Method of providing decarbonization protection for metallic surfaces
Assignee: Vereinigte Edelstahlwerke AG
•
Filing: 1974-08-06
•
Granted: 1976-07-13
•
Expires: 1994-08-06
Abstract
Abstract An improved technique is described for effecting decarbonization protection for the surfaces of ferrous metals during heat treatment in an oxidation atmosphere. The surface to be protected is coated, prior to the heat treating step, with a paste-like substance preferably formed from a mixture of boron carbide, potassium boron fluoride, borax and an aqueous binder. The resulting protective coating, which may be sprayed on the relevant surface, has a maximum thickness of .1 mm. Such relatively thin coating having the described composition, which in larger thicknesses is useful for boron-hardening of metallic surfaces, is effective to provide the required decarbonization protection without the accompanying disadvantages of excessive boron atom diffusion.
Inventors
- 👤 Klaus Hutterer
- 👤 Walter Schwarz
- 👤 Ekkehart Krainer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 12:07
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/68; C21D1/70
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
128 words
In a method of providing decarbonization protection of a metallic surface, particularly the surface of a ferrous material, during heat treatment thereof, wherein a boron-containing substance is deposited on the surface to form an adherent scale during the heat treatment step, and wherein the scale is removed after such heat treatment, the improvement wherein the depositing comprises the step of coating the surface to be protected with a thin paste-like substance prior to the heat treatment, said substance consisting essentially of from about 12 to about 80% of at least one boron-emitting material, an activator, and an aqueous binder, the maximum thickness of such coating being 1 mm, whereby the required decarbonization protection is provided without undesired hardening of the surface by significant infusion of boron atoms therein.
Claim 2
Dependent Claim
128 words
In a method of providing decarbonization protection of a metallic surface, particularly the surface of a ferrous material, during heat treatment thereof, wherein a boron-containing substance is deposited on the surface to form an adherent scale during the heat treatment step, and wherein the scale is removed after such heat treatment, the improvement wherein the depositing comprises the step of coating the surface to be protected with a thin paste-like substance prior to the heat treatment, said substance consisting essentially of from about 12 to about 80% of at least one boron-emitting material, an activator, and an aqueous binder, the maximum thickness of such coating being 1 mm, whereby the required decarbonization protection is provided without undesired hardening of the surface by significant infusion of boron atoms therein.
Claim 3
Dependent Claim
30 words
The method according to claim 1, in which the boron-emitting material is selected from at least one of the group consisting of boron carbide, iron boride, amorphous boron, and borax.
Claim 4
Dependent Claim
40 words
The method according to claim 1, in which the activator is selected from at least one of the group consisting of a fluoro borate, a halogen compound of an alkaline metal, and a halogen compound of an alkali earth metal.
Claim 5
Dependent Claim
22 words
The method according to claim 1, in which the binder is selected from the group consisting of waterglass, methylcellulose, and sodium silicate.
Claim 6
Dependent Claim
28 words
The method according to claim 1, in which the paste-like substance is formed from a mixture of boron carbide, borax, potassium boron fluoride, and an aqueous liquid binder.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-13 | 1980-01-12 | 1980-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-13 | 1984-01-12 | 1984-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-13 | 1988-01-12 | 1988-07-13 | $7700.00 | Window Closed / Lapsed |