Leaching tremolite impurity from talc

Claim 2

A process for the preparation of high purity talc from talc ore containing tremolite as an impurity, which comprises: crushing said talc ore to provide finely ground talc of a particle size of minus 20 mesh; combining said finely ground talc with a strong acid; leaching said talc by subjecting said combination of talc and acid to a temperature of at least 110°C at a pressure of at least 1.5 kg/cm 2 for a time sufficient to reduce the amount of tremolite in said talc to less than 1.0 weight percent; prior or subsequent to said leaching step, forming a dilute aqueous slurry of said talc and subjecting said slurry to at least one froth flotation; and recovering a high purity talc.

Claim 3

The process of claim 1 in which said talc is crushed to provide a particle size of 100 percent minus 100 mesh and 98 percent minus 200 mesh.

Claim 4

The process of claim 1 in which said strong acid is a strong mineral acid.

Claim 5

The process of claim 3 in which said strong mineral acid is hydrochloric acid.

Claim 6

The process of claim 1 in which said temperature is in the range of 110°-250°C, said pressure is in a range of 1.5-40 kg/cm 2 and said leaching step is conducted for at least 1 hour.

Claim 7

A process for the preparation of a high purity talc from ore containing tremolite as an impurity, which comprises: crushing said talc ore to provide a finely ground talc of a particle size of minus 20 mesh; forming a dilute aqueous slurry of said crushed talc; subjecting said slurry to at least one froth flotation; removing the froth formed during the final froth flotation step to obtain a talc concentrate; combining said talc concentrate obtained from said final froth flotation with a strong acid; leaching said talc by subjecting said combination of talc concentrate and acid to a temperature of at least 110°C at a temperature of at least 1.5 kg/cm 2 for a time sufficient to reduce the amount of tremolite in said talc to less than 1.0 weight percent; and washing said leached talc and drying to recover a high purity talc.

Claim 8

A process for the preparation of a high purity talc from ore containing tremolite as an impurity, which comprises: crushing said talc ore to provide a finely ground talc of a particle size of minus 20 mesh; forming a dilute aqueous slurry of said crushed talc; subjecting said slurry to at least one froth flotation; removing the froth formed during the final froth flotation step to obtain a talc concentrate; combining said talc concentrate obtained from said final froth flotation with a strong acid; leaching said talc by subjecting said combination of talc concentrate and acid to a temperature of at least 110°C at a temperature of at least 1.5 kg/cm 2 for a time sufficient to reduce the amount of tremolite in said talc to less than 1.0 weight percent; and washing said leached talc and drying to recover a high purity talc.

Claim 9

The process of claim 6 in which said talc is crushed to provide a particle size of 100 percent minus 100 mesh and 98 percent minus 200 mesh.

Claim 10

The process of claim 6 in which said strong acid is a strong mineral acid.

Claim 11

The process of claim 8 in which said strong mineral acid is hydrochloric acid.

Claim 12

The process of claim 6 in which said temperature is in the range of 110°-250°C, said pressure is in the range of 1.5-40 kg/cm 2 and said leaching step is conducted for at least 1 hour.

Claim 13

A process for the preparation of a high purity talc from talc ore containing tremolite as an impurity, which comprises: crushing said talc ore to provide finely ground talc of a particle size of minus 20 mesh; combining said finely ground talc with a strong acid; leaching said talc by subjecting said combination of talc and acid to a temperature of at least 110°C at a pressure of at least 1.5 kg/cm 2 for a time sufficient to reduce the amount of tremolite in said talc to less than 1.0 weight percent; subsequent to said leaching step, forming a dilute aqueous slurry of said leached talc; subjecting said slurry to at least one froth flotation; removing the froth formed during the final froth flotation step; and recovering a high purity talc from said floated froth.

Claim 14

A process for the preparation of a high purity talc from talc ore containing tremolite as an impurity, which comprises: crushing said talc ore to provide finely ground talc of a particle size of minus 20 mesh; combining said finely ground talc with a strong acid; leaching said talc by subjecting said combination of talc and acid to a temperature of at least 110°C at a pressure of at least 1.5 kg/cm 2 for a time sufficient to reduce the amount of tremolite in said talc to less than 1.0 weight percent; subsequent to said leaching step, forming a dilute aqueous slurry of said leached talc; subjecting said slurry to at least one froth flotation; removing the froth formed during the final froth flotation step; and recovering a high purity talc from said floated froth.

Claim 15

The process of claim 11 in which said talc is crushed to provide a particle size of 100 percent minus 100 mesh and 98 percent minus 200 mesh.

Claim 16

The process of claim 11 in which said strong acid is a strong mineral acid.

Claim 17

The process of claim 13 in which said strong mineral acid is hydrochloric acid.

Claim 18

The process of claim 11 in which said temperature is in the range of 110°-250°C, said pressure is in the range of 1.5-40 kg/cm 2 and said leaching step is conducted for at least 1 hour.