Adhesive composition containing a copolymer of butadiene, styrene, and acrylonitrile, plus a tackifying resin
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1974-11-29
•
Granted: 1976-07-20
•
Expires: 1994-11-29
Abstract
Abstract A rubbery copolymer of butadiene, styrene and acrylonitrile, if desired, with a tensile strength of about 50 to about 100 psig containing a minor amount of styrene, particularly in combination with selective tackifier resins. Said copolymer is preferably prepared by a step-wise aqueous emulsion polymerization with styrene and modifier being incrementally added. Said rubbery copolymer/tackifier mixture is particularly useful as an adhesive.
Inventors
- 👤 George W. Feeney
- 👤 Gary L. Burroway
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 07:32
CPC Classifications
C; C08; C08F; C08F236/00; C08F236/02; C08F236/04; C08F236/06; C09; C09J; C09J109/00; C08L; C08L2666/00; C08L2666/02; Y; Y10; Y10S; Y10S525/00; Y10S525/942
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
222 words
An adhesive composition which comprises an admixture of 100 parts by weight of the copolymer of butadiene, styrene and, optionally, acrylonitrile and about 50 to about 150 parts by weight of a tackifier resin selected from rosin esters and diolefin/olefin copolymers containing about 5 to about 35 weight percent aromatic units, where said copolymer is characterized by having an ultimate tensile strength in the range of about 50 to about 100 pounds per square inch and an ultimate elongation in the range of about 600 to about 1200 percent at 25°C, and is prepared by the method which comprises (1) aqueous emulsion free radical polymerizing in the presence of a modifier composed of primary and/or tertiary mercaptans, a monomer mixture comprising a total of 100 weight percent monomers comprised about 3 to about 8 weight percent styrene, about 97 to about 92 weight percent 1,3-butadiene and about 1 to about 4 weight percent acrylonitrile, if used, to a conversion of about 50 to about 75 weight percent of said monomers to a copolymer thereof, and (2) reacting an additional amount of about 2 to about 5 weight percent styrene, based on the total monomers used, with said copolymer to an extent of about 80 to about 98 weight percent conversion of the total monomers to a copolymer thereof, with additional mercaptan modifier.
Claim 2
Dependent Claim
222 words
An adhesive composition which comprises an admixture of 100 parts by weight of the copolymer of butadiene, styrene and, optionally, acrylonitrile and about 50 to about 150 parts by weight of a tackifier resin selected from rosin esters and diolefin/olefin copolymers containing about 5 to about 35 weight percent aromatic units, where said copolymer is characterized by having an ultimate tensile strength in the range of about 50 to about 100 pounds per square inch and an ultimate elongation in the range of about 600 to about 1200 percent at 25°C, and is prepared by the method which comprises (1) aqueous emulsion free radical polymerizing in the presence of a modifier composed of primary and/or tertiary mercaptans, a monomer mixture comprising a total of 100 weight percent monomers comprised about 3 to about 8 weight percent styrene, about 97 to about 92 weight percent 1,3-butadiene and about 1 to about 4 weight percent acrylonitrile, if used, to a conversion of about 50 to about 75 weight percent of said monomers to a copolymer thereof, and (2) reacting an additional amount of about 2 to about 5 weight percent styrene, based on the total monomers used, with said copolymer to an extent of about 80 to about 98 weight percent conversion of the total monomers to a copolymer thereof, with additional mercaptan modifier.
Claim 3
Dependent Claim
129 words
The adhesive composition of claim 1 where said tackifier resin is selected from hydrogenated rosin esters having an acid number of less than about 10 and from diolefin-olefin resins prepared by polymerizing in the presence of a catalyst selected from aluminum chloride and ethylaluminum dichloride, a monomer mixture comprised of at least one diolefin selected from piperylene along with at least one methyl branched chain α or β monoolefin containing 4 to 6 carbon atoms, where the mole ratio of diolefin to monoolefin is in the range of about 0.8/1 to about 2/1, in combination with about 10 to about 35 weight percent of at least one monomer selected from styrene and α-methyl styrene and about 0 to about 10 weight percent dicyclopentadiene, based on the total monomer mixture.
Claim 4
Dependent Claim
86 words
The adhesive composition of claim 2, prepared by mixing said copolymer and said tackifier in the presence of at least one solvent selected from toluene, benzene, xylene, pentane, hexane, heptane and octane, where said tackifier resin is selected from fully hydrogenated rosin esters and from diolefin/olefin copolymers prepared by polymerizing in the presence of aluminum chloride, a mixture comprising piperylene, olefins selected primarily from 2-methyl-1-butene and 2-methyl-2-butene, at least one monomer selected from styrene and α-methyl styrene and about 0 to about 10 weight percent dicyclopentadiene.
Claim 5
Dependent Claim
42 words
The adhesive composition of claim 2 where said diolefin/olefin resin tackifier is prepared by polymerizing piperylene with a methyl branched chain monoolefin containing 5 to 6 carbon atoms and has a softening point in the range of about 70° to about 140°C.
Claim 6
Dependent Claim
57 words
The adhesive composition of claim 1, where about 10 to about 40 weight percent of the overall modifier is a primary mercaptan and about 90 to about 60 weight percent is a tertiary mercaptan, said mercaptans containing from 8 to 16 carbon atoms with the primary added initially, and the tertiary mercaptan added with the incremental styrene.
References Cited (Backward Citations)
US2611719A
Cited
US2643235A
Cited
US2894924A
Cited
US2802808A
Cited
US3118854A
Cited
US3213159A
Cited
US3624183A
Cited
US3478005A
Cited
US3787531A
Cited
US3649425A
Cited
US3692756A
Cited
US3784530A
Cited
US3846352A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-20 | 1980-01-19 | 1980-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-20 | 1984-01-19 | 1984-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-20 | 1988-01-19 | 1988-07-20 | $7700.00 | Window Closed / Lapsed |