Grain refinement of titanium carbide tool steel
Assignee: Alloy Technology International Inc
•
Filing: 1973-11-06
•
Granted: 1976-06-29
•
Expires: 1993-11-06
Abstract
Abstract A sintered steel-bonded titanium carbide composition characterized by an improved combination of physical and anti-friction properties is provided comprising about 15% to 60% by weight of primary grains of titanium carbide dispersed through a steel matrix making up essentially the balance, the steel matrix being characterized metallographically by an austenitic decomposition product, said steel-bonded titanium carbide composition containing an effective amount of a grain-growth inhibitor ranging by weight from about 0.25% to 2% of a columbium-group carbide.
Inventors
- 👤 M. Kumar Mal
- 👤 Stuart E. Tarkan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:58
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0278; C22C33/0292; F; F01; F01C; F01C19/00; F01C19/02; Y; Y10; Y10T; Y10T428/00; Y10T428/26; Y10T428/268
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
71 words
A steel-bonded titanium carbide composition formed of primary grains of titanium carbide of average size less than 5 microns dispersed through a steel matrix characterized by an austenitic decomposition product, said composition containing an effective amount of a grain-growth inhibitor corresponding to by weight of about 0.25% to 2% of a Group VB carbide, said composition in the hardened state being characterized by improved anti-friction properties and improved resistance to wear.
Claim 2
Dependent Claim
71 words
A steel-bonded titanium carbide composition formed of primary grains of titanium carbide of average size less than 5 microns dispersed through a steel matrix characterized by an austenitic decomposition product, said composition containing an effective amount of a grain-growth inhibitor corresponding to by weight of about 0.25% to 2% of a Group VB carbide, said composition in the hardened state being characterized by improved anti-friction properties and improved resistance to wear.
Claim 3
Dependent Claim
42 words
The steel-bonded titanium carbide composition of claim 1, wherein the amount of titanium carbide in said composition ranges by weight from about 15% to 60%, and wherein said grain-growth inhibitor is selected from the group consisting of columbium carbide and tantalum carbide.
Claim 4
Dependent Claim
22 words
The steel-bonded titanium carbide composition of claim 2, wherein said amount of grain-growth inhibitor ranges by weight from about 0.25% to 1%.
Claim 5
Dependent Claim
15 words
The steel-bonded titanium carbide composition of claim 2, wherein said grain-growth inhibitor is tantalum carbide.
Claim 6
Dependent Claim
15 words
The steel-bonded titanium carbide composition of claim 2, wherein the grain-growth inhibitor is columbium carbide.
Claim 7
Dependent Claim
82 words
As an article of manufacture, a hardened wear resistant element made of a steel-bonded titanium carbide composition formed of primary grains of titanium carbide of average size less than 5 microns dispersed through a steel matrix characterized by the presence of martensite, said composition containing an effective amount of a grain-growth inhibitor corresponding to by weight from about 0.25% to 2% of a Group VB carbide, said hardened wear resistant element being characterized by improved anti-friction properties and improved resistance to wear.
Claim 8
Dependent Claim
82 words
As an article of manufacture, a hardened wear resistant element made of a steel-bonded titanium carbide composition formed of primary grains of titanium carbide of average size less than 5 microns dispersed through a steel matrix characterized by the presence of martensite, said composition containing an effective amount of a grain-growth inhibitor corresponding to by weight from about 0.25% to 2% of a Group VB carbide, said hardened wear resistant element being characterized by improved anti-friction properties and improved resistance to wear.
Claim 9
Dependent Claim
42 words
The hardened wear resistant element of claim 6, wherein the amount of titanium carbide in said composition ranges by weight from about 15% to 60%, and wherein said grain-growth inhibitor is selected from the group consisting of columbium carbide and tantalum carbide.
Claim 10
Dependent Claim
22 words
The hardened wear resistant element of claim 7, wherein said amount of grain-growth inhibitor ranges by weight from about 0.25% to 1%.
Claim 11
Dependent Claim
15 words
The hardened wear resistant element of claim 7, wherein said grain-growth inhibitor is tantalum carbide.
Claim 12
Dependent Claim
15 words
The hardened wear resistant element of claim 7, wherein the grain-growth inhibitor is columbium carbide.
Claim 13
Dependent Claim
19 words
The article of manufacture of claim 6, wherein the wear resistant element is an apex seal for rotary engines.
Claim 14
Independent Claim
139 words
A method of inhibiting the grain growth of titanium carbide grains in the production of a sintered, steel-bonded titanium carbide composition containing primary grains of titanium carbide dispersed through a steel matrix making up essentially the balance which comprises, providing a powder mixture of titanium carbide with powdered steel-forming ingredients, including an effective amount of a grain growth inhibitor corresponding to about 0.25% to 2% by weight of a Group VB carbide, compacting said mixture to a desired shape and sintering said shape at an elevated liquid phase sintering temperature of said matrix, whereby the titanium carbide grains in the resulting sintered product are characterized by an average grain size of less than 5 microns, by improved anti-friction properties and by improved resistance to wear by virtue of the presence of said effective amount of said Group VB carbide.
Claim 15
Independent Claim
139 words
A method of inhibiting the grain growth of titanium carbide grains in the production of a sintered, steel-bonded titanium carbide composition containing primary grains of titanium carbide dispersed through a steel matrix making up essentially the balance which comprises, providing a powder mixture of titanium carbide with powdered steel-forming ingredients, including an effective amount of a grain growth inhibitor corresponding to about 0.25% to 2% by weight of a Group VB carbide, compacting said mixture to a desired shape and sintering said shape at an elevated liquid phase sintering temperature of said matrix, whereby the titanium carbide grains in the resulting sintered product are characterized by an average grain size of less than 5 microns, by improved anti-friction properties and by improved resistance to wear by virtue of the presence of said effective amount of said Group VB carbide.
Claim 16
Dependent Claim
50 words
The method of claim 12, wherein said steel-bonded titanium carbide composition is produced to contain about 15% to 60% by weight of the titanium carbide based on the total composition, and wherein said grain-growth inhibitor in said composition is selected from the group consisting of columbium carbide and tantalum carbide.
Claim 17
Dependent Claim
22 words
The method of claim 13, wherein the amount of grain-growth inhibitor in said composition ranges in weight from about 0.25% to 1%.
Claim 18
Dependent Claim
15 words
The method of claim 13, wherein the grain-growth inhibitor in said composition is tantalum carbide.
Claim 19
Dependent Claim
15 words
The method of claim 13, wherein the grain-growth inhibitor in said composition is columbium carbide.
References Cited (Backward Citations)
US2828202A
Cited
GB1074405A
Cited
US3369891A
Cited
US3492101A
Cited
US3651934A
Cited
US3720504A
Cited
US3653982A
Cited
US3723077A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-29 | 1979-12-29 | 1980-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-29 | 1983-12-29 | 1984-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-29 | 1987-12-29 | 1988-06-29 | $7700.00 | Window Closed / Lapsed |