Reduction of dislocations in multilayer structures of zinc-blend materials
Assignee: AT&T Inc
•
Filing: 1974-04-25
•
Granted: 1976-06-08
•
Expires: 1994-04-25
Abstract
Abstract Described is a procedure for virtually eliminating disclocations in multilayer structures of materials having a crystallographic zinc-blend structure, in particular quaternary layers of Al y Ga 1 -y As 1 -z P z grown on Al x Ga 1 -x As substrates (y > x ≧ 0). By carefully controlling the quaternary layer thickness and the lattice parameter mismatch at the growth temperature, it is possible to change the direction of substrate dislocations as they enter the substrate/layer interface. The length of the dislocation in the interfacial plane can be extended so that it is "infinitely" long, i.e., it reaches the edge of the wafer. As a result, the epitaxial quaternary layer and all layers subsequently grown thereon will be virtually dislocation free, provided that the thickness, stress and uniformity of the layers are such that no surface dislocation souces are activated. Also described are double heterostructure junction lasers with reduced values of both stress and dislocations.
Inventors
- 👤 Pierre Marc Petroff
- 👤 George Arthur Rozgonyi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:23
CPC Classifications
H; H01; H01S; H01S5/00; H01S5/30; H01S5/32; H01S5/323; H01S5/32308; H01S5/20; H10; H10H; H10H20/00; H10H20/80; H10H20/81; H10H20/811; H10H20/822; H10H20/824; H01S5/2054; H01S5/2059; H01S5/22; H01S5/223; H01S5/3211; Y; Y10; Y10S; Y10S148/00; Y10S148/065; Y10S148/066; Y10S148/067; Y10S148/097; Y10S148/107; Y10S438/00; Y10S438/938
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
85 words
A semiconductor device comprising a first layer of a material having a zinc-blende crystallographic structure and exhibiting a non-zero dislocation density, a second layer of a material having a zinc-blende crystallographic structure formed on said first layer so that misfit dislocations are generated at the interface between said layers, the thickness and composition of said second layer being effective to generate a unidirectional array of misfit dislocations at said interface which virtually prevents any defects in said first layer from extending into said second layer.
Claim 2
Dependent Claim
85 words
A semiconductor device comprising a first layer of a material having a zinc-blende crystallographic structure and exhibiting a non-zero dislocation density, a second layer of a material having a zinc-blende crystallographic structure formed on said first layer so that misfit dislocations are generated at the interface between said layers, the thickness and composition of said second layer being effective to generate a unidirectional array of misfit dislocations at said interface which virtually prevents any defects in said first layer from extending into said second layer.
Claim 3
Dependent Claim
51 words
The structure of claim 1 wherein said first layer comprises Al x Ga 1 -x As, said second layer comprises Al y Ga 1 -y As 1 -z P z , and the fraction y of Al in said second layer exceeds the fraction x of Al in said first layer.
Claim 4
Dependent Claim
38 words
The structure of claim 2 wherein the thickness of said second layer is in the approximate range of 1 μm to 3 μm and the fraction z of phosphorus is in the range of about 0.03 to 0.007.
Claim 5
Dependent Claim
27 words
The structure of claim 3 wherein said second layer is epitaxially grown from a gallium solution containing about 1 to 5 × 10.sup. -5 atom percent phosphorus.
Claim 6
Dependent Claim
86 words
A double heterostructure light emitting device including: a GaAs substrate comprising said first layer of claim 2, a first wide bandgap layer comprising said Al y Ga 1 -y As 1 -z P z layer of claim 2, an active layer comprising Al p Ga 1 -p As, 0 ≦ p < y, formed on said first wide bandgap layer, and a second wide bandgap layer comprising Al q Ga 1 -q As 1 -m P m , q > p, formed on said active layer.
Claim 7
Dependent Claim
16 words
The device of claim 5 wherein p is substantially zero and said active layer comprises GaAs.
Claim 8
Dependent Claim
39 words
The device of claim 5 wherein said substrate is n-type, said Al y Ga 1 -y As 1 -z P z layer is n-type, and said Al q Ga 1 -q As 1 -m P m layer is p-type.
Claim 9
Dependent Claim
11 words
The device of claim 7 wherein said active layer is p-type.
Claim 10
Dependent Claim
28 words
The device of claim 8 including further a low resistivity contacting layer of p-GaAs formed on said Al q Ga 1 -q As 1 -m P m layer.
Claim 11
Dependent Claim
101 words
A semiconductor structure comprising a substrate of a material having a zinc-blende crystallographic structure and exhibiting a non-zero dislocation density, a device composed of a material having a zinc-blende crystallographic structure to be carried by said substrate, and means interposed between and contiguous with major surfaces of said substrate and said device for virtually preventing any defects in said substrate from extending into said device comprising a layer of material having a zinc-blende crystallographic structure, the composition and thickness of said layer being effective to generate a unidirectional array of misfit dislocations at the interface between said layer and said substrate.
Claim 12
Dependent Claim
101 words
A semiconductor structure comprising a substrate of a material having a zinc-blende crystallographic structure and exhibiting a non-zero dislocation density, a device composed of a material having a zinc-blende crystallographic structure to be carried by said substrate, and means interposed between and contiguous with major surfaces of said substrate and said device for virtually preventing any defects in said substrate from extending into said device comprising a layer of material having a zinc-blende crystallographic structure, the composition and thickness of said layer being effective to generate a unidirectional array of misfit dislocations at the interface between said layer and said substrate.
Claim 13
Independent Claim
46 words
A method of preventing defects in a zinc-blende substrate from extending into a zonc-blende epitaxial layer grown thereon comprising controlling the composition and thickness of said layer so that a unidirectional array of misfit dislocations is generated at the interface between said substrate and said layer.
Claim 14
Independent Claim
46 words
A method of preventing defects in a zinc-blende substrate from extending into a zonc-blende epitaxial layer grown thereon comprising controlling the composition and thickness of said layer so that a unidirectional array of misfit dislocations is generated at the interface between said substrate and said layer.
References Cited (Backward Citations)
US3812516A
Cited
US3838359A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-08 | 1979-12-08 | 1980-06-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-08 | 1983-12-08 | 1984-06-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-08 | 1987-12-08 | 1988-06-08 | $7700.00 | Window Closed / Lapsed |