Fireproof product using magnesium oxychloride cement
Assignee: Thompson Chemicals Inc
•
Filing: 1973-09-17
•
Granted: 1976-06-15
•
Expires: 1993-09-17
Abstract
Abstract A method of making a foamed fireproof product of magnesium oxychloride cement and the resulting product. A porous substrate is impregnated with a foaming mixture of magnesium chloride, magnesium oxide, and frothing agent in water. The mixture hardens with small voids throughout the porous substrate, thus providing a fireproof product of low density. The foamed product may be formed in a mold with fibrous elements inroduced into the foaming mixture. The fireproof products of relatively low density are particularly valuable for building and construction purposes. Magnesium powder is the preferred frothing agent which, in combination with a surfactant, induces a large volume of small bubbles that remain in the composition as it is set.
Inventors
- 👤 Henry Clark Thompson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:53
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/36; C08J9/40; C04; C04B; C04B28/00; C04B28/30; C04B28/32; C08J9/35; C08K; C08K3/00; C08K3/01; C08K3/016; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/91; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10S521/00; Y10S521/906; Y10S521/907; Y10S521/918; Y10T; Y10T428/00; Y10T428/24; Y10T428/24628; Y10T428/24669; Y10T428/24694; Y10T428/24711; Y10T428/249921; Y10T428/249953; Y10T428/249955; Y10T428/249956; Y10T428/249962; Y10T428/249964; Y10T428/249965; Y10T428/249967; Y10T428/249968; Y10T428/249981; Y10T428/31504; Y10T428/31551; Y10T428/31609
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
78 words
An article of manufacture comprising a burnable porous substrate impregnated substantially throughout its cross section with a fireproofing amount of foamed magnesium oxychloride cement formed by mixing aqueous magnesium chloride having a specific gravity of between 21.5° and 22.5° Baume with between 5 and 6.5 pounds magnesium oxide per gallon of aqueous magnesium chloride and a frothing agent reactive with said mixture to produce bubbles, in an amount between 2 and 40% of the weight of the substrate.
Claim 2
Dependent Claim
78 words
An article of manufacture comprising a burnable porous substrate impregnated substantially throughout its cross section with a fireproofing amount of foamed magnesium oxychloride cement formed by mixing aqueous magnesium chloride having a specific gravity of between 21.5° and 22.5° Baume with between 5 and 6.5 pounds magnesium oxide per gallon of aqueous magnesium chloride and a frothing agent reactive with said mixture to produce bubbles, in an amount between 2 and 40% of the weight of the substrate.
Claim 3
Dependent Claim
13 words
An article as in claim 1 wherein the substrate comprises cellulose foam sponge.
Claim 4
Dependent Claim
12 words
An article as in claim 1 wherein the substrate comprises polyurethane foam.
Claim 5
Dependent Claim
12 words
An article as in claim 1 wherein the substrate comprises fiberboard panel.
Claim 6
Dependent Claim
12 words
An article as in claim 1 wherein the substrate comprises corrugated cardboard.
Claim 7
Dependent Claim
75 words
An article of manufacture comprising glass fibers and a fireproofing amount of foamed magnesium oxychloride cement made by mixing aqueous magnesium chloride having a specific gravity between 21.5° and 22.5° Baume with between 5 and 6.5 pounds magnesium oxide per gallon of aqueous magnesium chloride and a metallic frothing agent reactive with said mixture to produce bubbles, said cement being present in an amount between 2 and 40% of the weight of the glass fibers.
Claim 8
Dependent Claim
75 words
An article of manufacture comprising glass fibers and a fireproofing amount of foamed magnesium oxychloride cement made by mixing aqueous magnesium chloride having a specific gravity between 21.5° and 22.5° Baume with between 5 and 6.5 pounds magnesium oxide per gallon of aqueous magnesium chloride and a metallic frothing agent reactive with said mixture to produce bubbles, said cement being present in an amount between 2 and 40% of the weight of the glass fibers.
Claim 9
Dependent Claim
50 words
An article as in claim 6 comprising a strong, resilient layer of chopped glass fibers thoroughly impregnated with foamed magnesium oxychloride cement containing filler and supporting layers on each side thereof of foamed magnesium oxychloride cement, the density of the article being between 20 and 40 pounds per cubic foot.
References Cited (Backward Citations)
US735335A
Cited
US1372118A
Cited
US1429451A
Cited
US1500207A
Cited
US1965538A
Cited
US2200850A
Cited
US2598980A
Cited
US2702753A
Cited
US3050427A
Cited
US3133830A
Cited
US3013901A
Cited
GB964569A
Cited
US3573941A
Cited
US3522069A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-15 | 1979-12-15 | 1980-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-15 | 1983-12-15 | 1984-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-15 | 1987-12-15 | 1988-06-15 | $7700.00 | Window Closed / Lapsed |