Belleville spring
Assignee: BorgWarner Automotive Transmission and Engine Component Corp
•
Filing: 1974-08-23
•
Granted: 1976-06-22
•
Expires: 1994-08-23
Abstract
Abstract A washer-type spring, commonly called a Belleville spring, which has an improved fatigue life and residual compressive stresses resulting from the creation of a carbon gradient through the spring thickness. This improved spring is formed from a plain carbon or low alloy steel which, after blanking, cutting and forming, is heated to a temperature above the austenitizing temperature in a carbon-rich atmosphere, held at this temperature until suitably carburized, and then quenched.
Inventors
- 👤 Michael A. Schober
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 19:50
CPC Classifications
F; F16; F16B; F16B43/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
70 words
An improved Belleville spring formed of a low carbon steel having an original carbon content not higher than 0.40% carbon and provided with a case hardened surface to a depth in the range of 0.010 to 0.040 inches and having residual compressive stresses in the surface of the spring, said spring surface having a carbon content of at least approximately twice the carbon content at the core of the spring.
Claim 2
Dependent Claim
70 words
An improved Belleville spring formed of a low carbon steel having an original carbon content not higher than 0.40% carbon and provided with a case hardened surface to a depth in the range of 0.010 to 0.040 inches and having residual compressive stresses in the surface of the spring, said spring surface having a carbon content of at least approximately twice the carbon content at the core of the spring.
Claim 3
Dependent Claim
25 words
An improved Belleville spring as set forth in claim 1, in which the residual compressive stresses are in the range of -70,000 to -80,000 psi.
Claim 4
Dependent Claim
27 words
An improved Belleville spring as set forth in claim 2, in which the fatigue life of the spring is improved in the range of 100 to 300%.
Claim 5
Dependent Claim
35 words
An improved Belleville spring as set forth in claim 1, in which said case hardened surface is formed by carburization in an atmosphere having a carbon potential of 0.60 to 1.20% carbon and subsequent quenching.
Claim 6
Dependent Claim
26 words
An improved Belleville spring as set forth in claim 1, in which said case hardened depth is in the range of from 0.010 to 0.025 inches.
Claim 7
Dependent Claim
61 words
An improved Belleville spring as set forth in claim 1, in which the raw material for the spring has an original carbon content of approximately 0.20 to 0.40% carbon, and the case hardened spring has a surface carbon content of approximately 0.75% carbon, a core carbon content of approximately 0.35% carbon and an effective case hardened depth of about 0.020 inches.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-22 | 1979-12-22 | 1980-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-22 | 1983-12-22 | 1984-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-22 | 1987-12-22 | 1988-06-22 | $7700.00 | Window Closed / Lapsed |