Abstract
Abstract Transmission mode negative electron affinity gallium arsenide (GaAs) photthodes and dynodes with a technique for the fabrication thereof, utilizing multilayers of GaAs and gallium aluminum arsenide (GaAlAs) wherein the GaAs layers serve as the emitting layer and as intermediate construction layers and the GaAlAs layer serves as a passivating window.
Inventors
- 👤 William A. Gutierrez
- 👤 Herbert L. Wilson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:17
CPC Classifications
H; H01; H01J; H01J9/00; H01J9/02; H01J9/12; H10; H10P; H10P50/00; H10P50/60; H10P50/61; H10P50/617; H10P50/64; H10P50/642; H10P50/646; Y; Y10; Y10S; Y10S148/00; Y10S148/051; Y10S148/056; Y10S148/065; Y10S148/072; Y10S148/12; Y10S148/135
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
114 words
A method of fabricating a transmission mode gallium arsenide electron emitter comprising the steps of: preparing a p-doped gallium arsenide seed crystal for growth by chemically polishing the growth surface; epitaxially growing an etch stop layer of lightly n-doped gallium arsenide onto the prepared surface of the seed crystal; epitaxially growing a p-doped gallium arsenide emitter layer onto the etch stop layer; epitaxially growing a lightly p-doped gallium aluminum arsenide passivating window layer onto the emitter layer; preferentially removing the gallium arsenide seed crystal from the etch stop layer; preferentially removing the gallium arsenide etch stop layer from the emitter layer; and providing ohmic contact means for the exposed surface of the emitter layer.
Claim 2
Independent Claim
114 words
A method of fabricating a transmission mode gallium arsenide electron emitter comprising the steps of: preparing a p-doped gallium arsenide seed crystal for growth by chemically polishing the growth surface; epitaxially growing an etch stop layer of lightly n-doped gallium arsenide onto the prepared surface of the seed crystal; epitaxially growing a p-doped gallium arsenide emitter layer onto the etch stop layer; epitaxially growing a lightly p-doped gallium aluminum arsenide passivating window layer onto the emitter layer; preferentially removing the gallium arsenide seed crystal from the etch stop layer; preferentially removing the gallium arsenide etch stop layer from the emitter layer; and providing ohmic contact means for the exposed surface of the emitter layer.
Claim 3
Dependent Claim
54 words
The method of claim 1, wherein the seed crystal is selected with a thickness of approximately 15 mils, growth of the etch stop layer is held to approximately 2 microns, growth of the emitter layer is held to a range of 1-2 microns, and growth of the passivating window reaches at least 100 microns.
Claim 4
Dependent Claim
18 words
The method of claim 1 further comprising the application of an antireflection coating to the passivating window layer.
Claim 5
Dependent Claim
26 words
The method of claim 3 wherein removal of the gallium arsenide seed crystal is effected by preferential etching in a 0.2M KOH solution by electrochemical processing.
Claim 6
Dependent Claim
24 words
The method of claim 4, wherein the preferential removal of the etch stop layer of gallium aluminum arsenide is effected by etching with HCl.
Claim 7
Dependent Claim
54 words
The method of claim 3 wherein the emitter layer is made self-standing by the preferential etching away of portions of the antireflection coating and passivating layer in a desired active region while leaving a portion of the passivating layer on the periphery of the structure as a mechanical support ring for the emitter layer.
Claim 8
Dependent Claim
21 words
The method of claim 6, wherein the selective etching away of the passivating layer is effected by a concentrated HCl etch.
Claim 9
Dependent Claim
25 words
The method of claim 7, wherein backsurface recombination velocity is minimized by ion implantation in the active region to a depth of approximately 1000 angstroms.
Claim 10
Dependent Claim
13 words
The photocathode resulting from the practice of the fabrication method of claim 6.
Claim 11
Dependent Claim
13 words
The photocathode resulting from the practice of the fabrication method of claim 1.
References Cited (Backward Citations)
US3478213A
Cited
US3672992A
Cited
US3762968A
Cited
US3862859A
Cited
US3914136A
Cited
US3901745A
Cited
US3901744A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-03 | 1980-02-02 | 1980-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-03 | 1984-02-02 | 1984-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-03 | 1988-02-02 | 1988-08-03 | $7700.00 | Window Closed / Lapsed |