Patent US3960798A successfully refreshed from Google Patents.
US3960798A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for regulating hardening speed of self-hardening mold
Assignee: Hitachi Ltd
•
Filing: 1974-08-26
•
Granted: 1976-06-01
•
Expires: 1994-08-26
Abstract
Abstract A process for regulating the hardening speed of a self-hardening mold which comprises adding an alcohol as a hardening speed regulating agent when a mold is formed with molding sand prepared by adding a polyvinyl alcohol solution and a boron compound to refractory particles and then kneading the mixture. As the hardening speed regulating agent, polyhydric alcohol such as ethylene glycol, mannitol, sorbitol, glycerol, etc., and monohydric alcohols such as methyl alcohol, ethyl alcohol, isopropyl alcohol, etc., may be used.
Inventors
- 👤 Tetsuo Nakazawa
- 👤 Osamu Nishida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:46
CPC Classifications
B; B22; B22C; B22C1/00; B22C1/16; B22C1/20
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
87 words
A process for regulating the hardening speed of a self-hardening mold which comprises adding 0.1 to 3 parts by weight of an aliphatic alcohol as a hardening speed regulating agent when a mold is formed with a molding sand prepared by adding 1 to 10 parts by weight of a polyvinyl alcohol solution having a concentration of 5 to 30% by weight and from 0.01 to 2.1 parts by weight of a boron compound to 100 parts by weight of refractory particles and then kneading the mixture.
Claim 2
Dependent Claim
87 words
A process for regulating the hardening speed of a self-hardening mold which comprises adding 0.1 to 3 parts by weight of an aliphatic alcohol as a hardening speed regulating agent when a mold is formed with a molding sand prepared by adding 1 to 10 parts by weight of a polyvinyl alcohol solution having a concentration of 5 to 30% by weight and from 0.01 to 2.1 parts by weight of a boron compound to 100 parts by weight of refractory particles and then kneading the mixture.
Claim 3
Dependent Claim
29 words
A process according to claim 1, wherein said aliphatic alcohol is selected from the group consisting of methyl alcohol, ethyl alcohol, isopropyl alcohol, sorbitol, mannitol, ethylene glycol and glycerol.
Claim 4
Dependent Claim
44 words
A process according to claim 1, wherein from 0.1 to 2.1 parts by weight of a boron compound selected from the group consisting of manganese borate, boric acid, magnesium borate and calcium borate are added to 100 parts by weight of the refractory particles.
Claim 5
Dependent Claim
45 words
A process according to claim 1, wherein from 0.01 to 1.3 parts by weight of a boron compound selected from the group consisting of borax, sodium perborate, potassium borate, boron oxide and ammonium borate are added to 100 parts by weight of the refractory particles.
Claim 6
Dependent Claim
20 words
A process according to claim 4, wherein the boron compound added is borax and the refractory particles are silica sand.
Claim 7
Dependent Claim
84 words
A process for regulating the hardening speed of a self-hardening mold which comprises adding 0.2 part by weight of an aliphatic alcohol as a hardening speed regulating agent selected from the group consisting of sorbitol, methyl alcohol, ethylene glycol and glycerol when a mold is formed by adding 4 parts by weight of a polyvinyl alcohol solution having a concentration of 10% by weight and 1 part by weight of borax to 100 parts by weight of silica sand and then kneading the mixture.
Claim 8
Dependent Claim
84 words
A process for regulating the hardening speed of a self-hardening mold which comprises adding 0.2 part by weight of an aliphatic alcohol as a hardening speed regulating agent selected from the group consisting of sorbitol, methyl alcohol, ethylene glycol and glycerol when a mold is formed by adding 4 parts by weight of a polyvinyl alcohol solution having a concentration of 10% by weight and 1 part by weight of borax to 100 parts by weight of silica sand and then kneading the mixture.
Claim 9
Dependent Claim
71 words
A process for regulating the hardening speed of a self-hardening mold which comprises adding 0.2 to 0.8 parts by weight of glycerol as a hardening speed regulating agent when a mold is formed by adding 4 parts by weight of a polyvinyl alcohol solution having a concentration of 15% by weight and one part by weight of borax to 100 parts by weight of silica sand and then kneading the mixture.
Claim 10
Dependent Claim
71 words
A process for regulating the hardening speed of a self-hardening mold which comprises adding 0.2 to 0.8 parts by weight of glycerol as a hardening speed regulating agent when a mold is formed by adding 4 parts by weight of a polyvinyl alcohol solution having a concentration of 15% by weight and one part by weight of borax to 100 parts by weight of silica sand and then kneading the mixture.
Claim 11
Dependent Claim
64 words
A process for regulating the hardening speed of a self-hardening mold which comprises adding 4 parts by weight of an aqueous solution containing 10% by weight of polyvinyl alcohol and 5 to 35% by weight of isopropyl alcohol as a hardening speed regulating agent and 0.5 parts by weight of borax to 100 parts by weight of silica sand and then kneading the mixture.
Claim 12
Dependent Claim
64 words
A process for regulating the hardening speed of a self-hardening mold which comprises adding 4 parts by weight of an aqueous solution containing 10% by weight of polyvinyl alcohol and 5 to 35% by weight of isopropyl alcohol as a hardening speed regulating agent and 0.5 parts by weight of borax to 100 parts by weight of silica sand and then kneading the mixture.
Claim 13
Dependent Claim
21 words
A process according to claim 8, wherein said isopropyl alcohol has a concentration of 25% by weight within said aqueous solution.
Claim 14
Dependent Claim
60 words
A molding sand containing 1 to 10 parts by weight of an aqueous polyvinyl alcohol solution having a concentration of 5 to 30% by weight, 0.01 to 2.1 parts by weight of a boron compound and 0.1 to 3 parts by weight of an aliphatic alcohol as a hardening speed regulating agent per 100 parts by weight of refractory particles.
Claim 15
Dependent Claim
60 words
A molding sand containing 1 to 10 parts by weight of an aqueous polyvinyl alcohol solution having a concentration of 5 to 30% by weight, 0.01 to 2.1 parts by weight of a boron compound and 0.1 to 3 parts by weight of an aliphatic alcohol as a hardening speed regulating agent per 100 parts by weight of refractory particles.
Claim 16
Dependent Claim
37 words
A molding sand according to claim 10, wherein from 0.1 to 2.1 parts by weight of a boron compound selected from the group consisting of manganese borate, boric acid, magnesium borate and calcium borate are contained therein.
Claim 17
Dependent Claim
38 words
A molding sand according to claim 10, wherein from 0.1 to 1.3 parts by weight of a boron compound selected from the group consisting of borax, sodium perborate, potassium borate, boron oxide and ammonium borate are contained therein.
Claim 18
Dependent Claim
20 words
A molding sand according to claim 12, wherein the boron compound is borax and the refractory particles are silica sand.
Claim 19
Dependent Claim
30 words
A molding sand according to claim 10, wherein said aliphatic alcohol is selected from the group consisting of methyl alcohol, ethyl alcohol, isopropyl alcohol, sorbitol, mannitol, ethylene glycol and glycerol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-06-01 | 1979-12-01 | 1980-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-06-01 | 1983-12-01 | 1984-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-06-01 | 1987-12-01 | 1988-06-01 | $7700.00 | Window Closed / Lapsed |