⏱️ 0.0 years remaining
Method for the preparation of porous ferrous metal impregnated with magnesium metal
Assignee: Farley Inc
•
Filing: 1975-03-25
•
Granted: 1976-08-03
•
Expires: 1995-03-25
Abstract
Abstract A composition of matter comprising a mass of ferrous scrap pieces compressed together in random orientation forming a network of interlocking pieces has been prepared. The ferrous metal network has a density of 1.2 to 4.0 g/cc, a porosity of 50% to 85% and a short transverse tensile strength (S.T.T.S.) of at least 2 psi, preferably at least 2.5 psi.
Inventors
- 👤 Jairaj Easwaran
- 👤 George S. Foerster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:41
CPC Classifications
C; C21; C21C; C21C7/00; C21C7/04; C21C7/064; C21C1/00; C21C1/02; C21C1/10; C22; C22B; C22B1/00; C22B1/14; C22B1/24; C22B1/248; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
137 words
A process for producing a porous ferrous metal network impregnated with magnesium which comprises selecting ferrous metal scrap pieces which have a density of 0.1 to 1.0 g/cc, said scrap pieces having lengths from 1/8 to 9 inches, widths from 1/64 to 1 inch and thicknesses from 1 to 100 mils, compacting said pieces using a pressure of from 0.5 to 8.0 tons per square inch to form a metal network having a density from 1.2 to 4.0 g/cc, a porosity of 50 to 85% and a short transverse tensile strength of at least 2 psi, immersing said metal network into a molten bath of magnesium to impregnate said network with said magnesium, the impregnated metal network containing from 18 to 55% by weight of the impregnated network and removing said impregnated network from said molten magnesium.
Claim 2
Dependent Claim
137 words
A process for producing a porous ferrous metal network impregnated with magnesium which comprises selecting ferrous metal scrap pieces which have a density of 0.1 to 1.0 g/cc, said scrap pieces having lengths from 1/8 to 9 inches, widths from 1/64 to 1 inch and thicknesses from 1 to 100 mils, compacting said pieces using a pressure of from 0.5 to 8.0 tons per square inch to form a metal network having a density from 1.2 to 4.0 g/cc, a porosity of 50 to 85% and a short transverse tensile strength of at least 2 psi, immersing said metal network into a molten bath of magnesium to impregnate said network with said magnesium, the impregnated metal network containing from 18 to 55% by weight of the impregnated network and removing said impregnated network from said molten magnesium.
Claim 3
Dependent Claim
33 words
Method according to claim 1 in which the ferrous metal scrap pieces contain an oil coating and that the oil coating is removed by heating the scrap pieces to burn off the oil.
Claim 4
Dependent Claim
166 words
A process for producing a porous ferrous metal network impregnated with magnesium which comprises selecting ferrous metal scrap pieces which have a density of from 0.1 to 1.0 g/cc, said scrap metal pieces having lengths from 1/8 to 9 inches, widths from 1/64 to 1 inch and thicknesses from 1 to 100 mils, said metal scrap pieces having an oil coating on their surfaces, compacting said pieces using a pressure of from 0.5 to 8.0 tons per square inch to form a metal network having a density of from 1.2 to 4.0 g/cc, preheating said metal network at a temperature from 500° F. to 1200°F. to burn off the oil, the preheating time not exceeding one hour when temperatures of about 1200°C. are employed, and immersing said network into a molten bath of magnesium to impregnate the metal network with from 18% to 55% of magnesium by weight, based on the total weight of the impregnated network and removing said impregnated network from said molten magnesium.
Claim 5
Dependent Claim
166 words
A process for producing a porous ferrous metal network impregnated with magnesium which comprises selecting ferrous metal scrap pieces which have a density of from 0.1 to 1.0 g/cc, said scrap metal pieces having lengths from 1/8 to 9 inches, widths from 1/64 to 1 inch and thicknesses from 1 to 100 mils, said metal scrap pieces having an oil coating on their surfaces, compacting said pieces using a pressure of from 0.5 to 8.0 tons per square inch to form a metal network having a density of from 1.2 to 4.0 g/cc, preheating said metal network at a temperature from 500° F. to 1200°F. to burn off the oil, the preheating time not exceeding one hour when temperatures of about 1200°C. are employed, and immersing said network into a molten bath of magnesium to impregnate the metal network with from 18% to 55% of magnesium by weight, based on the total weight of the impregnated network and removing said impregnated network from said molten magnesium.
Claim 6
Dependent Claim
28 words
Process according to claim 3 in which the weight gain due to oxidation of the metal network during the preheating step is held to no more than 3%.
Claim 7
Dependent Claim
48 words
Process according to claim 3 in which the impregnated metal network is removed from the molten magnesium and immersed into an oil bath to cool said impregnated network, said cooled impregnated network when removed from said oil contains an oil coating to prevent oxidation of the impregnated magnesium.
References Cited (Backward Citations)
US1491392A
Cited
US2675308A
Cited
US2881068A
Cited
US2839393A
Cited
US3017267A
Cited
US3549541A
Cited
US3656989A
Cited
US3634066A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-03 | 1980-02-02 | 1980-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-03 | 1984-02-02 | 1984-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-03 | 1988-02-02 | 1988-08-03 | $7700.00 | Window Closed / Lapsed |