Mechanical seals
Assignee: U S GRAPHITE Inc A CORP OF MI
•
Filing: 1973-12-06
•
Granted: 1976-07-13
•
Expires: 1993-12-06
Abstract
Abstract A long wearing mechanical seal assembly comprising two paired sealing members of predetermined composition wherein the contacting surfaces are in rotating relationship with respect to one another, and wherein the members cooperate to prevent fluid flow between the contacting surfaces, a first one of said members being composed of a material suitable for a seal seat (e.g., cast iron, alumina ceramic or chrome plated steel) and the second member comprising a seal composed of a graphitic matrix that is filled with particulate, non-abrasive matter (e.g. Nepheline syenite, alpha-alumina or quartz) which is harder than the matrix and which has a microhardness greater than the matrix to prevent the seal from wearing at the wear rate of the matrix.
Inventors
- 👤 James R. Floyd
- 👤 Paul N. Dalenberg
- 👤 Robert B. Slivensky
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:50
CPC Classifications
F; F16; F16J; F16J15/00; F16J15/16; F16J15/34; F16J15/3496; Y; Y10; Y10S; Y10S277/00; Y10S277/922; Y10S277/935; Y10S277/936; Y10S277/939; Y10S277/94; Y10S277/943
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
161 words
In a method of preparing a mechanical seal and seat assembly of the class wherein a relatively movable seal and seat therefor have confronting sealing interfaces to seal off a fluid which wets the interface and wherein the seal comprises a graphitic matrix bonded by a binder; the steps of: homogeneously dispersing non-abrasive particles in a particulate matrix mix comprising hydrocarbon binder and graphite, compressing the mix and particles into seal form, and baking the seal to substantially dehydrogenize the binder to create a non-graphitic free carbon bond for the graphite and particles, to form a seal having said particles in said seal interface; and matching the seal interface with a seat interface, the seat interface having a microhardness of at least about 200 kilograms per square millimeter; and the particles, being of a size and shape to be non-abrasively smooth to the seat interface and having a microhardness in the range of at least about 200 kilograms per square millimeter.
Claim 2
Dependent Claim
161 words
In a method of preparing a mechanical seal and seat assembly of the class wherein a relatively movable seal and seat therefor have confronting sealing interfaces to seal off a fluid which wets the interface and wherein the seal comprises a graphitic matrix bonded by a binder; the steps of: homogeneously dispersing non-abrasive particles in a particulate matrix mix comprising hydrocarbon binder and graphite, compressing the mix and particles into seal form, and baking the seal to substantially dehydrogenize the binder to create a non-graphitic free carbon bond for the graphite and particles, to form a seal having said particles in said seal interface; and matching the seal interface with a seat interface, the seat interface having a microhardness of at least about 200 kilograms per square millimeter; and the particles, being of a size and shape to be non-abrasively smooth to the seat interface and having a microhardness in the range of at least about 200 kilograms per square millimeter.
Claim 3
Dependent Claim
16 words
The method of claim 1 wherein said particles have curvilinear surfaces which prevent them from abrading.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein said particles are so small in size that they do not abrade.
Claim 5
Dependent Claim
20 words
The method of claim 1 wherein said particles are less than 10 percent by weight of the mix and particles.
Claim 6
Dependent Claim
18 words
The method of claim 1 wherein said seat is an alumina ceramic and said particles comprise calcined alpha-alumina.
Claim 7
Dependent Claim
24 words
The method of claim 1 wherein the seat is an alumina ceramic and the particles comprise nepheline syenite, the fluid being of hydrocarbonaceous character.
Claim 8
Dependent Claim
22 words
The method of claim 1 wherein the seat is a cast iron, the particles comprise calcined alpha-alumina and the fluid incorporates oil.
Claim 9
Dependent Claim
18 words
The method of claim 1 wherein the seat is a cast iron and the particles comprise nepheline syenite.
Claim 10
Dependent Claim
20 words
The method of claim 1 wherein the particles are about 0.025 to 45 percent of the volume of the matrix.
Claim 11
Dependent Claim
21 words
The method of claim 1 wherein the particles have a particle size in the range of about 0.1 to 100 microns.
Claim 12
Dependent Claim
20 words
The method of claim 1 wherein the particles have a microhardness of about 200 to 4500 kilograms per square millimeter.
Claim 13
Dependent Claim
27 words
The method of claim 1 wherein the seat is composed of alpha-alumina ceramic and the particles are selected from the group consisting of alpha-alumina and tungsten carbide.
Claim 14
Dependent Claim
25 words
The method of claim 1 wherein the particles are selected from the group consisting of alpha-alumina, tungsten carbide, silicon-carbide, diamond dust, quartz, and nepheline syenite.
Claim 15
Dependent Claim
33 words
The method of claim 1 wherein the seal interface is machined to desired shape after the baking step, and then rendered less porous by forcing resin into its pores and curing the resin.
Claim 16
Dependent Claim
28 words
The method of claim 1 wherein the seal is machined to desired shape, and then rendered less porous by forcing a resin into its pores curing the resin.
Claim 17
Dependent Claim
35 words
The method of claim 1 wherein the non-abrasive particles are generally in the range of 1/10th of a micron to 100 microns in size, and the seal is baked at temperatures up to about 2100°F.
Claim 18
Dependent Claim
164 words
In a method of preparing a mechanical seal and seat assembly of the class wherein a relatively movable seal and seat therefor have confronting sealing interfaces to seal off a fluid which wets the interface and wherein the seal comprises a graphitic matrix bonded by a binder; the steps of homogeneously dispersing carbide forming particles in a particulate matrix mix comprising hydrocarbon binder and graphite, compressing the mix and particles into seal form, and baking the seal to substantially dehydrogenize the binder to create a non-graphitic free carbon bond for the graphite and to form dispersed carbide particles in situ in said matrix at said seal interface; and matching the seal interface with a seat interface, the seat interface having a microhardness of at least about 200 kilograms per square millimeter; and the particles being of a size and shape to be non-abrasively smooth to the seat interface and having a microhardness in the range of at least about 200 kilograms per square millimeter.
Claim 19
Dependent Claim
164 words
In a method of preparing a mechanical seal and seat assembly of the class wherein a relatively movable seal and seat therefor have confronting sealing interfaces to seal off a fluid which wets the interface and wherein the seal comprises a graphitic matrix bonded by a binder; the steps of homogeneously dispersing carbide forming particles in a particulate matrix mix comprising hydrocarbon binder and graphite, compressing the mix and particles into seal form, and baking the seal to substantially dehydrogenize the binder to create a non-graphitic free carbon bond for the graphite and to form dispersed carbide particles in situ in said matrix at said seal interface; and matching the seal interface with a seat interface, the seat interface having a microhardness of at least about 200 kilograms per square millimeter; and the particles being of a size and shape to be non-abrasively smooth to the seat interface and having a microhardness in the range of at least about 200 kilograms per square millimeter.
Claim 20
Dependent Claim
20 words
The method of claim 17 wherein the particles have a microhardness of about 200 to 4500 kilograms per square millimeter.
Claim 21
Dependent Claim
13 words
The method of claim 17 wherein the carbide forming particles comprise tungsten powder.
References Cited (Backward Citations)
US2362436A
Cited
US2425209A
Cited
US3093382A
Cited
US2886352A
Cited
US2982671A
Cited
US3218086A
Cited
US3588128A
Cited
DE1911537A1
Cited
US3619430A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-13 | 1980-01-12 | 1980-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-13 | 1984-01-12 | 1984-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-13 | 1988-01-12 | 1988-07-13 | $7700.00 | Window Closed / Lapsed |