Molded articles of plastics having improved surface characteristics and process for producing the same
Assignee: Dai Nippon Printing Co Ltd
•
Filing: 1974-11-25
•
Granted: 1976-07-06
•
Expires: 1994-11-25
Abstract
Abstract A molded article of plastic having on its surface a cured film of a coating material comprising at least 30% by weight of at least one polyfunctional compound selected from the group consisting of poly-methacryloyloxy compounds having a molecular weight of 250 to 800 and containing at least three methacryloyloxy groups in the molecule and poly-acryloyloxy compounds having a molecular weight of 250 to 800 and containing at least three acryloyloxy groups in the molecule, and optionally 0.01 to 5% by weight of a fluorine-containing surfactant and 0.01 to 5% by weight of a carbonyl compound as photosensitizer has improved surface characteristics, particularly a high surface hardness, a high surface smoothness, high heat resistance, high abrasion resistance and a minimized optical distortion. Said molded article of plastic having improved surface characteristics can be prepared by coating the molded substrate of plastic with said coating material to a thickness of 1 to 50 mu and then subjecting the coated article to a light of 2,000 to 8,000 A in an inert atmosphere to cure the coating material.
Inventors
- 👤 Makoto Matsuo
- 👤 Takao Suzuki
- 👤 Keisuke Yoshihara
- 👤 Tuneo Ikeda
- 👤 Kunio Chikanishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 08:37
CPC Classifications
B; B29; B29C; B29C45/00; B29C45/0001; B29D; B29D11/00; B29D11/00865; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/046; C08J2433/00; Y; Y10; Y10S; Y10S428/00; Y10S428/918; Y10T; Y10T428/00; Y10T428/31; Y10T428/31504; Y10T428/31855; Y10T428/31909; Y10T428/31928; Y10T428/31935
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
113 words
A molded article of plastic having improved surface characteristics which comprises a molded substrate of plastic and a cured film formed on the surface of the molded substrate, characterized in that the cured film is formed from a coating material comprising at least 30 % by weight of at least one polyfunctional compound selected from the group consisting of polymethacryloyloxy compounds having at least three methacryloyloxy groups in one molecule and a molecular weight of 250 to 800 and polyacryloyloxy compounds having at least three acryloyloxy groups in one molecule and a molecular weight of 250 to 800, and a fluorine-containing surfactant, in which the fluorine atom, is bonded to a carbon atom.
Claim 2
Dependent Claim
113 words
A molded article of plastic having improved surface characteristics which comprises a molded substrate of plastic and a cured film formed on the surface of the molded substrate, characterized in that the cured film is formed from a coating material comprising at least 30 % by weight of at least one polyfunctional compound selected from the group consisting of polymethacryloyloxy compounds having at least three methacryloyloxy groups in one molecule and a molecular weight of 250 to 800 and polyacryloyloxy compounds having at least three acryloyloxy groups in one molecule and a molecular weight of 250 to 800, and a fluorine-containing surfactant, in which the fluorine atom, is bonded to a carbon atom.
Claim 3
Dependent Claim
41 words
A molded article of plastic according to claim 1, wherein the molded substrate of plastic is prepared from one member selected from the group consisting of polymethyl methacrylate, methyl methacrylate copolymers, polystyrene, styrene-acrylonitrile copolymers, polyallyl diglycol carbonates, polycarbonates and cellulose esters.
Claim 4
Dependent Claim
69 words
A molded article of plastic according to claim 1, wherein the molded substrate of plastic is prepared by subjecting a thermoplastic resin to injection molding using a mold capable of satisfying the condition represented by the formula, S.sub.A /S.sub.B ≧ 0.2 wherein S A is the cross-sectional area of the joint portion between the gate and the cavity, and S B is the maximum cross-sectional area of the cavity.
Claim 5
Dependent Claim
75 words
A molded article of plastic according to claim 1, wherein the molded substrate of plastic is prepared by subjecting a thermoplastic resin to injection molding under such conditions that the injection time t 1 satisfies the formulas: ##EQU3## wherein t 1 is the injection time, t 2 is the hold time, t 3 is the cooling time, V is the volume of the mold cavity, and a is the average thickness of the molded substrate.
Claim 6
Dependent Claim
83 words
A molded article of plastic according to claim 1, wherein the molded substrate of plastic is prepared by subjecting a thermoplastic resin to injection molding using a mold capable of satisfying the condition represented by the formula, S A /S B ≧0.2, wherein S A and S B are as defined above, and under such conditions that the injection time t 1 satisfies the formulas: ##EQU4## wherein t 1 , t 2 , t 3 , V and a are as defined above.
Claim 7
Dependent Claim
94 words
A molded article of plastic according to claim 1, wherein the cured film is formed from a coating material comprising at least 30 % by weight of at least one polyfunctional compound selected from the group consisting of polymethacryloyloxy compounds having at least three methacryloyloxy groups in one molecule and a molecular weight of 250 to 800 and polyacryloyloxy compounds having at least three acryloyloxy groups in one molecule and a molecular weight of 250 to 800, and at least one member selected from the group consisting of monoacryloyloxy, monomethacryloyloxy, diacryloyloxy and dimethacryloyloxy compounds.
Claim 8
Dependent Claim
20 words
A molded article of plastic according to claim 1, wherein the thickness of the cured film is 1 to 50μ.
Claim 9
Dependent Claim
27 words
A molded article of plastic according to claim 1, wherein the content of the fluorine-containing surfactant in the coating material is 0.01 to 5 % by weight.
Claim 10
Dependent Claim
20 words
A molded article of plastic according to claim 1, wherein the molded substrate of plastics is a lens shaped one.
Claim 11
Dependent Claim
55 words
A molded article of plastic according to claim 1, wherein the polyfunctional compound is a 2:8 to 8:2 weight ratio mixture of at least one of triacryloyloxy and trimethacryloyloxy compounds having a molecular weight of 250 to 800 and at least one of tetraacryloyloxy and tetramethacryloyloxy compounds having a molecular weight of 250 to 800.
Claim 12
Dependent Claim
37 words
A molded article of plastic according to claim 1, wherein the polyfunctional compound is selected from the group consisting of trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythritol tetraacrylate, pentaerythritol tetramethacrylate, glycerol triacrylate, glycerol trimethacrylate, di-trimethylolpropane tetraacrylate and di-trimethylolpropane tetramethacrylate.
Claim 13
Dependent Claim
227 words
A molded article of plastic having improved surface characteristics characterized in that % coating material comprising a polyfunctional compound consisting of 40 to 90 % by weight of a 2:8 to 8:2 weight ratio mixture of at least one of triacryloyloxy and trimethacryloyloxy compounds having a molecular weight of 250 to 800 and at least one of tetraacryloyloxy and tetramethacryloyloxy compounds having a molecular weight of 250 to 800, and 10 to 60 % by weight of at least one of diacryloyloxy, dimethacryloyloxy, monoacryloyloxy and monomethacryloyloxy compounds, 0.01 to 5 % by weight, based on the weight of the coating material, of a carbonyl compound as a photosensitizer and 0.01 to 5 % by weight, based on the weight of the coating material, of a fluorine-containing nonionic surfactant, in which the fluorine atom, is bonded to a carbon atom, is coated on the surface of a molded substrate of plastic, and is then irradiated with light of a wavelength of 2,000 to 8,000 A in an inert atmosphere to form a cured film of 3 to 30μ in thickness, said molded substrate being prepared by injection-molding polymethyl methacrylate, methyl methacrylate copolymer or polycarbonate under such conditions that the following three formulas are satisfied: ##EQU5## wherein S A , S B , t 1 , t 2 , t 3 , V and a are as defined above.
Claim 14
Dependent Claim
227 words
A molded article of plastic having improved surface characteristics characterized in that % coating material comprising a polyfunctional compound consisting of 40 to 90 % by weight of a 2:8 to 8:2 weight ratio mixture of at least one of triacryloyloxy and trimethacryloyloxy compounds having a molecular weight of 250 to 800 and at least one of tetraacryloyloxy and tetramethacryloyloxy compounds having a molecular weight of 250 to 800, and 10 to 60 % by weight of at least one of diacryloyloxy, dimethacryloyloxy, monoacryloyloxy and monomethacryloyloxy compounds, 0.01 to 5 % by weight, based on the weight of the coating material, of a carbonyl compound as a photosensitizer and 0.01 to 5 % by weight, based on the weight of the coating material, of a fluorine-containing nonionic surfactant, in which the fluorine atom, is bonded to a carbon atom, is coated on the surface of a molded substrate of plastic, and is then irradiated with light of a wavelength of 2,000 to 8,000 A in an inert atmosphere to form a cured film of 3 to 30μ in thickness, said molded substrate being prepared by injection-molding polymethyl methacrylate, methyl methacrylate copolymer or polycarbonate under such conditions that the following three formulas are satisfied: ##EQU5## wherein S A , S B , t 1 , t 2 , t 3 , V and a are as defined above.
Claim 15
Dependent Claim
26 words
A molded article of plastic according to claim 1, wherein the fluorine-containing surfactant, in which the fluorine atom, is bonded to a carbon atom is non-ionic.
Claim 16
Dependent Claim
59 words
A molded article of plastic according to claim 13, wherein the nonionic surfactant is selected from the group consisting of N-alkyl perfluorocarbon sulfonamides, N-dimethylaminopropyl perfluorocarbon sulfonamide, N-carboxylmethyl perfluorocarbon sulfonamide, polyoxyethylene perfluorocarbon sulfonamide ethers, N-dimethylamino propyl perfluorocarbon acid amides, N-alkyl perfluorocarbon acid amides, polyoxyethylene perfluorocarbon acid amide ethers, perfluorocarbon sulfonic acids, perfluorocarbon acid alkyl esters, and perfluorocarbon acid hydroxy amides.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-06 | 1980-01-05 | 1980-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-06 | 1984-01-05 | 1984-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-06 | 1988-01-05 | 1988-07-06 | $7700.00 | Window Closed / Lapsed |