 wherein the sparingly crosslinked polybutylene terephthalate has a melted state viscosity VF of about 3500 to about 5500 poises at 260° C.
Claim 7
Dependent Claim
18 words
The product of claim 1, wherein the polybutylene terephthalate contains about 0.3 to 0.4 mole percent of trimethylolpropane.
Claim 8
Dependent Claim
21 words
The product of claim 1 wherein each component of the filament is present in an amount of about 50% by weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-03 | 1980-02-02 | 1980-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-03 | 1984-02-02 | 1984-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-03 | 1988-02-02 | 1988-08-03 | $7700.00 | Window Closed / Lapsed |