Method for producing a semi-conductor body
Assignee: Federal Mogul Ignition LLC
•
Filing: 1974-10-25
•
Granted: 1976-07-06
•
Expires: 1994-10-25
Abstract
Abstract A method for producing a semi-conductor body is disclosed. The batch for the body is silicon carbide and reactive alumina. The batch is first dry ball milled with from 1/2 to 2% fatty acid and pressed into a shape. The shape is then fired either in air below 2300°F. or in an inert gas atmosphere to a temperature from about 2000° to 3000°F., and for a time sufficiently long to produce a semi-conductor body having a specified apparent porosity. An impregnation step is also disclosed to achieve the specified apparent porosity.
Inventors
- 👤 Francis H. Dulin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 02:51
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/515; C04B35/56; C04B35/565; C04B41/45; C04B41/50; C04B41/5076; C04B41/5089; C04B41/80; C04B41/81; C04B41/85; H; H01; H01B; H01B1/00; H01T; H01T13/00; H01T13/40; H01T13/41
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
159 words
A method for producing a semi-conductor body which consists essentially of mixing from 20 to 80 parts by weight of silicon carbide substantially all of which has a particle size from 150 to 800 mesh, with from 80 to 20 parts by weight of reactive alumina, substantially all of which has a particle size less than about 2 microns, dry ball milling the mixture for about 2 hours with from 1/2 to 2 percent by weight fatty acid, based on the alumina, pressing a shape from the resulting mixture and firing the shape to a temperature from about 1900° to 3000° F., with the proviso that the firing, when in air, is to a temperature from about 1900° to 2300° F. and when in an inert gas atmosphere, is to a temperature from about 2000° to 3000° F., and for a time sufficiently long to produce a semi-conductor body having an apparent porosity from substantially 10 to 25 percent.
Claim 2
Independent Claim
159 words
A method for producing a semi-conductor body which consists essentially of mixing from 20 to 80 parts by weight of silicon carbide substantially all of which has a particle size from 150 to 800 mesh, with from 80 to 20 parts by weight of reactive alumina, substantially all of which has a particle size less than about 2 microns, dry ball milling the mixture for about 2 hours with from 1/2 to 2 percent by weight fatty acid, based on the alumina, pressing a shape from the resulting mixture and firing the shape to a temperature from about 1900° to 3000° F., with the proviso that the firing, when in air, is to a temperature from about 1900° to 2300° F. and when in an inert gas atmosphere, is to a temperature from about 2000° to 3000° F., and for a time sufficiently long to produce a semi-conductor body having an apparent porosity from substantially 10 to 25 percent.
Claim 3
Dependent Claim
29 words
A method as claimed in claim 1 wherein from 30 to 80 parts by weight 400 mesh silicon carbide and 70 to 20 parts by weight alumina are present.
Claim 4
Dependent Claim
22 words
A method as claimed in claim 2 wherein 52 parts by weight silicon carbide and 48 parts by weight alumina are present.
Claim 5
Dependent Claim
41 words
A method as claimed in claim 1 wherein from 10 to 40 parts by weight 400 mesh silicon carbide, from 10 to 40 parts by weight 800 mesh silicon carbide, and from 20 to 80 parts by weight alumina are present.
Claim 6
Dependent Claim
35 words
A method as claimed in claim 4 wherein about 26 parts by weight 400 mesh silicon carbide, about 26 parts by weight 800 mesh silicon carbide and about 48 parts by weight alumina are present.
Claim 7
Dependent Claim
14 words
A method as claimed in claim 1 wherein the fatty acid is oleic acid.
Claim 8
Dependent Claim
54 words
A method as claimed in claim 1 wherein prior to firing, the shape is impregnated with a silicate selected from the group consisting of ammonium silicate and ethyl silicate, treated with a gelling agent selected from the group consisting of a basic gas, an acid gas and an acid- or base-releasing compound, and dried.
Claim 9
Dependent Claim
14 words
A method as claimed in claim 7 wherein the organic silicate is ethyl silicate.
Claim 10
Dependent Claim
24 words
A method as claimed in claim 7 wherein the gelling agent is selected from the group consisting of CO 2 and NH 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-06 | 1980-01-05 | 1980-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-06 | 1984-01-05 | 1984-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-06 | 1988-01-05 | 1988-07-06 | $7700.00 | Window Closed / Lapsed |