Formation of laminated glass articles
Assignee: Pilkington Automotive Ltd
•
Filing: 1974-08-05
•
Granted: 1976-07-27
•
Expires: 1994-08-05
Abstract
Abstract In forming a laminated glass article a first stage comprises assembling two glass sheets with an interlayer of thermoplastic transparent plastics material and heating the assembly to a first temperature at which some softening of the plastics material occurs. In the second stage the assembly is heated to a second higher temperature and maintained at the second temperature for a period such that full bonding occurs between the glass sheets and the interlayer, and then cooled, the exposed periphery of the interlayer being maintained at a pressure which is a controlled amount below that applied to the faces of the glass sheets for at least part of the period that the assembly is heated to the second temperature.
Inventors
- 👤 John Pickard
- 👤 Richard Melling
- 👤 Arthur Joseph Nobbs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:42
CPC Classifications
B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B17/10005; B32B17/10009; B32B17/10036; B32B17/1055; B32B17/10761; B32B17/10807; B32B17/10816; B32B17/10825; B32B17/10834; B60; B60J; B60J10/00; B60J10/70; B32B2307/00; B32B2307/40; B32B2307/412; B32B2605/00
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
210 words
A method of effecting final bonding between two glass sheets with an interlayer of thermoplastic transparent plastics material between the sheets comprising the steps of: a. providing an assembly of two glass sheets with an interlayer of thermoplastic transparent plastics material between them; b. heating the assembly to an elevated temperature sufficient to render said material flowable and maintaining such temperature for a selected period of time; c. subjecting the major faces of the sheets to a pressure in excess of atmospheric pressure during said selected period of time such that the glass sheets and interlayer become fully bonded together; d. subjecting the exposed periphery of the interlayer at the edges of the sheets during said selected period of time to a pressure in excess of atmospheric pressure but lower than that applied to the faces of the sheets by an amount sufficient to provide a pressure differential between the pressures of steps (c) and (d) which is in the range of 0.14 Kg/cm 2 to 1.05 Kg/cm 2 , said lower pressure being maintained at the exposed periphery of the interlayer for at least part of the period while the assembly is maintained at said elevated pressure and temperature; and e. cooling the assembly after full bonding has occurred.
Claim 2
Independent Claim
210 words
A method of effecting final bonding between two glass sheets with an interlayer of thermoplastic transparent plastics material between the sheets comprising the steps of: a. providing an assembly of two glass sheets with an interlayer of thermoplastic transparent plastics material between them; b. heating the assembly to an elevated temperature sufficient to render said material flowable and maintaining such temperature for a selected period of time; c. subjecting the major faces of the sheets to a pressure in excess of atmospheric pressure during said selected period of time such that the glass sheets and interlayer become fully bonded together; d. subjecting the exposed periphery of the interlayer at the edges of the sheets during said selected period of time to a pressure in excess of atmospheric pressure but lower than that applied to the faces of the sheets by an amount sufficient to provide a pressure differential between the pressures of steps (c) and (d) which is in the range of 0.14 Kg/cm 2 to 1.05 Kg/cm 2 , said lower pressure being maintained at the exposed periphery of the interlayer for at least part of the period while the assembly is maintained at said elevated pressure and temperature; and e. cooling the assembly after full bonding has occurred.
Claim 3
Dependent Claim
23 words
A method according to claim 1 in which the glass sheets and interlayer are of the same shape and size when assembled together.
Claim 4
Dependent Claim
32 words
A method according to claim 1 in which the assembly is mounted in a closed pressure vessel for the application of heat and pressure to bond the interlayer and glass sheets together.
Claim 5
Dependent Claim
15 words
A method according to claim 1 in which the interlayer comprises a sheet of polyvinyl-butyral.
Claim 6
Dependent Claim
24 words
A method according to claim 3, in which the pressure in said vessel is raised to 2 Kg/cm 2 to 14 Kg/cm 2 .
Claim 7
Dependent Claim
24 words
A method according to claim 3, in which the temperature in said vessel is raised to more than 100°C, such as 120°C to 160°C.
Claim 8
Independent Claim
252 words
A method of effecting final bonding between two glass sheets with an interlayer of thermoplastic transparent plastic material between the sheets consisting of the steps of: a. providing a de-aerated and partially bonded assembly of two glass sheets with an interlayer of thermoplastic transparent plastics material; b. surrounding the periphery of the assembly with a pressure reduction chamber in sealing engagement with the periphery of the assembly such that the exposed periphery of the interlayer is in communication with the interior of the chamber; c. heating the assembly to an elevated temperature sufficient to render said material flowable; d. subjecting the major faces of the sheets to a pressure in excess of atmospheric pressure during said selected period of time such that the glass sheets and interlayer become fully bonded together; e. maintaining a pressure in the chamber which is in excess of atmospheric pressure but below that applied to the major faces of the sheets by an amount sufficient to provide a pressure differential between the pressures of steps (d) and (e) which is in the range of 0.14 Kg/cm 2 to 1.05 Kg/cm 2 so that the sheets are held together with the interlayer and the marginal edges of the sheets are drawn in towards each other for at least part of the period while the assembly is maintained at said elevated pressure and temperature; and f. cooling the assembly after bonding has occurred and maintaining the pressure differential of step (e) during at least the commencement of such cooling.
Claim 9
Independent Claim
252 words
A method of effecting final bonding between two glass sheets with an interlayer of thermoplastic transparent plastic material between the sheets consisting of the steps of: a. providing a de-aerated and partially bonded assembly of two glass sheets with an interlayer of thermoplastic transparent plastics material; b. surrounding the periphery of the assembly with a pressure reduction chamber in sealing engagement with the periphery of the assembly such that the exposed periphery of the interlayer is in communication with the interior of the chamber; c. heating the assembly to an elevated temperature sufficient to render said material flowable; d. subjecting the major faces of the sheets to a pressure in excess of atmospheric pressure during said selected period of time such that the glass sheets and interlayer become fully bonded together; e. maintaining a pressure in the chamber which is in excess of atmospheric pressure but below that applied to the major faces of the sheets by an amount sufficient to provide a pressure differential between the pressures of steps (d) and (e) which is in the range of 0.14 Kg/cm 2 to 1.05 Kg/cm 2 so that the sheets are held together with the interlayer and the marginal edges of the sheets are drawn in towards each other for at least part of the period while the assembly is maintained at said elevated pressure and temperature; and f. cooling the assembly after bonding has occurred and maintaining the pressure differential of step (e) during at least the commencement of such cooling.
Claim 10
Dependent Claim
27 words
A method according to claim 7, in which prior to applying heat to effect full bonding, the pressure in the hollow chamber is reduced below atmospheric pressure.
Claim 11
Dependent Claim
27 words
A method according to claim 8, in which some heat is applied to the assembly while the pressure in the hollow chamber is maintained below atmospheric pressure.
Claim 12
Dependent Claim
35 words
A method according to claim 8, in which some increase in pressure on the major faces of the glass sheets is effected before the pressure within the chamber is raised to atmospheric pressure or higher.
Claim 13
Dependent Claim
159 words
In the method of forming a laminated glass article, the steps of: a. assembling two glass sheets with an interlayer of thermoplastic transparent material between them; b. de-aerating and partially bonding the assembly of step (a); c. heating the assembly of step (b) to an elevated temperature sufficient to render said material thermoplastic and maintaining such temperature for a selected period of time sufficient to permit bonding of the glass sheets to the interlayer; d. during step (c), subjecting the major faces of the glass sheets to a first pressure while subjecting the periphery of the assembly to a second pressure, said first and second pressures each being greater than atmospheric and being selected such that the second pressure is lower than the first pressure and presents a pressure differential within the range 0.14 Kg/cm 2 to 1.05 Kg/cm 2 ; and then e. cooling said assembly while maintaining said pressure differential during at least commencement of such cooling.
Claim 14
Dependent Claim
159 words
In the method of forming a laminated glass article, the steps of: a. assembling two glass sheets with an interlayer of thermoplastic transparent material between them; b. de-aerating and partially bonding the assembly of step (a); c. heating the assembly of step (b) to an elevated temperature sufficient to render said material thermoplastic and maintaining such temperature for a selected period of time sufficient to permit bonding of the glass sheets to the interlayer; d. during step (c), subjecting the major faces of the glass sheets to a first pressure while subjecting the periphery of the assembly to a second pressure, said first and second pressures each being greater than atmospheric and being selected such that the second pressure is lower than the first pressure and presents a pressure differential within the range 0.14 Kg/cm 2 to 1.05 Kg/cm 2 ; and then e. cooling said assembly while maintaining said pressure differential during at least commencement of such cooling.
Claim 15
Dependent Claim
40 words
A method according to claim 11, in which the pressure differential is maintained at least during the latter part of the period while the assembly is maintained at said elevated temperature and being maintained during subsequent cooling of the assembly.
Claim 16
Dependent Claim
25 words
In the method as defined in claim 11 wherein said pressure differential is maintained in the range 0.28 Kg/cm 2 to 0.7 Kg/cm 2 .
References Cited (Backward Citations)
US3249479A
Cited
US2992953A
Cited
US3074466A
Cited
US3281296A
Cited
US3347723A
Cited
US3532590A
Cited
US3558415A
Cited
US3806387A
Cited
US3852136A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-27 | 1980-01-26 | 1980-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-27 | 1984-01-26 | 1984-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-27 | 1988-01-26 | 1988-07-27 | $7700.00 | Window Closed / Lapsed |