Method of imparting increased dezincification resistance to brass
Assignee: NKT AS
•
Filing: 1974-07-10
•
Granted: 1976-06-15
•
Expires: 1994-07-10
Abstract
Abstract A method in which to a brass containing 61-66% of copper there is added 0.02% of an alloying element such as arsenic, antimony or phosphorus and up to 4% of lead and in the case of chill casting and pressure die casting alloys 0.05-0.8% of aluminum, the remainder being zinc and usual impurities from the raw materials used, and in which the alloy after chill casting, pressure die-casting or sand casting, after extrusion or, where applicable, after hot pressing of parts cut from extruded rods, is heated to a temperature in the interval between 450 and 600° Celcius for a period so selected that the β-crystals are broken up, thus avoiding the occurence of a coherent structure of β-crystals through the brass.
Inventors
- 👤 Borge Lunn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 03:04
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/08
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
128 words
The method of making a brass alloy of the type consisting essentially of primary zinc and from 61 to 66 per cent by weight of copper, suitable for casting, extruding and working and of imparting increased dezincification-resistance to the resulting brass product, said method comprising the steps of initially including in the alloy a small proportion of at least 0.02 per cent by weight of an anti-dezincification agent, and subjecting the resulting brass alloy product to heat treatment in the temperature range of from 450° to 600°C., and continuing the heat treatment at the selected temperature for a period of time sufficient to breakup the beta crystal structure normally formed in the brass alloy into individual units in the alloy and without mutual coherence throughout the alloy product.
Claim 2
Independent Claim
128 words
The method of making a brass alloy of the type consisting essentially of primary zinc and from 61 to 66 per cent by weight of copper, suitable for casting, extruding and working and of imparting increased dezincification-resistance to the resulting brass product, said method comprising the steps of initially including in the alloy a small proportion of at least 0.02 per cent by weight of an anti-dezincification agent, and subjecting the resulting brass alloy product to heat treatment in the temperature range of from 450° to 600°C., and continuing the heat treatment at the selected temperature for a period of time sufficient to breakup the beta crystal structure normally formed in the brass alloy into individual units in the alloy and without mutual coherence throughout the alloy product.
Claim 3
Dependent Claim
25 words
The method according to claim 1, including the step of adding up to about 4 per cent by weight of lead to the alloy composition.
Claim 4
Dependent Claim
25 words
The method according to claim 1, including the step of adding from 0.05 to 0.8 per cent by weight of aluminum to the alloy composition.
Claim 5
Dependent Claim
12 words
The method according to claim 1, wherein said anti-dezincification agent is arsenic.
Claim 6
Dependent Claim
32 words
The method according to claim 1, wherein the anti-dezincification agent is present in at least 0.02 per cent by weight and is selected from the group consisting of arsenic, antimony and phosphorus.
Claim 7
Dependent Claim
58 words
The method according to claim 1 wherein prior to said heat treatment, said alloy is first hot formed at a temperature above the temperature of said heat treatment and then cooled to the heat treatment range but not below and then held at the heat treatment range for said period of time sufficient to breakup the beta-crystal structure.
Claim 8
Dependent Claim
62 words
The method of claim 1, wherein prior to said heat treatment said alloy is first hot formed at a temperature above the temperature of said treatment and then allowed to cool to a temperature below the temperature of said heat treatment and subsequently reheated to the temperature of said heat treatment for said period of time sufficient to breakup the beta-crystal structure.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-15 | 1979-12-15 | 1980-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-15 | 1983-12-15 | 1984-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-15 | 1987-12-15 | 1988-06-15 | $7700.00 | Window Closed / Lapsed |