Process for finishing tetrafluoroethylene-hexafluoropropylene copolymers
Assignee: EIDP Inc
•
Filing: 1975-04-03
•
Granted: 1976-07-13
•
Expires: 1995-04-03
Abstract
Abstract It is known to heat treat melt-processible blends of copolymers of tetrafluoroethylene and hexafluoropropylene in the molten state at elevated temperatures for several hours in the presence of an atmosphere containing water vapor in order to remove volatile material from the copolymer and to improve the thermal stability of the copolymer. Such heating results in foaming of the molten copolymer which is undesirable. According to the process of this invention, the foaming can be reduced by employing a blend of two or more of the copolymers, at least one of which has a melt viscosity higher, and at least one of which has a melt viscosity lower, than the final desired viscosity of the treated blend.
Inventors
- 👤 Charles Eugene Bailey
- 👤 Miguel Jacinto Roura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:41
CPC Classifications
C; C08; C08L; C08L27/00; C08L27/02; C08L27/12; C08L27/18
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
225 words
A process for heat stabilizing copolymers of tetrafluoroethylene and hexafluoropropylene which comprises heating between about 340°C. and about 380°C. for a time sufficient to drive off substantially all volatiles in an atmosphere of air containing between about 3% and about 20% of water vapor, based on weight of atmosphere, a blend of melt-processible copolymers of tetrafluoroethylene and hexafluoropropylene having between about 6.75 and about 27 weight percent hexafluoropropylene, said blend containing: A. 10-80% by weight of the blend of one or more of said copolymers having a melt viscosity that is: 1. at least 50 percent greater than the melt viscosity desired in the treated blend; 2. no more than five times the melt viscosity desired in the treated blend; 3. at least 13 × 10 4 poise at 372°C.; B. 10-80% by weight of the blend of one or more of said copolymers having a melt viscosity that is between 1 × 10 4 and 5 × 10 4 poise at 372°C., provided that the melt viscosity is no more than one-half the melt viscosity desired in the treated blend; and C. 0-33% by weight of the blend of one or more of said copolymers having a melt viscosity of between 5 × 10 4 and 13 × 10 4 poise at 372°C., wherein the total percent by weight of the blend comprises 100%.
Claim 2
Dependent Claim
225 words
A process for heat stabilizing copolymers of tetrafluoroethylene and hexafluoropropylene which comprises heating between about 340°C. and about 380°C. for a time sufficient to drive off substantially all volatiles in an atmosphere of air containing between about 3% and about 20% of water vapor, based on weight of atmosphere, a blend of melt-processible copolymers of tetrafluoroethylene and hexafluoropropylene having between about 6.75 and about 27 weight percent hexafluoropropylene, said blend containing: A. 10-80% by weight of the blend of one or more of said copolymers having a melt viscosity that is: 1. at least 50 percent greater than the melt viscosity desired in the treated blend; 2. no more than five times the melt viscosity desired in the treated blend; 3. at least 13 × 10 4 poise at 372°C.; B. 10-80% by weight of the blend of one or more of said copolymers having a melt viscosity that is between 1 × 10 4 and 5 × 10 4 poise at 372°C., provided that the melt viscosity is no more than one-half the melt viscosity desired in the treated blend; and C. 0-33% by weight of the blend of one or more of said copolymers having a melt viscosity of between 5 × 10 4 and 13 × 10 4 poise at 372°C., wherein the total percent by weight of the blend comprises 100%.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein the minimum amount of component (A) present is 17 weight percent of said blend.
Claim 4
Dependent Claim
14 words
The process of claim 1 wherein no component (C) is present in the blend.
Claim 5
Dependent Claim
50 words
The process of claim 1 wherein the amount of component (A) present is between about 30% and about 80% by weight of said blend and the melt viscosity of the copolymers of component (A) is between about 15 × 10 4 and about 20 × 10 4 poises at 372°C.
Claim 6
Dependent Claim
58 words
The process of claim 1 wherein, in Component (A) of the blend, the melt viscosity of said copolymers is 1. at least twice as great as the melt viscosity desired in the treated blend; 2. no more than five times the melt viscosity desired in the treated blend; 3. at least 13 × 10 4 poise at 372°C.
Claim 7
Dependent Claim
50 words
The process of claim 1 wherein the amount of component (A) present is between about 20% and about 40% by weight of said blend and the melt viscosity of the copolymers of Component (A) is between about 25 × 10 4 and about 30 × 10 4 poise at 372°C.
Claim 8
Dependent Claim
50 words
The process of claim 1 wherein the amount of component (A) present is between about 30% and about 50% by weight of said blend and the melt viscosity of the copolymers of component (A) is between about 20 × 10 4 and about 25 × 10 4 poise at 372°C.
Claim 9
Dependent Claim
30 words
The process of claim 1 wherein the melt viscosity desired in the treated blend is between about 6 × 10 4 and about 13 × 10 4 poises at 372°C.
References Cited (Backward Citations)
US2946763A
Cited
US3085083A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-13 | 1980-01-12 | 1980-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-13 | 1984-01-12 | 1984-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-13 | 1988-01-12 | 1988-07-13 | $7700.00 | Window Closed / Lapsed |