Abstract An improved technique for producing optical fibers is disclosed. In this technique the optical fiber preform is fabricated by axial deposition from a direction along the preform axis as opposed to radial deposition from a direction perpendicular to the preform axis. The instant technique does not require a cylindrical mandrel and, consequently, the technique does not require removal of a mandrel and the collapse of a non-solid preform prior to drawing. In addition to these advantages, the technique may be used to form optical fibers with highly resolved longitudinal gradations in index of refraction. The resolution of such gradations when formed using the instant technique is limited only by the deposition rate and the ability to rapidly alter the concentration of the material being deposited.
A method of forming an optical fiber, comprising: forming thermochemically a particulate glass precursor material capable of being consolidated into a glass of optical loss less than 50 db/km; rotating a base member about an axis substantially perpendicular to its flat surface; directing axially a stream of the said particulate matter onto the rotating flat base member from a direction substantially perpendicular to the surface of the base member; and drawing the structure into an optical fiber.
Claim 2
Independent Claim
77 words
A method of forming an optical fiber, comprising: forming thermochemically a particulate glass precursor material capable of being consolidated into a glass of optical loss less than 50 db/km; rotating a base member about an axis substantially perpendicular to its flat surface; directing axially a stream of the said particulate matter onto the rotating flat base member from a direction substantially perpendicular to the surface of the base member; and drawing the structure into an optical fiber.
Claim 3
Dependent Claim
26 words
The method of claim 1 wherein the composition of the particulate material is varied during the deposition to yield a spatially periodic longitudinally graded optical fiber.
Claim 4
Dependent Claim
20 words
The method of claim 2 wherein the gradations in the optical fiber are between 1mm and 10mm in longitudinal extent.
Claim 5
Dependent Claim
13 words
The method of claim 1 where the particulate material is SiO 2 .
Claim 6
Dependent Claim
24 words
The method of claim 2 wherein the particulate material is SiO 2 , and is doped with Ge to yield the said longitudinal gradation.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein the particulate material is formed by means of a hydrolysis burner.