Manufacturing method for electrophotographic developing agent
Assignee: Fujifilm Holdings Corp
•
Filing: 1970-05-28
•
Granted: 1976-05-25
•
Expires: 1990-05-28
Abstract
Abstract This invention is a method for manufacturing an electrophotographic developer for use in electrophotography or electrostatic recording processes. The developer comprises polymer particles by suspension polymerizing, in an aqueous phase, a polymerization liquid comprising at least one polymerizable vinyltype monomer, a polymerization initiator, and a finely divided dispersion stabilizer either sparingly soluble or insoluble in water and said monomer. Said polymerization liquid is blended prior to suspension polymerization. The improvement includes adding to said liquid, a resinous substance, as a fluidizer which is soluble in the monomer and having a solubility parameter in the range of from 7.8 to 16.1. During the blending, the dispersion stabilizer is uniformly dispersed throughout said polymerization liquid. Next, the blended polymerization liquid containing the fluidizer is suspended in the aqueous phase and then such blend is subjected to said suspension polymerization to effect polymer particles having diameters in the range of 0.1 to 100μ.
Inventors
- 👤 Shigeru Sadamatsu
- 👤 Hiroyuki Kaneko
- 👤 Keitaro Ohe
- 👤 Daijiro Nishio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 15:50
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/0802; G03G9/0804; G03G9/0806; G03G9/097; G03G9/09708; G03G9/12; G03G9/135
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
184 words
In a manufacturing method for producing an electrophotographic developer comprising polymer particles by suspension polymerizing, in an aqueous phase, a polymerization liquid comprising at least one polymerizable vinyltype monomer selected from the group consisting of styrene, acrylic alkyl, methacrylic alkyl, vinyl chloride and vinyl acetate, a polymerization initiator, and a finely divided dispersion stabilizer either sparingly soluble or insoluble in water and said monomer, said polymerization liquid being blended prior to said suspension polymerization, the improvement comprising adding to said polymerization liquid a resinous substance, as a fluidizer, soluble in the synthetic resin monomer and having a solubility parameter in the range of from 7.8 to 16.1, the addition ratio of said resinous substance to said vinyltype monomer being approximately 0.001% to 1%, said dispersion stabilizer being uniformly dispersed throughout said polymerization liquid during said blending, next suspending the blended polymerization liquid containing the fluidizer in said aqueous phase, and then subjecting the blend to said suspension polymerization whereby the formation of said polymer particles having average particle diameters in the range of from 0.1 to 100 μ is effected during said suspension polymerization.
Claim 2
Dependent Claim
184 words
In a manufacturing method for producing an electrophotographic developer comprising polymer particles by suspension polymerizing, in an aqueous phase, a polymerization liquid comprising at least one polymerizable vinyltype monomer selected from the group consisting of styrene, acrylic alkyl, methacrylic alkyl, vinyl chloride and vinyl acetate, a polymerization initiator, and a finely divided dispersion stabilizer either sparingly soluble or insoluble in water and said monomer, said polymerization liquid being blended prior to said suspension polymerization, the improvement comprising adding to said polymerization liquid a resinous substance, as a fluidizer, soluble in the synthetic resin monomer and having a solubility parameter in the range of from 7.8 to 16.1, the addition ratio of said resinous substance to said vinyltype monomer being approximately 0.001% to 1%, said dispersion stabilizer being uniformly dispersed throughout said polymerization liquid during said blending, next suspending the blended polymerization liquid containing the fluidizer in said aqueous phase, and then subjecting the blend to said suspension polymerization whereby the formation of said polymer particles having average particle diameters in the range of from 0.1 to 100 μ is effected during said suspension polymerization.
Claim 3
Dependent Claim
22 words
In a manufacturing method for an electrophotographic developer as claimed in claim 1, wherein said polymerization initiator is benzoyl peroxide or azobisisobutylonitrile.
Claim 4
Dependent Claim
52 words
A manufacturing method for an electrophotographic developer as claimed in claim 1, wherein the finely divided dispersion stabilizer is selected from the group consisting of metallic powders, inorganic oxides, and inorganic salts so long as these are either sparingly soluble or insoluble in water as well as in the monomer being used.
Claim 5
Dependent Claim
26 words
A manufacturing method for an electrophotographic developer as claimed in claim 3, wherein said finely divided dispersion stabilizer is said metallic powder and it is aluminum.
Claim 6
Dependent Claim
36 words
A manufacturing method for an electrophotographic developer as claimed in claim 3, wherein said finely divided dispersion stabilizer is said inorganic oxide and it is selected from the group consisting of zinc white and titanium oxide.
Claim 7
Dependent Claim
42 words
A manufacturing method for an electrophotographic developer as claimed in claim 3, wherein said finely divided dispersion stabilizer is said inorganic salt and it is selected from the group consisting of calcium carbonate, magnesium carbonate, potassium phosphate, calcium phosphate and barium sulfate.
Claim 8
Dependent Claim
31 words
In a manufacturing method for an electrophotographic developer as claimed in claim 1, wherein said resinous substance is ethylcellulose resin, polyurethane resin, amino resin, epoxy resin, phenol resin or alkyd resin.
Claim 9
Dependent Claim
26 words
In a manufacturing method as in claim 1 where the range of said polymer particles is from 0.1 to 25 microns in average particle diameter thereof.
Claim 10
Dependent Claim
22 words
In a manufacturing method for an electrophotographic developer as claimed in claim 1, wherein coloring materials are incorporated in said polymerization liquid.
References Cited (Backward Citations)
US2788288A
Cited
US3011918A
Cited
US3190847A
Cited
US3335100A
Cited
US3338991A
Cited
US3391082A
Cited
US3554778A
Cited
US3706722A
Cited
US3585140A
Cited
US3634251A
Cited
US3586654A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-25 | 1979-11-24 | 1980-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-25 | 1983-11-24 | 1984-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-25 | 1987-11-24 | 1988-05-25 | $7700.00 | Window Closed / Lapsed |